Silane-terminiated polysulfide rubber sealant and preparation method thereof
A polysulfide rubber, silane-terminated technology, used in adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of complex construction process, two-component and other problems, achieve easy reaction conditions, promote adhesion, The effect of less air pollution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] (1) Add 100g of liquid polysulfide rubber G21, 33.3g of xylene, and 22.17g of γ-(2,3-glycidyloxy) to a four-necked flask equipped with a stirrer, a thermometer, a reflux condenser and an air guide tube. Propyltrimethoxysilane, feed a stable high-purity nitrogen flow as the protective atmosphere of the reaction system, stir; then slowly raise the temperature to 120°C, react at constant temperature for 30 hours, then cool down to 80°C to remove the solvent in a vacuum, and then obtain alkoxysilane End-capped polysulfide rubber (oligomer).
[0030] (2) Weigh 100g of the above-mentioned silane-terminated polysulfide rubber, 100g of modified active light calcium carbonate, and 65g of mica powder for initial mixing, then place the above-mentioned materials after initial mixing on a three-roll mill for grinding, and grind for three Obtain the base glue of silane-terminated polysulfide rubber sealant after one pass;
[0031] (3) Add 40g of dioctyl phthalate to the base rubber ...
Embodiment 2
[0034] The difference between this embodiment and embodiment 1 is:
[0035]The epoxy silane added in step 1 is 20.67g γ-(2,3-glycidoxy)propylmethyldimethoxysilane, and the constant temperature reaction is 33h; the modified active light calcium carbonate in step 2 is 80g 1. The inorganic extender filler is 70 g of diatomite; the surface dry time of the silane-terminated polysulfide rubber sealant obtained in step 4 is 5 hours, the solid drying time is 48 hours, the Shore A hardness is 48, and the tensile strength is 1.6 MPa.
Embodiment 3
[0037] The difference between this embodiment and embodiment 1 is:
[0038] Add 100g of liquid polysulfide rubber LP-23 and 30g of γ-(2,3-glycidoxy)propyltrimethoxysilane in step 1; the plasticizer added in step 3 is 40g of dibutyl phthalate, Insulate for 3.5 hours and drop to room temperature of 45°C; add 0.3 g of dibutyltin dilaurate and 0.1 g of dihexylamine in step 4, and the surface dry time of the obtained silane-terminated polysulfide rubber sealant is 3.5 hours, and the dry time is 60 hours. The Shore A hardness is 38 and the tensile strength is 1.2MPa.
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap