Leather comprehensive fat liquor and preparation method of the same

A fatliquor, leather technology, applied in leather impregnation, small raw hide/large raw hide/leather/fur treatment, small raw hide/large raw hide/leather hide/fur chemical treatment, etc. Large, poor stability and other problems, to achieve the effect of good softness and fullness, improved softness and hand feel, and good appearance and fluidity

Active Publication Date: 2013-05-08
传化智联股份有限公司 +2
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The comprehensive fatliquoring agents imported on the market and domestically developed have their own advantages and disadvantages, but they generally have weaknesses such as high price, poor stability, easy delamination, large amount of solvent and pungent odor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Leather comprehensive fat liquor and preparation method of the same
  • Leather comprehensive fat liquor and preparation method of the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Set the mass ratio to C 8 -C 10 Alcohol:C 12 -C 14 Alcohol:C 16 -C 18 Alcohol=8%:80%:12% mixed higher carbon alcohol and maleic anhydride are mixed in a molar ratio of 1:1, and reacted at 100°C for 6 hours to obtain a mixed higher carbon alcohol ester; then mixed higher carbon alcohol Alcohol esterification and anhydrous sodium sulfite were added into anhydrous sodium sulfite at a molar ratio of 1:1, and reacted at 85°C for 4 hours to obtain esterified sulfitated products of higher alcohols.

[0023] 2. The esterification sulfitation product of the above-mentioned high carbon alcohol is cooled to 60 ℃, and is measured by mass ratio: the esterification sulfitation product of high carbon alcohol: modified soybean lecithin: sulfited rapeseed oil: lanolin : Natural beef hoof oil: No. 10 white oil: Sodium lauryl sulfate: water = 22:12:12:2:2:3:1:46 Add the compound ingredients, stir for 1 hour and then use saturated sodium hydroxide Adjust the pH value of the aqueou...

Embodiment 2

[0025] 1. The mass ratio is: C 8 -C 10 Alcohol:C 12 -C 14 Alcohol:C 16 -C 18 Alcohol=12%:80%:8% mixed higher carbon alcohol and maleic anhydride are mixed in a molar ratio of 1:0.8, and reacted at 100°C for 6 hours to obtain a mixed higher carbon alcohol ester; then mixed higher carbon alcohol Alcohol and sodium metabisulfite were added into sodium metabisulfite at a molar ratio of 1:0.4, and reacted at 80°C for 4 hours to obtain esterified sulfitated products of higher alcohols.

[0026] 2. The esterification sulfitation product of the above-mentioned high carbon alcohol is cooled to 60 ℃, and is measured by mass ratio: the esterification sulfitation product of high carbon alcohol: modified soybean lecithin: sulfited rapeseed oil: lanolin : Natural beef hoof oil: No. 10 white oil: Sodium lauryl sulfate: Water = 27:12:6:1:1:4:1:48 Add compound ingredients, stir for 1 hour and then use saturated sodium hydroxide Adjust the pH value of the aqueous solution to 6-8, stir for...

Embodiment 3

[0028] 1. The mass ratio is: C 8 -C 10 Alcohol:C 12 -C 14 Alcohol:C 16 -C 18 Alcohol=15%:75%:10% mixed higher alcohol alcohol and maleic anhydride are mixed at a molar ratio of 1:0.6, and reacted at 150°C for 2 hours to obtain a mixed higher alcohol ester; then mixed higher alcohol Alcohol and anhydrous sodium sulfite were added into anhydrous sodium sulfite at a molar ratio of 1:0.6, and reacted at 80°C for 4 hours to obtain esterified sulfitated products of higher alcohols.

[0029] 2. The esterification sulfitation product of above-mentioned high carbon alcohol is cooled to 60 ℃, is the esterification sulfitation product of high carbon alcohol with mass ratio: modified soybean lecithin: sulfitated rapeseed oil: lanolin: natural Bovine hoof oil: No. 10 white oil: sodium lauryl sulfate: water = 25:12:8:2:2:3:1:47, add the compound ingredients, stir for 1 hour and adjust with saturated sodium hydroxide aqueous solution When the pH value reaches 6-8, stir for 0.5 hours, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a leather comprehensive fat liquor and a preparation method of the same. Currently, the defects, such as high price, poor stability, layering propensity, high solvent dosage and pungent smell, are common issues for the leather comprehensive fat liquor. In the method, esterification and sulfitation products of high alcohol, modified soybean phospholipid, sulfonated plant oil, animal fat, mineral oil emulsifier and water are mixed evenly at 45-65 DEG C, the pH value is regulated to be 6-8, and the solid content is regulated to be 45-55%, thus, the leather comprehensive fat liquor is obtained. The product of the method is excellent in appearance liquidity, the leather fatted by the fat liquor is excellent in softness and fullness, and the surface of the fatted leather is smooth and moist.

Description

technical field [0001] The invention relates to the technical field of leather chemical industry, in particular to a synthetic leather fatliquoring agent and a preparation method thereof. Background technique [0002] Fatliquor is the most used leather chemical material in tanning production. Fatliquoring is also one of the important processes in the leather processing process. After the leather is treated with fatliquoring, a layer of lubricating oil is wrapped on the surface of the leather fiber, which improves the The relative sliding performance between fibers reduces the friction between leather fibers, so that the leather becomes soft, fold-resistant, plump and elastic. At the same time, through the interaction between the active groups in the fatliquoring agent and the leather fibers, Increase the strength and extensibility of leather, and improve the comprehensive performance of leather. As the leather industry has higher and higher requirements for leather fatliquo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C14C9/02
Inventor 宋鹏王胜鹏王小君曾军闫哲
Owner 传化智联股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap