Preparation method of slag stones
A technology of stone and slag, which is applied in the field of preparing slag stone from hot blast furnace slag, can solve the problems of high energy consumption of cold blast furnace slag, low utilization rate of blast furnace slag, and high production cost of products, and achieve water saving, low cost, The effect of improving the utilization rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0053] Weigh raw materials: (kg)
[0054] Blast furnace slag 70, quartz sand 20, sodium fluorosilicate 6, soda ash 9, fluorite 2, ammonium dihydrogen phosphate 2, zinc oxide 1.5.
[0055] Preparation of slag stone:
[0056] Step 1: Transfer 70 kg of blast furnace slag discharged from the blast furnace to the glass melting furnace through the insulation slag bag, during which the temperature of the blast furnace slag is not lower than 1350°C;
[0057] Step 2: Put the weighed quartz sand, sodium fluorosilicate, soda ash, fluorite, ammonium dihydrogen phosphate, and zinc oxide into the mixer and mix them evenly to form a mixture, and add the mixture into the preheating furnace Carry out preheating treatment, preheat to 400 ~ 600 ℃ and add to the glass melting furnace;
[0058] Step 3: After the mixture is preheated, it is in gentle contact with the blast furnace slag in the glass melting furnace, and the blast furnace slag in the glass melting furnace and the mixture are heated...
Embodiment 2
[0064] Weigh raw materials: (kg)
[0065] Blast furnace slag 50, quartz sand 30, sodium fluorosilicate 10, soda ash 15, fluorite 4, ammonium dihydrogen phosphate 2.
[0066] Preparation of slag stone:
[0067] Step 1: Transfer 50 kg of blast furnace slag discharged from the blast furnace to the glass melting furnace through the insulation slag bag, during which the temperature of the blast furnace slag is not lower than 1350°C;
[0068] Step 2-step 4: same as embodiment 1;
[0069] Step 5: quickly send the slab into an annealing and crystallization kiln for heat treatment: keep it at 650°C for 2 hours for nucleation treatment, then raise the temperature to 860°C at a rate of 5°C / min and hold it for 1.5 hours for crystallization treatment, Then carry out natural cooling, and cool to room temperature after 2-4 hours;
[0070] Step 6: Cutting, surface grinding and polishing the original slag stone slab as required to obtain slag stone.
[0071] The slag stone material provide...
Embodiment 3
[0073] Blast furnace slag 60, quartz sand 30, sodium fluorosilicate 5, soda ash 9, fluorite 3, ammonium dihydrogen phosphate 1, zinc oxide 2.
[0074] Preparation of slag stone:
[0075] Step 1: Transfer 60 kg of blast furnace slag discharged from the blast furnace to the glass melting furnace through the insulation slag bag, during which the temperature of the blast furnace slag is not lower than 1350°C;
[0076] Step 2-step 3: same as embodiment 1;
[0077] Step 4: The mold is preheated at a constant temperature of 600° C. in an electric furnace for more than 4 hours, and the above-mentioned melt is poured into a preheated mold at a pouring temperature not lower than 400° C. to make a slab with a thickness of 15 mm;
[0078] Step 5: Send the poured slab together with the mold into the annealing and crystallization kiln for heat treatment: heat at 750°C for 1 hour for nucleation treatment, then raise the temperature to 930°C at a rate of 3°C / min and hold for 0.5 hours for cr...
PUM
Property | Measurement | Unit |
---|---|---|
Flexural strength | aaaaa | aaaaa |
Flexural strength | aaaaa | aaaaa |
Flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap