Biomedical material and preparation method thereof

A technology for biomedical materials and products, applied in electrolytic coatings, polyester coatings, anodic oxidation, etc.

Inactive Publication Date: 2015-01-28
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a new biomedical material and its preparation method in view of the outstanding problems existing in the existing biomedical materials and their application technologies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biomedical material and preparation method thereof
  • Biomedical material and preparation method thereof
  • Biomedical material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] The sample of AZ91 magnesium alloy in mold casting state was taken as the research object. Using distilled water as solvent, prepare 20.0g / L sodium chloride solution as anodic polarization electrolyte. Connect the equal-area samples of the same material to the wires, then connect them to the two output ports of the sinusoidal AC power supply, and immerse them in the above-mentioned electrolyte with a temperature control of 25°C, keep the distance between the samples at 3cm, and use a constant current of 1.0mA / cm at 50Hz 2 After processing for 30 minutes, it was found that the surface of the sample was evenly distributed with finely crushed pits with the same size and depth visible to the naked eye. The washed and dried anodized sample and the stainless steel cylinder form an electrode pair, the sample is connected to the negative pole of the DC power supply, and the stainless steel cylinder is connected to the positive pole of the DC power supply, respectively immersed ...

Embodiment 2

[0062] The sample of high-purity magnesium as cast metal was taken as the research object. Except that the concentration of sodium chloride was changed to 100.0g / L, the other conditions of anodic polarization were controlled the same as in Example 1. It was found that, except that the area of ​​a single pit increased, the density of pits and their distribution uniformity decreased, the others were the same as in the implementation example 1. Except that the concentration of magnesium chloride was changed to 0.5g / L, other conditions and results of cathodic deposition were the same as in Example 1. Except that the temperature is changed to 350°C and the time is changed to 24h, the control and results of other heat treatment conditions are the same as in Example 1. Using chloroform as a solvent, first prepare four parts of 30.0g / LPLLA solution, then add 10.0g / L magnesium hydroxide and pure magnesium powder (spherical, median particle size d 50 =47 μm), β-TCP and CPP, stirred ev...

Embodiment 3

[0064] The sample of AZ31 magnesium alloy in mold casting state was taken as the research object. Except that the concentration of sodium chloride was changed to 20.0 mg / L, other conditions of anodic polarization were controlled as in Example 1. It was found that the treatment effect was the same as in Example 1 except that the density and depth of pits were reduced. Except that the concentration of magnesium chloride was changed to 150.0g / L, other conditions and results of cathodic deposition were the same as in Example 1. Except that the temperature was changed to 550° C. and the time was changed to 1 h, the control and results of other heat treatment conditions were the same as in Example 1. Using chloroform as solvent, prepare 75.0g / LPLLA solution, marked as solution S 08 ; Take ethanol as dispersant (liquid), add 0.5g / L magnesium hydroxide (solid dispersed phase), stir well to obtain a suspension, marked as solution S 09 . Using dichloromethane as a solvent, first prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses biomedical material and a preparation method thereof. The preparation method includes: 1, melting and forming; 2, polarizing an anode; 3, depositing the anode; 4, performing thermal treatment; 5, coating. The biomedical material comprises a pure magnesium or magnesium-alloy base and a functional film which covers the surface of the base and which has the functions of degradation protection and self-degradation. The biomedical material features controllability, full degradation and full absorption, and the strict requirements for ideal features of the degradable biomaterial are met. The biomedical material has the advantages that an optimal solution is provided for the absorbable biomedical material, especially the contradiction between biodegradability and degrading speed control in medical magnesium alloy, and related materials and techniques are applicable to common medical instruments and are more competitive in production of high-end medical instruments, such as implant instruments, especially 'secondary-operation-free' implants.

Description

technical field [0001] The invention belongs to the technical field of manufacturing and application of biomedical new materials and medical device products, and in particular relates to a biomedical new material and a preparation method thereof. Background technique [0002] With the development of social economy and the improvement of living standards, human beings are paying unprecedented attention to their own medical and health undertakings. The increasing pressure of survival, the accelerated pace of life, the intensification of environmental pollution, the frequent occurrence of food, transportation and production safety accidents, local wars, and natural disasters have caused diseases and traumas to become the ever-lingering haze of human beings. As an important means of modern medicine—an important basis and component of medical devices, biomaterials are used for the diagnosis and treatment of diseases, the repair, replacement or function enhancement of tissues and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D7/24B05D3/10C25D11/30C25D9/12C09D167/04C09D7/12
Inventor 张永君贾书功李爱红董连军夏兰梅沈军陶胜
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com