Preparation of afi-structured aluminum phosphate molecular sieve membrane supported by porous alumina carrier

A technology of aluminum phosphate molecular sieve and porous alumina, which is applied in the direction of molecular sieve characteristic silicoaluminophosphate, molecular sieve and alkali exchange phosphate, etc. Good gas separation permeability, environmentally friendly effect

Active Publication Date: 2016-06-15
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above preparation methods all have certain shortcomings: the in situ synthesis method has relatively strict requirements on the substrate and synthesis conditions; the secondary synthesis method inevitably requires pre-prepared nano-scale molecular sieve crystals as seed crystals, and the coating process is cumbersome and complicated. ; In addition, since these two methods are based on hydrothermal synthesis technology, the self-generated pressure of the system generated during the synthesis process will lead to certain safety hazards; in addition, a large amount of acid-base waste liquid generated during the synthesis process will also cause certain damage to the environment. Pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of afi-structured aluminum phosphate molecular sieve membrane supported by porous alumina carrier
  • Preparation of afi-structured aluminum phosphate molecular sieve membrane supported by porous alumina carrier
  • Preparation of afi-structured aluminum phosphate molecular sieve membrane supported by porous alumina carrier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Add 65.7 grams of 1-butyl-3-methylimidazolium bromide ionic liquid into a 100 ml beaker, heat up to 100°C, evenly add 0.05 gram of hydrofluoric acid with a mass concentration of 40%, stir for 2 hours until uniform, and Wherein dripping 0.575 gram mass concentration is the phosphoric acid of 85%, evenly adds 0.0825 gram tetraethylammonium chloride then, P 2 o 5 :F - : The molar ratio of organic amine: ionic liquid is 1: 0.4: 0.2: 120, continue to stir for 10 minutes, then pour the reaction solution into the reactor in which the δ-circular flake-shaped alumina carrier has been placed in advance, and pay attention to the fact that the carrier must be completely Immersed in the reaction solution, the amount ratio of the support body to the precursor reaction solution is 0.5 (cm 2 ·ml -1 surface area of ​​the support), the reactor was heated to 150°C and kept for 36 hours, then the reactor was lowered to room temperature, the support was taken out, ultrasonically washed t...

Embodiment 2

[0033] Add 65.7 grams of 1-butyl-3-methylimidazolium bromide ionic liquid into a 100 ml beaker, heat up to 90°C, evenly add 0.3 grams of hydrofluoric acid with a mass concentration of 40%, stir for 2 hours until uniform, and Wherein dripping 3.45 gram mass concentration is the phosphoric acid of 85%, evenly adds 0.495 gram tetraethylammonium chloride then, P 2 o 5 :F - : The molar ratio of organic amine: ionic liquid is 1: 0.4: 0.2: 20, continue to stir for 10 minutes, then pour the reaction solution into the reactor in which the γ-square flake-shaped alumina carrier is placed in advance, and pay attention to the fact that the carrier must be completely submerged into the reaction solution, the amount ratio of the support body to the precursor reaction solution is 0.6 (cm 2 ·ml -1 surface area of ​​the support), the reactor was heated to 120°C and kept for 480 hours, then the reactor was lowered to room temperature, the support was taken out, ultrasonically washed three tim...

Embodiment 3

[0035] Add 110 grams of 1-butyl-3-methylimidazolium bromide ionic liquid into a 100 milliliter beaker, heat up to 100 ° C, evenly add 0.625 grams of hydrofluoric acid with a mass concentration of 40%, stir for 2 hours until uniform, and Wherein dripping 0.2875 gram mass concentration is the phosphoric acid of 85%, evenly adds 2.625 gram tetraethylammonium chlorides then, P 2 o 5 :F - : The molar ratio of organic amine: ionic liquid is 1: 10: 10: 400, continue to stir for 10 minutes, then pour the reaction solution into the reactor in which the θ-square flake-shaped alumina carrier has been placed in advance, and pay attention to the fact that the carrier must be completely submerged into the reaction solution, the amount ratio of the support body to the precursor reaction solution is 0.4 (cm 2 ·ml -1 surface area of ​​the support), the temperature of the reactor was raised to 280° C., and kept for 0.5 hours, then the reactor was lowered to room temperature, the carrier was ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an AFI structure aluminophosphate molecular sieve membrane supported by a porous alumina carrier. According to the method, an ionic liquid is taken as a reaction medium, and under the auxiliary effects of organic amine and a mineralizer, the porous alumina carrier reacts with a phosphorus-containing compound, so that the AFI structure microporous aluminophosphate molecular sieve membrane can be synthesized on the surface of the alumina carrier. The AFI molecular sieve membrane prepared by the method disclosed in the invention has good gas permeation separation performance. The method provided in the invention is characterized by synthesis of the molecular sieve membrane in the ionic liquid, thus overcoming self-generation of high pressure by the system during conventional hydrothermal synthesis of a molecular sieve membrane. The method involved in the invention has the advantages of environmental-friendliness and simple operation.

Description

technical field [0001] The invention relates to an ionothermal synthesis method of a microporous aluminum phosphate molecular sieve membrane, more precisely relates to an aluminum phosphate molecular sieve membrane with an AFI zeolite structure and a preparation method thereof. Background technique [0002] Molecular sieves are a class of inorganic microporous materials with regular pore structures. For decades, researchers and engineers have been working on the research and synthesis of molecular sieves with different pore characteristics as catalysts for specific chemical reaction processes. With the continuous advancement of science and technology, people gradually realize that if molecular sieves can be prepared into membranes, they can combine the characteristics of molecular sieve materials and film materials to greatly broaden their application fields: using the precise molecular sieving function of molecular sieve micropores At the same time, combined with the chara...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B37/08C01B39/54
Inventor 田志坚李科达厉晓蕾王磊马怀军徐仁顺王炳春
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI