Sintered flux for submerged-arc welding for nickel-based alloy

A technology of sintering flux and submerged arc welding, which is applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc., and can solve problems such as cracks, weld porosity, weld strength, and plasticity decline

Active Publication Date: 2013-11-20
HOHAI UNIV CHANGZHOU
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the weld is well formed and slag is easy to remove, the resulting weld is prone to defects such as pores and cracks
Moreover, the weld metal obtained by using these fluxes ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] According to the design component content of the present invention, the flux powder is prepared, and the flux adopts the common sintered flux production method, that is: dry mixing, wet mixing, granulation, low-temperature drying, and high-temperature drying of the powder composed of the components. The sintered flux is prepared by sintering, sieving, etc., and the particle size of the finished product is within the range of φ0.5-5mm. Considering the decomposition characteristics of carbonate, the sintering temperature is controlled in the range of 600-800 °C, and its composition is shown in Table 1.

[0021] Table 1 The specific composition of flux (by weight percentage)

[0022] CaF 2 MgO Al 2 o 3 CaCO 3 Ti mn 35 15 34 6 5 5

[0023] The developed flux and the nickel-based alloy submerged arc welding wire with a diameter of 3.2mm are used for cooperating tests. The MZ-1000 DC submerged arc automatic welding ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses sintered flux for submerged-arc welding for nickel-based alloy, and belongs to the technical field of welding materials. The sintered flux comprises, by weight, 25-35% of CaF<2>, 10-20% of MgO, 30-40% of Al<2>O<3>, 5-10% of CaCO<3>, 3-8% of Ti and 3-8% of Mn. The sintered flux has the advantages of stable electric arcs, easiness in removing slag, attractive formed welding seams, smooth transition and capability of overcoming shortcomings such as welding cracks and the like in a welding procedure.

Description

technical field [0001] The invention relates to a sintered flux for nickel-based alloy submerged arc welding, which belongs to the technical field of welding materials. The flux is suitable for submerged arc welding of nickel-based alloy structural parts in petrochemical, metallurgy, atomic energy, ocean development, aviation, aerospace and other industries. Background technique [0002] Nickel-based alloys (Ni≥55%) are important structural materials, which are particularly sensitive to harmful components and can dissolve gases, so welding is difficult: on the one hand, liquid nickel can dissolve a large amount of O 2 、H 2 , and CO gas, and the solubility drops sharply during the condensation period, causing pores and hydrogen embrittlement, and due to the oxidation of nickel during welding, Ni-NiO low-melting eutectics are formed, and these low-melting eutectics are distributed on the grain boundaries during crystallization. It is prone to brittleness; on the other hand, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/362
Inventor 杨可
Owner HOHAI UNIV CHANGZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap