Super-specular anti-scraping transfer film and preparation method thereof

A super-mirror, transfer film technology, applied in the field of transfer film, can solve the problems of poor scratch resistance of leather transfer film, difficult to meet decorative needs, low mirror gloss, etc., to improve scratch resistance and mirror effect, decorative effect is good, High specular gloss effect

Inactive Publication Date: 2013-12-11
DONGGUAN GUODING OPTICAL MEMBRANE TECH
View PDF7 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The Chinese invention patent with application number 200910052388.9 discloses a paint transfer film for decoration, which consists of five layers from outside to inside: bearing layer, release layer, printing layer, paint layer and adhesive layer, among which, The release layer is coated with a release agent. The release agent is one or more of water-based wax emulsion, acrylic emulsion and pure acrylic emulsion. However, the film-forming properties of water-based wax emulsion, acrylic emulsion and pure acrylic emulsion are poor. , no recoatability, the release layer formed by coating is thin, not scratch-resistant, and the mirror gloss is low, and the decorative effect is poor
[0004] The Chinese invention patent with application number 201210262380.7 discloses a mirror transfer film and its production method and application. The mirror transfer film includes a carrier layer, a release layer, a transparent protective layer, a color layer, Aluminum layer, connecting layer and adhesive layer, among which, the release layer is composed of cellulose resin containing silicone oil. The release layer composed of this cellulose resin is prone to rainbow light, and there is a certain degree of haze, the surface brightness is low, and the mirror effect Not strong, it is difficult to meet the increasing decoration needs of the majority of users
[0005] In summary, the problems of poor scratch resistance and low mirror brightness of leather transfer film need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-specular anti-scraping transfer film and preparation method thereof
  • Super-specular anti-scraping transfer film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A super-mirror anti-scratch transfer film of the present embodiment comprises the following preparation steps:

[0038] a, get the base film layer 1, the base film layer 1 is a PET film;

[0039] B, the water-based polyurethane that is 50 parts by weight, the methyl alcohol of 10 parts and the water of 10 parts are mixed and stirred evenly, is modulated into water-based release coating, and the viscosity of water-based release coating is 30cps;

[0040] C, the water-based release coating prepared in the step b is dropped into the first coating trough of the coating machine, utilizes the first coating roller to coat the water-based release coating on the surface of the PET film, the first coating roller The coating speed is 30m / min to form a water-based release coating;

[0041] d. The PET film coated with water-based release coating is transported to the drying device for drying treatment. After the water-based release coating is dried, it becomes the water-based relea...

Embodiment 2

[0045] A super-mirror anti-scratch transfer film of the present embodiment comprises the following preparation steps:

[0046] a, get the base film layer 1, the base film layer 1 is a PET film;

[0047] B, the water-based polyurethane that is 60 parts by weight, the methyl alcohol of 20 parts and the water of 20 parts are mixed and stirred evenly, is modulated into water-based release coating, and the viscosity of water-based release coating is 26cps;

[0048] C, the water-based release coating prepared in the step b is dropped into the first coating trough of the coating machine, utilizes the first coating roller to coat the water-based release coating on the surface of the PET film, the first coating roller The coating speed is 60m / min to form a water-based release coating;

[0049] d. The PET film coated with water-based release coating is transported to the drying device for drying treatment. After the water-based release coating is dried, it becomes the water-based relea...

Embodiment 3

[0053] A super-mirror anti-scratch transfer film of the present embodiment comprises the following preparation steps:

[0054] a, get the base film layer 1, the base film layer 1 is a PET film;

[0055] B, the water-based polyurethane that is 70 parts by weight, the isopropanol of 30 parts and the water of 30 parts are mixed and stirred evenly, is modulated into water-based release coating, and the viscosity of water-based release coating is 20cps;

[0056] C, the water-based release coating prepared in the step b is dropped into the first coating trough of the coating machine, utilizes the first coating roller to coat the water-based release coating on the surface of the PET film, the first coating roller The coating speed is 100m / min to form a water-based release coating;

[0057] d. The PET film coated with water-based release coating is transported to the drying device for drying treatment. After the water-based release coating is dried, it becomes the water-based release...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of transfer films, in particular to a super-specular anti-scraping transfer film and a preparation method thereof. The preparation method of the super-specular anti-scraping transfer film comprises the following steps that a PET (Polyethylene Terephthalate) thin film is taken; waterborne polyurethane, an alcohol organic solvent and water in parts by weight are mixed and stirred uniformly, and blended into waterborne release dope; the surface of the PET thin film is coated with the blended waterborne release dope to form a waterborne release coating layer; the waterborne release coating layer is dried to be a waterborne release layer; a semifinished PET thin film loaded with the waterborne release layer is prepared; the outer surface of the waterborne release layer is coated with information coating layer dope to form an information coating layer; a vacuum aluminum coated layer and a gum application layer are arranged on the surface of the information coating layer sequentially; and the finished super-specular anti-scraping transfer film is prepared. The super-specular anti-scraping transfer film is high in scraping resistance, and high in specular glossiness, and the preparation method of the super-specular anti-scraping transfer film is simple in technology and high in production efficiency.

Description

technical field [0001] The invention relates to the technical field of transfer films, in particular to a super-mirror anti-scratch transfer film and a preparation method thereof. Background technique [0002] The transfer film is an intermediate carrier, which exists on the transfer paper base or plastic base, carries the printed or printed pattern, and is used to transfer to a layer of chemical elastic film on the printed article. It is widely used in advertising, decoration etc. At present, in order to achieve the functions of rich color, fineness, brilliance, durability, wear resistance and high temperature resistance of leather, it is generally necessary to print on the surface of leather. Due to the unevenness of leather products, transfer technology is generally used in the process of selecting printing. Leather The transfer film came into being. When in use, the leather transfer film is hot-bonded with artificial leather, PU leather and genuine leather by pressing a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B27/36B32B27/40B32B15/08B32B15/20C09D175/04C09D4/02B41M5/00
Inventor 林丽芬
Owner DONGGUAN GUODING OPTICAL MEMBRANE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products