Preparation method of metal coated PVC (Polyvinyl Chloride) sectional material for improving plasticity

A plasticity and metal film technology, applied in the direction of rosin adhesives, adhesives, etc., can solve the problems of uneven bonding between metal and PVC, difficult continuous production, and poor adhesion of adhesives, so as to achieve plasticity Strong, solves the effect of easy aging, uniform and strong bonding

Inactive Publication Date: 2014-04-16
山东华信塑胶股份有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above-mentioned method is to apply the adhesive on the surface of the inner lining without special extruder processing, the adhesive effect of the adhesive is not good, the bonding between the metal and PVC is uneven, the bonding strength is not high, and it is easy to cause metal Layer by layer, and it is not easy to carry out continuous production
The prepared PVC-aluminum-plastic co-extruded profile has low plasticity and is not conducive to production and processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The preparation of the PVC profile with aluminum film on the surface to improve plasticity, the thickness of the aluminum film is 0.3mm, the steps are as follows:

[0037] (1) Mixing: 100kg SG-5 PVC resin powder, 10kg light calcium carbonate, 3.5kg calcium zinc stabilizer, 0.8kg stearic acid, 0.5kg calcium stearate, 0.5kg PE wax, 6kg CPE, 3kg of anti-impact ACR, 1kg of processing aid type ACR and 5kg of titanium dioxide were mixed in a high-speed mixer and the temperature was controlled at 120°C. After reaching the temperature, it was transferred to a cold mixer to cool to 40°C and discharged to obtain a mixed material;

[0038] (2) Extrusion of PVC profiles, vacuum cooling and shaping: Put the compounded materials into a 65-type conical twin-screw extruder to melt and extrude, and the temperature of the extruder is controlled at 160-205°C; after vacuum cooling and shaping, Get PVC profiles;

[0039] (3) Coating the surface of the aluminum film with hot melt adhesive: ...

Embodiment 2

[0043] The preparation of PVC profiles with a copper-clad film on the surface to improve plasticity, the thickness of the copper film is 2mm, the steps are as follows:

[0044] (1) Mixing: 100kg SG-4 PVC resin powder, 12kg active calcium carbonate, 3.8kg calcium zinc stabilizer, 0.5kg stearic acid, 0.3kg calcium stearate, 0.6kg PE wax, 3kg CPE, 3kg Impact-resistant ACR, 0.8kg of processing aid type ACR and 4kg of titanium dioxide were mixed in a high-speed mixer and controlled at a temperature of 125°C. After reaching the temperature, it was transferred to a cold mixer to cool to 45°C and discharged to obtain a mixed material;

[0045] (2) Extrusion of PVC profiles, vacuum cooling and shaping: Put the compounded materials into an 80-type conical twin-screw extruder to melt and extrude, and the temperature of the extruder is controlled at 165-200°C; after vacuum cooling and shaping, Get PVC profiles;

[0046] (3) Coating the surface of the copper film with hot melt adhesive: M...

Embodiment 3

[0050] The preparation of the PVC profiles coated with stainless steel film on the surface to improve plasticity, the thickness of the stainless steel film is 6mm, the steps are as follows:

[0051] (1) Mixing: 100kg SG-5 type PVC resin powder, 25kg active calcium carbonate, 5kg organotin stabilizer, 0.5kg stearic acid, 0.5kg calcium stearate, 1.2kg PE wax, 10kg CPE, 5kg anti Punch ACR, put 3kg of processing aid type ACR and 8kg of titanium dioxide into a high-speed mixer and mix and control the temperature at 135°C. After reaching the temperature, transfer to a cold mixer to cool to 30°C and discharge to obtain the mixed material;

[0052] (2) Extrusion of PVC profiles, vacuum cooling and shaping: Put the compounded materials into a 90-type parallel twin-screw extruder to melt and extrude, and the temperature of the extruder is controlled at 180-205°C; after vacuum cooling and shaping, the obtained PVC profiles;

[0053] (3) Coating the surface of stainless steel film with h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a metal coated PVC (Polyvinyl Chloride) sectional material for improving plasticity. The PVC sectional material with the surface coated with a metal film is prepared by material mixing, extrusion, vacuum cooling and sizing of the PVC sectional material, coating of hot melt adhesive on the surface of the metal film, coating of the metal film on the surface of the PVC sectional material, cutting and molding. According to the preparation method provided by the invention, a PVC raw material and the hot melt adhesive are respectively treated by a separate extruder, so that the bonding strength of the hot melt adhesive is high, the bonding of the metal film is uniform and strong, the bonding strength is high, delamination is unlikely to occur, and the continuous production of the hot melt adhesive, PVC raw material powder and PVC sectional material products with the surfaces coated with the metal films can be realized.

Description

technical field [0001] The invention relates to a method for preparing a metal-coated PVC profile with improved plasticity, and belongs to the technical field of composite profile preparation. Background technique [0002] The materials used in the doors and windows of housing construction have increasingly replaced the original wooden windows and steel windows with aluminum alloy or plastic steel, and the use of plastic steel doors and windows is more common. Plastic-steel doors and windows have many advantages, and are known as a new generation of energy-saving doors and windows rising after wooden windows, steel windows, and aluminum alloy windows. Compared with aluminum windows and steel windows, they are superior in sealing, heat preservation, and corrosion resistance. Coordinated with similar buildings, it has better aesthetics and can meet individual needs, and has good fire resistance and insulation. However, plastic steel profiles will age and change color under lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C69/00B29C47/00B29C65/02C08L27/06C08L23/28C08K13/02C08K3/26C09J123/08C09J193/04
Inventor 汤毅李小虎
Owner 山东华信塑胶股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com