A method for treating waste residue containing arsenic by cement rotary kiln

A cement rotary kiln and waste residue technology, which is applied in the field of disposal of arsenic waste residue, resource utilization, and harmless arsenic waste residue, can solve problems such as health damage to operators, serious secondary pollution, and surrounding environmental pollution, and avoid secondary pollution. Secondary pollution, health protection, and the effect of reducing environmental pollution

Active Publication Date: 2015-11-25
云南省环境科学研究院(中国昆明高原湖泊国际研究中心)
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. The energy consumption is large. Since the volatilization temperature of arsenic is 600-800°C, it is necessary to add fuel to realize the volatilization of arsenic and achieve the purpose of harmless disposal of arsenic-containing waste residue, so the energy consumption is relatively high
[0007] 2. Secondary pollution is serious. During the incineration of arsenic-containing waste, arsenic is collected in the form of compound dust in the dust collection system. However, the current pure arsenic-containing waste incineration disposal equipment inevitably emits a small amount in the tail gas. At the same time, there will also be certain unorganized emissions, which will pollute the surrounding environment and cause damage to the health of operators.
[0008] 3. The final disposal has not been realized, and the disposed waste residue still needs further disposal. After the arsenic-containing waste residue is treated, there may still be traces of arsenic or other harmful elements in the waste residue. Heavy metal pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for treating waste residue containing arsenic by cement rotary kiln
  • A method for treating waste residue containing arsenic by cement rotary kiln
  • A method for treating waste residue containing arsenic by cement rotary kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Example 1: The method of treating arsenic-containing waste residue by cement rotary kiln:

[0031] Raw material 1: arsenic-containing waste residue

[0032] The main components of arsenic-containing waste residue are shown in the table below:

[0033]

[0034] Raw material 2: limestone 81.92%, sandstone 8.65%, pyrite slag 2.23%, laterite 3.60%, phosphorus slag 3.0%.

Embodiment 2

[0037] Example 2: The method of treating arsenic-containing waste residue by cement rotary kiln:

[0038] Raw material 1: arsenic-containing waste residue

[0039] The main components of arsenic-containing waste residue are shown in the table below

[0040]

[0041] Raw material 2: limestone 81.12%, sandstone 8.25%, pyrite slag 2.03%, laterite 3.60%, phosphorus slag 3.0%.

[0042] method of execution:

[0043] Under the operating conditions of maintaining the cement kiln as kiln tail temperature: 1050°C, kiln head temperature: 900-1100°C, and rotating speed: 4.1r / min, the weight of raw material (the sum of raw material 1 and raw material 2) based on arsenic-containing waste residue The percentage is 2.0%. The arsenic-containing waste residue is evenly transported to the raw material mill through the feeder, and then sent to the rotary kiln to produce fired cement clinker. The treated cement clinker is analyzed by X-ray diffractometer. Quantitative determination by diffra...

Embodiment 3

[0044] Example 3: The method of treating arsenic-containing waste residue by cement rotary kiln:

[0045] Raw material 1: arsenic-containing waste residue

[0046] The main components of arsenic-containing waste residue are shown in the table below

[0047]

[0048] Raw material 2: limestone 80.12%, sandstone 7.26%, pyrite slag 1.93%, laterite 3.60%, phosphorus slag 3.0%.

[0049] method of execution:

[0050] Under the operating conditions of maintaining the cement kiln as kiln tail temperature: 1050°C, kiln head temperature: 900-1100°C, and rotating speed: 4.1r / min, the weight of raw material (the sum of raw material 1 and raw material 2) based on arsenic-containing waste residue If the percentage is 4.0%, X-ray diffractometer will be used to carry out diffraction quantitative determination on the treated cement clinker, and the content of arsenic in the clinker is between 196.57 mg / kg and 218.70 mg / kg. Using "Solid Waste Leaching Toxic Leaching Method Sulfuric Acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for treating arsenic-containing waste residues by using a cement rotary kiln, belonging to the field of solid waste and hazardous waste treatment and disposal technologies. The method comprises the steps of (1) mixing the arsenic-containing waste residues with a cement raw material to obtain a raw material for preparing a cement clinker, wherein the arsenic-containing waste residues account for 0.6-4.0% of the weight of the raw material; and (2) putting the raw material obtained by mixing in the step (1) into the cement rotary kiln to prepare an arsenic-containing cement clinker. The method disclosed by the invention has the advantages that the arsenic-containing waste residues are treated through the existing dry method cement rotary kiln to facilitate harmless and resource utilization of the arsenic-containing waste residues, potential environmental pollution risks and secondary pollution during harmless treatment of the arsenic-containing waste residues are effectively controlled, and the environmental benefit and economic benefit are obvious.

Description

technical field [0001] The invention belongs to the technical field of solid waste and hazardous waste treatment and disposal, and specifically relates to a method for treating arsenic-containing waste residue by a cement rotary kiln, and more specifically relates to a method for disposing of arsenic-containing waste residue while using the existing dry-process cement production line to produce cement , a method for realizing harmless and resourceful utilization of arsenic-containing waste residue. Background technique [0002] Arsenic is a metalloid notoriously toxic and has many allotropes. Arsenic exists widely in nature, and arsenic and its compounds are widely used. With the mass production of arsenic, a large amount of arsenic-containing waste residue (also known as arsenic-containing waste) is also produced. Its long-term stockpiling and rainwater leaching have caused serious damage. Environmental issues. At present, there are a large number of arsenic-containing wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/24
CPCY02P40/145Y02P40/10
Inventor 吴学勇张涛尚江涛牛学奎王金华毕廷涛
Owner 云南省环境科学研究院(中国昆明高原湖泊国际研究中心)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com