Preparation method for aluminum-plated paper packaging material for cigarettes

A packaging material and aluminized paper technology, applied in the field of packaging materials, can solve the problems of difficult to control product color difference, poor surface finish of aluminized paper, rough nitrocellulose coating, etc., and achieve the effect of reducing production costs

Inactive Publication Date: 2014-05-28
WUXI HUANGSHENG PACKING PROD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vacuum aluminized paper made by this process method has the following disadvantages: because the nitrocellulose coating on the surface of the aluminized paper becomes rough when the polyester film is peeled off, the surface finish of the aluminized paper is poor and lacks l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for preparing aluminized paper packaging material for cigarettes, the method comprising the steps of:

[0016] 1) Coating a release coating on the polyester film and drying it at 142°C to form an easy-release coating with a thickness of 2g / square meter; wherein the composition of the release coating is: acetate fiber 18-22% plain resin, 7-9% divinyl chloride resin, 24-26% acrylic resin, 1.5-2.5% polypropylene wax, 1-2% dioctyl phthalate, titanate coupling agent 0.5-1.5%, 2-hydroxy-4-methoxybenzophenone 0.2-0.4%, dibutyltin dilaurate 0.1-0.2%, the balance is butanone;

[0017] 2) Heat and melt metal aluminum in a vacuum environment, and spray it on the above-mentioned easy-peelable coating to form a vacuum aluminized transfer film;

[0018] 3) Apply an adhesive on the aluminum film of the aluminized transfer film and paste a composite paper layer, dry at 60°C, and then cool and solidify at room temperature to form a composite semi-finished product;

[0019] 4)...

Embodiment 2

[0021] A method for preparing aluminized paper packaging material for cigarettes, the method comprising the steps of:

[0022] 1) Coating a stripping coating on the polyester film and drying it at 146°C to form an easy-peeling coating with a thickness of 1.9g / square meter; wherein the composition of the stripping coating is: acetic acid Cellulose resin 18-22%, dibasic vinyl chloride resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling Agent 0.5-1.5%, 2-hydroxy-4-methoxybenzophenone 0.2-0.4%, dibutyltin dilaurate 0.1-0.2%, the balance is butanone;

[0023] 2) Heat and melt metal aluminum in a vacuum environment, and spray it on the above-mentioned easy-peelable coating to form a vacuum aluminized transfer film;

[0024] 3) Apply an adhesive on the aluminum film of the aluminized transfer film and paste a composite paper layer, dry at 90°C, and then cool and solidify at room temperature to form a composite semi-finished product...

Embodiment 3

[0027] A method for preparing aluminized paper packaging material for cigarettes, the method comprising the steps of:

[0028] 1) Coating a stripping coating on a polyester film and drying it at 144°C to form an easy-peeling coating with a thickness of 1.95g / square meter; wherein the composition of the stripping coating is in weight percent: acetic acid Cellulose resin 18-22%, dibasic vinyl chloride resin 7-9%, acrylic resin 24-26%, polypropylene wax 1.5-2.5%, dioctyl phthalate 1-2%, titanate coupling Agent 0.5-1.5%, 2-hydroxy-4-methoxybenzophenone 0.2-0.4%, dibutyltin dilaurate 0.1-0.2%, the balance is butanone;

[0029] 2) Heat and melt metal aluminum in a vacuum environment, and spray it on the above-mentioned easy-peelable coating to form a vacuum aluminized transfer film;

[0030] 3) Apply an adhesive on the aluminum film of the aluminized transfer film and paste a composite paper layer, dry at 75°C, and then cool and solidify at room temperature to form a composite semi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for an aluminum-plated paper packaging material for cigarettes. The preparation method comprises the following steps: (1) coating a polyester thin film with stripping coating, wherein the stripping coating layer consists of the components in percentage by weight: 18-22 percent of cellulose acetate resin, 7-9 percent of bi-chloride-vinyl resin, 24-26 percent of acrylic resin, 1.5-2.5 percent of polypropylene wax, 1-2 percent of dioctyl phthalate, 0.5-1.5 percent of a titanate coupling agent, 0.2-0.4 percent of 2-hydroxy-4-methoxybenzophenone, 0.1-0.2 percent of dibutyltin dilaurate and the balance of butanone; (2) performing vacuum aluminum plating; (3) adhering composite paper; (4) performing stripping to obtain the aluminum-plated paper packaging material for the cigarettes.

Description

technical field [0001] The invention relates to the technical field of packaging materials, in particular to a method for preparing an aluminized paper packaging material for cigarettes. Background technique [0002] Vacuum aluminized paper is a packaging material used in the packaging industry in recent years. It has a good metallic texture and is suitable for processing on embossing machines and high-speed cross-cutting machines. It has the advantages of avoiding light, moisture, and degradability. It can replace Aluminized plastic films and pure aluminum thin composite materials have broad prospects due to their low aluminum consumption, and have been widely used in the packaging and decoration of cigarettes, food, medicine, and trademarks. At present, the vacuum aluminized paper with coloring effect all adopts the pre-coloring method. The process method is to coat a polyester film with an easy-peelable coating made of nitrocellulose, and then coat it on the easy-peelable...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/10D21H19/60D21H19/04
Inventor 黄盛
Owner WUXI HUANGSHENG PACKING PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap