Digital holographic anti-counterfeiting glue cap and preparation method thereof

A holographic anti-counterfeiting, plastic cap technology, applied in the directions of copying/marking methods, locking equipment, printing, etc., can solve the problems of low market exclusivity, reduced anti-counterfeiting strength, and consumers cannot distinguish the authenticity from the fake, and achieves a large number of anti-counterfeiting features, Improve the effect of anti-counterfeiting

Active Publication Date: 2014-08-06
SHANDONG TAIBAO PREVENTING COUNTERFEIT
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, the anti-counterfeiting trademark of the enterprise will lose its anti-counterfeiting effect and significance, causing huge economic losses and immeasurable serious consequences to the enterprise, and also seriously damaging the interests of consumers and affecting the market order.
2. Use embedded anti-counterfeiting materials (ultraviolet ink anti-counterfeiting materials, laser holographic anti-counterfeiting materials, precision printing anti-counterfeiting materials, pattern anti-counterfeiting materials, light angle color-changing anti-counterfeiting materials or polymer holographic anti-counterfeiting materials, etc.) for anti-counterfeiting, due to the high penetration rate of all anti-counterfeiting materials , low market exclusivity, simple manufacturing process greatly reduces its anti-counterfeiting strength
3. Using printed QR codes for anti-counterfeiting, the disadvantage is that because the printed QR codes are fixed, it is easy for counterfeiters to carry out counterfeit printing, so that consumers cannot distinguish the authenticity and bring losses to consumers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 10000 products:

[0048] 1. Select the base material: PVC is used as the base material for the production of rubber caps, the thickness is 0.1mm, the shrinkage rate is 25% in the longitudinal direction and 45% in the transverse direction, the folding diameter is 25mm, and the sealing strength is 100g / cm;

[0049] 2. Plate-making printing: the engraving depth of the gravure printing plate is 45μm, the mesh number of the plate roller is customized according to the printing requirements, the pressure is 0.1Mpa, the winding tension is 1A, the unwinding tension is 0.5A, the traction tension is 1A, and the photoelectric device for color registration should be well maintained The distance between the reflector and the scanning head is 7mm, and the temperature is 75°C;

[0050] 3. Production of hot stamping foil:

[0051] ①Choose PET with a thickness of 18 μm as the base material to coat the release layer and the information layer. The coating amount is controlled at 0.8g / ㎡, t...

Embodiment 2

[0063] 20000 products:

[0064] 1. Select base material: PVC thickness 0.5mm, shrinkage rate: longitudinal 25%, transverse 47%, folding diameter 500mm, sealing strength 100g / cm;

[0065] 2. Plate-making printing: gravure plate, engraving depth is 47μm, plate roller mesh number is customized according to printing requirements, pressure is 0.3Mpa, winding tension is 2A, unwinding tension is 1.5A, traction tension is 2A, and the photoelectric device for color registration should be well maintained The distance between the reflector and the scanning head is 8mm, and the temperature is 85°C;

[0066] 3. Production of hot stamping foil:

[0067] ①Choose PET with a thickness of 20 μm as the substrate, and coat the release layer and the information layer. The coating amount is controlled at 1g / ㎡, the temperature is 160°C, and the thickness of the release layer is 2 μm; the 180-degree peel strength of the release layer is 0.003KN / m;

[0068] ②Design: Self-designed plate-making anti-...

Embodiment 3

[0079] 30000 products:

[0080] 1. Select base material: PVC thickness 1mm, shrinkage rate: longitudinal 25%, transverse 50%, folding diameter 720mm, sealing strength 100g / cm;

[0081] 2. Plate-making printing: the engraving depth of the gravure printing plate is 50 μm, the mesh number of the plate roller is customized according to the printing requirements, the pressure is 0.5Mpa, the winding tension is 3A, the unwinding tension is 2A, the traction tension is 2.5A, and the distance between the reflective plate and the scanning head is 9mm , temperature 95°C;

[0082] 3. Production of hot stamping foil:

[0083] ①Choose PET with a thickness of 25 μm as the substrate, and coat the release layer and the information layer. The coating amount is controlled at 1.2g / ㎡, the temperature is 180°C, and the thickness of the release layer is 2.5 μm; the release layer is peeled off at 180 degrees The strength is 0.004KN / m;

[0084] ②Design: self-designed, anti-counterfeiting plate-makin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of anti-counterfeiting packages and particularly relates to a digital holographic anti-counterfeiting glue cap and a preparation method thereof. The digital holographic anti-counterfeiting glue cap comprises a glue cap and a thermally-printed foil layer, wherein the glue cap, a printing layer, an aqueous priming coat and the thermally-printed foil layer are sequentially connected, and the thermally-printed foil layer is transferred to the glue cap in a cramping manner. The preparation method comprises the steps of material selection, designing, plate-making, mold pressing, printing, aluminum washing, printing layer coating, code printing, coating transfer, slitting, forming. According to the preparation method, digital holographicanti-counterfeiting thermally-printed foil is transferred to a fixed position of the glue cap by virtue of a cramping transfer technique, so that the holographic and digital anti-counterfeiting techniques are integrated; as the number of anti-counterfeiting characteristics is large, the anti-counterfeiting capability is improved; an anti-counterfeiting mark is replaced by virtue of the digital holographic anti-counterfeiting glue cap so as to achieve an untransferable purpose, and a positioning transfer method of the thermally-printed foil on a PVC (Polyvinyl Chloride) material is realized.

Description

technical field [0001] The invention belongs to the technical field of anti-counterfeiting packaging, in particular to a digital holographic anti-counterfeiting rubber cap and a preparation method thereof. Background technique [0002] At present, all kinds of bottled wines on the market usually use heat-shrinkable plastic caps that prevent secondary use to play an anti-counterfeiting role. Heat shrinkage makes the rubber cap fit closely with the shape of the bottle body. In order to suppress counterfeiting, the following anti-counterfeiting methods are now taken: 1. The method of pasting anti-counterfeiting trademarks is used for anti-counterfeiting. An opportunity to take advantage of. Consumers often only destroy the plastic cap when opening the wine bottle, leaving the anti-counterfeiting trademark intact on the waste rubber cap. Counterfeiters recycle these waste rubber caps with anti-counterfeiting trademarks at high prices, and then cut off the anti-counterfeiting t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B65D55/02B41M3/14B41M5/00
Inventor 张钦永田辰琪巩建宝田茂涛田孝友田丽萍
Owner SHANDONG TAIBAO PREVENTING COUNTERFEIT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com