Mixed neoprene sealant
A technology of sealant and neoprene, applied in the field of sealant, can solve the problems of many ingredients and complex production process, and achieve the effect of simple production, easy availability of raw materials, and improved fluidity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1
[0020] A chloroprene hybrid sealant, the raw materials of which by weight include: chloroprene CR244216 parts, natural rubber 12 parts, low-cis butadiene rubber 8 parts, terpene resin 18 parts, xylene 125 parts, and magnesium oxide 6 parts , 75 parts of talc powder, 11 parts of thickener; firstly mix the neoprene rubber, natural rubber and butadiene rubber in the above raw materials and knead it in an open rubber mixer for 20 minutes, cut the material to obtain flakes, and move the flakes to Soak in 80wt% xylene solution based on the weight of total xylene to obtain a glue solution, the immersion time is not less than 84h; put the glue solution into the kneader and stir evenly, add terpene resin and stir for 15min, then add total talc Stir 50wt% of talc by weight, then add the remaining talc and stir evenly, continue to add magnesium oxide and thickener and stir for 20 minutes to obtain a mixed glue; add the remaining xylene to the mixed glue to adjust the cons...
Example Embodiment
[0021] Example 2
[0022] A chloroprene hybrid sealant, the raw materials of which by weight include: 20 parts of neoprene, 15 parts of natural rubber, 10 parts of butadiene rubber, 20 parts of terpene resin, 150 parts of xylene, 9 parts of magnesium oxide, and talc 85 parts, thickener 13 parts; firstly mix the neoprene rubber, natural rubber and butadiene rubber in the above raw materials and knead in an open rubber mixer for 15 minutes. Soak the glue in 83wt% xylene solution based on the weight of toluene, and the immersion time is not less than 72h; put the glue into the kneader and stir evenly, add the terpene resin and stir for 10 minutes, and then add the glue based on the total talc weight. Stir 45wt% talc powder evenly, then add the remaining talc powder and stir evenly, continue to add magnesium oxide and thickener and stir for 15 minutes to obtain a mixed glue; add the remaining xylene to the mixed glue to adjust the consistency of the glue to 0.45L / min to obtain a ne...
Example Embodiment
[0023] Example 3
[0024] A chloroprene hybrid sealant, the raw materials of which by weight include: 14 parts of neoprene, 10 parts of natural rubber, 7 parts of butadiene rubber, 16 parts of terpene resin, 110 parts of xylene, 4 parts of magnesium oxide, and talc 69 parts and 9 parts of diatomaceous earth; firstly mix the neoprene, natural rubber and butadiene rubber in the above raw materials and knead in an open rubber mixer for 23 minutes. Soak the glue in 78wt% xylene solution based on the weight of toluene to obtain a glue solution, the soaking time is not less than 90h; put the glue into the kneader and stir evenly, add the terpene resin and stir for 18 minutes, and then add the glue based on the total talc weight. Stir the 52wt% talc evenly, then add the remaining talc and stir evenly, continue to add magnesium oxide and diatomaceous earth and stir for 23 minutes to obtain a mixed glue; add the remaining xylene to the mixed glue to adjust the consistency of the glue to 0...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap