Halogen-free flame retardant cable compound

A flame retardant cable material and raw material technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problem of poor flame retardant performance, and achieve the effect of good flame retardant performance, excellent extrusion process performance, and high LOI value

Active Publication Date: 2016-06-01
ANHUI MEITENG SPECIAL ELECTRIC CABLE MATERIALS
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing cable materials have poor flame retardancy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0015] Each raw material was weighed according to the data corresponding to Examples 1-5 in Table 1. The raw materials are mixed on a mixer, plasticized and granulated on a screw extruder to obtain the halogen-free flame-retardant cable material of the present invention.

[0016] Table 1: Halogen-free flame retardant cable material formula table Unit: kg

[0017]

[0018] The LDPE resin is LLDPE resin with the brand name DFDA-7042 produced by Sinopec Maoming Company. The EPDM resin selects the EPDM resin of EPDM EPDM whose model number is 4640 from American Dow Company. EVA resin selects the EVA resin that the U.S. DuPont company trade mark is 670A for use.

Embodiment 2

[0020] Performance test of the halogen-free flame-retardant cable material in Example 2: tensile strength 10.6MPa, elongation 200%, volume resistivity at 20°C, 1.8×10 13 Ω·m, oxygen index 30.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

A halogen-free flame-retardant cable material is disclosed. The cable material comprises following raw materials by weight: 60-80 parts of LDPE resin, 15-25 parts of EPDM resin, 5-15 parts of EVA resin, 70-90 parts of aluminium hydroxide, and 6-8 parts of red phosphorus. The cable material is excellent in extrusion process property, high in LOI value and good in flame retardant property.

Description

technical field [0001] The invention relates to a cable material, in particular to a halogen-free flame-retardant cable material. Background technique [0002] Plastics for wire and cable insulation and sheathing are commonly known as cable materials, including rubber, plastic, nylon and other varieties. Cable material production enterprises take cable production enterprises as users, as long as there is a demand for wire and cable, there will be a market for cable materials. Except for bare wire products such as steel-cored aluminum stranded wire and electromagnetic wire, almost all wire and cable products require an insulation layer. At present, there are nearly 5,000 wire and cable production enterprises in my country, and there is also a huge demand for wire and cable products for urban and rural power grid transformation, western development, and large-scale upgrading of communication facilities. Therefore, from a period of time, cable materials have a wide market in m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/16C08L23/08C08K13/02C08K3/22C08K3/02C08K5/20C08K5/1565H01B3/44H01B7/295
CPCC08L23/06C08L2201/02C08L2201/22C08L2203/202C08L2205/03C08L2207/066H01B3/441H01B7/295C08L23/16C08L23/0853C08K2003/2227C08K2003/026C08K13/02
Inventor 黄毅
Owner ANHUI MEITENG SPECIAL ELECTRIC CABLE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com