Pink glass-ceramic plate and production method thereof

A production method and technology of glass-ceramic, applied in the field of pink glass-ceramic plate and its production, can solve the problems of high energy consumption, restricting the rapid development and large-scale production of glass-ceramic, and achieve the effect of low cost

Active Publication Date: 2017-06-06
四川一名微晶科技股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional glass-ceramic production mostly adopts the sintering process. The high energy consumption of the sintering process in the production of glass-ceramics has always been a key bottleneck restricting the rapid development and large-scale production of glass-ceramics.
[0004] At present, beige and brown glass-ceramic plates are produced by using the waste granite by the full electric fusion calendering process, but the beige and brown glass-ceramic plates are difficult to meet the market's demand for multi-variety and multi-color glass-ceramics. Therefore, it is necessary to continuously study the formula and production process of glass-ceramics of different colors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pink glass-ceramic plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] According to one embodiment of the present invention, the production method of pink glass-ceramics comprises the following steps:

[0038] 1. Select raw materials according to the following parts by weight, and send them to the mixer for mixing. The mixing time is 4 minutes, and 10Kg of water is added.

[0039] raw material name dolomite granite Calcium Dihydrogen Phosphate Light burnt magnesium Cobalt trioxide Weight (Kg) 119.1 350.0 12.5 31.1 5

[0040] Table 1: Chemical composition (weight percent) of raw materials

[0041] chemical composition dolomite granite Cobalt trioxide Calcium Dihydrogen Phosphate Light burnt magnesium Na 2 o

0.21 3.706 0 0 0 MgO 21.26 0.2687 0 0 79.6 Al 2 o 3

0.32 11.7 0 0 0.2 SiO 2

0.75 77.306 0 0 1.4 P 2 o 5

0 0.0193 0 51 0 K 2 o

0.01 4.721 0 0 0 CaO 30.03 0.398 0 17 2.1 Fe 2 o 3

0.1...

Embodiment 2

[0051] According to one embodiment of the present invention, the production method of pink glass-ceramics comprises the following steps:

[0052] 1. Select raw materials according to the following parts by weight, and send them to the mixer for mixing. The mixing time is 4 minutes, and 10Kg of water is added.

[0053] raw material name dolomite granite Calcium Dihydrogen Phosphate Light burnt magnesium Cobalt trioxide Weight (Kg) 152.6 343.5 14.4 14.6 2.5

[0054]2. Send the above-mentioned mixture into the melting pool of the all-electric melting furnace, and melt it into molten glass at a melting temperature of 1400 ° C. The molten glass is clarified and homogenized in the melting pool at a temperature of 1400 ° C. After clarification and homogenization for 8 hours, the clarified and homogenized glass liquid was obtained.

[0055] 3. The clarified and homogenized molten glass enters the forehearth through the liquid hole and the ascending ch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pink glass-ceramic plate and a production method thereof. The pink glass-ceramic plate comprises the following components in parts by weight: 2-4 parts of Na2O, 8-11 parts of MgO, 9-11 parts of Al2O3, 55-70 parts of SiO2, 1-3 parts of P2O5, 3-4 parts of K2O3, 6-10 parts of CaO and 0.5-1.5 parts of Co2O3. The production method comprises the following steps: mixing the following materials in parts by weight: 24-31 parts of dolomite, 65-78 parts of granite, 2-6 parts of calcium dihydrogen phosphate, 0.5-1 part of cobalt sesquioxide and 2-4 parts of caustic calcined magnesite, and then producing by adopting all-electric melting calendering. According to the invention, the formula of the pink glass-ceramic plate is obtained by researching the proportion of a glass-ceramic plate for a long term, and the production method for producing the pink glass-ceramic plate is obtained. The pink glass-ceramic plate disclosed by the invention breaks through the condition of single color of the traditional glass-ceramic plate.

Description

technical field [0001] The invention relates to a building material and a production method thereof, in particular to a pink glass-ceramic plate and a production method thereof. Background technique [0002] Glass-ceramic not only has the basic properties of glass, but also has the polycrystalline characteristics of ceramics. It combines the characteristics of glass and ceramics and becomes a unique new type of material. Because of its high mechanical strength, high hardness, good wear resistance, strong corrosion resistance, good chemical stability and thermal stability, and can adapt to harsh environments, it has developed rapidly in the world in recent years. In particular, the "Twelfth Five-Year New Material Industry Development Plan" announced by the Ministry of Industry and Information Technology in January 2012 included rolled glass-ceramic in the list of inorganic non-metallic new materials that will be developed as a key development, and has a great impact on the de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C4/02C03C10/00
Inventor 秦刚秦小平王刚琳姜小元徐国梁熊冰峰
Owner 四川一名微晶科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com