Black glass-ceramic plate and production method thereof

A technology of glass-ceramic and plate, which is applied in the field of black glass-ceramic plate and its production, can solve the problems of high energy consumption, restricting the rapid development and large-scale production of glass-ceramic, and achieve the effect of low cost

Active Publication Date: 2015-09-23
四川一名微晶科技股份有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional glass-ceramic production mostly adopts the sintering process. The high energy consumption of the sintering process in the production of glass-ceramics has always been a key bottleneck restricting the rapid development and large-scale production of glass-ceramics.
[0004] At present, beige and brown glass-ceramic plates are produced by using the waste granite by the full electric fusion calendering process, but the beige and brown glass-ceramic plates are difficult to meet the market's demand for multi-variety and multi-color glass-ceramics. Therefore, it is necessary to continuously study the formula and production process of glass-ceramics of different colors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black glass-ceramic plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] According to one embodiment of the present invention, the production method of black glass-ceramics comprises the following steps:

[0023] 1. Select raw materials according to the following parts by weight, and send them to the mixer for mixing. The mixing time is 4 minutes, and 10Kg of water is added.

[0024] raw material name

Magnesite

granite

Calcium Dihydrogen Phosphate

heavy calcium

Basalt

Weight (Kg)

70

190

2.4

7.6

230

[0025] Table 1: Chemical composition of raw materials (weight percent)

[0026]

[0027] 2. Send the above-mentioned mixture into the melting pool of the all-electric melting furnace, control the melting temperature to 1350°C, and clarify and homogenize the melted glass. The temperature of clarification and homogenization is 1400°C. The time is 8h.

[0028] 3. The clarified and homogenized glass enters the forehearth through the flow hole and the ascending channel, and the temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a black microcrystalline glass sheet material and a production method thereof. The black microcrystalline glass sheet material contains the following ingredients in parts by weight: 2-4 parts of Na2O, 6-10 parts of MgO, 8-13 parts of Al2O3, 55-65 parts of SiO2, 0.5-2 parts of P2O5, 3-4 parts of K2O, 4-8 parts of CaO, 5-10 parts of Fe2O3 and 1.5-2.5 parts of TiO2. The production method comprises the steps of mixing 9-20 parts by weight of magnesite, 30-50 parts by weight of granite, 0.5-3 parts by weight of calcium dihydrogen phosphate, 1-8 parts by weight of heavy calcium carbonate and 30-70 parts by weight of basalt and then producing by adopting all-electric melting calendering. According to the black microcrystalline glass sheet material and the production method thereof, through the long-term research on the proportioning ratio of microcrystalline glass sheet materials, a formula for the black microcrystalline glass sheet material is obtained, and the production method of the black microcrystalline glass sheet material is also obtained; the situation that the existing microcrystalline glass sheet materials are single in color is broken through; basalt waste residues and granite are taken as main raw materials, the basalt waste residues contain a large amount of iron and titanium, titanium can serve as a crystal nucleating agent, the content of P2O5 can be reduced, and iron oxide red is not required to be added into the raw materials; the raw materials are all easily obtained and are low in cost.

Description

technical field [0001] The invention relates to a building material and a production method thereof, in particular to a black glass-ceramic plate and a production method thereof. Background technique [0002] Glass-ceramic not only has the basic properties of glass, but also has the polycrystalline characteristics of ceramics. It combines the characteristics of glass and ceramics and becomes a unique new type of material. Because of its high mechanical strength, high hardness, good wear resistance, strong corrosion resistance, good chemical stability and thermal stability, and can adapt to harsh environments, it has developed rapidly in the world in recent years. In particular, the "Twelfth Five-Year New Material Industry Development Plan" announced by the Ministry of Industry and Information Technology in January 2012 included rolled glass-ceramic in the list of inorganic non-metallic new materials that will be developed as a key development, and has a great impact on the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C10/00C03C4/02C03B32/02
Inventor 秦刚秦小平姜小元王刚琳王桃徐国梁熊冰峰
Owner 四川一名微晶科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products