Universal fully-biodegradable color masterbatch and preparation method thereof

A biodegradable polyester and all-biological technology, applied in the field of universal fully biodegradable color masterbatch and its preparation, can solve the problems of limited versatility and poor compatibility, and achieve good dispersion effect, good processing performance and good coloring effect of effect

Inactive Publication Date: 2014-10-22
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF8 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of color masterbatch is often not widely used, and it is more suitable for coloring the same matrix as the carrier resin, otherwise there will be problems of poor compatibility

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Universal fully-biodegradable color masterbatch and preparation method thereof
  • Universal fully-biodegradable color masterbatch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Dry PBAT (blown film grade, BASF) in a blast oven at 80°C for 6 hours, and dry talc powder (with a particle size of 1250 mesh) in a blast oven at 120°C for 5 hours.

[0029] (2) Take 80 parts of PBAT, 10 parts of titanium dioxide, 10 parts of talc powder, 3 parts of ADR-4368, 5 parts of stearic acid, and 0.6 parts of tetrakis[β-(3,5-di-tert-butyl-4-hydroxybenzene base) propionic acid] pentaerythritol ester was mixed in a high-speed mixer for 5 minutes.

[0030] (3) Put the obtained mixture into a twin-screw extruder to extrude, draw strands, water-cool and pelletize to obtain a fully biodegradable color masterbatch. The temperature of each zone of the twin-screw extruder is: 90°C in the first zone, 110°C in the second zone, 120°C in the third zone, 130°C in the fourth zone, 140°C in the fifth zone, 150°C in the sixth zone, and 155°C in the head; the screw speed is 100rpm, and the long diameter The ratio is 40 / 1.

Embodiment 2

[0032] (1) Dry PBS (blown film grade, Anqing Hexing Company) in a blast oven at 60°C for 24 hours, and dry calcium carbonate (with a particle size of 800 mesh) in a blast oven at 105°C for 10 hours.

[0033] (2) Take 30 parts of PBS, 40 parts of carbon black, 30 parts of calcium carbonate, 0.5 parts of ADR-4370, 20 parts of calcium stearate, 0.1 parts of β-(3,5-di-tert-butyl-4-hydroxyphenyl ) Propionate octadecyl alcohol ester was mixed at high speed in a high-speed mixer for 15 minutes.

[0034] (3) Put the obtained mixture into a twin-screw extruder to extrude, draw strands, water-cool and pelletize to obtain a fully biodegradable color masterbatch. The temperature of each zone of the twin-screw extruder is: 90°C in the first zone, 110°C in the second zone, 120°C in the third zone, 130°C in the fourth zone, 140°C in the fifth zone, 150°C in the sixth zone, and 155°C in the head; the screw speed is 300rpm, and the long diameter The ratio is 44 / 1.

Embodiment 3

[0036] (1) PLA (4032D, NatureWorks) was dried in a blast oven at 70°C for 10 hours, and montmorillonite (with a particle size of 2500 mesh) was dried in a blast oven at 110°C for 8 hours.

[0037] (2) Take 60 parts of PLA, 20 parts of red powder, 20 parts of montmorillonite, 1.5 parts of ADR-4370, 15 parts of polyethylene wax, 0.5 parts of 2-methylenebis(4-methyl-6-tert-butyl Phenol) was mixed in a high-speed mixer for 10 minutes.

[0038] (3) Put the obtained mixture into a twin-screw extruder to extrude, draw strands, water-cool and pelletize to obtain a fully biodegradable color masterbatch. The temperature of each zone of the twin-screw extruder is: 150°C in the first zone, 160°C in the second zone, 170°C in the third zone, 175°C in the fourth zone, 175°C in the fifth zone, 170°C in the sixth zone, and 165°C in the head; the screw speed is 200rpm, and the long diameter The ratio is 48 / 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high-molecular materials, and relates to a universal fully-biodegradable color masterbatch and a preparation method thereof. The universal fully-biodegradable color masterbatch comprises the formula compositions in parts by weight: 30-80 parts of biodegradable polyester, 10-40 parts of a pigment, 10-30 parts of a filler, 0.5-3 parts of a compatilizer, 5-20 parts of a lubricant and 0.1-0.6 part of an anti-oxidant. The fully-biodegradable color masterbatch is obtained through melt blending, extrusion, strip pulling and pelletizing by employing a double screw extruder. The fully-biodegradable color masterbatch is completely biodegradable, good in processing performance and good in dispersing effect in a matrix, and has extremely good compatibility with a polyester matrix even a masterbatch carrier and a biodegradable polyester matrix are different polyesters. The masterbatch gives play to extremely good coloring effect on a product when being applied to a biodegradable polyester.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a universal fully biodegradable color masterbatch and a preparation method thereof. Background technique [0002] The use of plastic materials has penetrated into all areas of people's lives, and is widely used as food packaging, electronic and electrical product packaging, shopping bags, garbage bags and disposable injection molding products. The raw materials of traditional plastic materials such as polypropylene (PP), polyethylene (PE), polystyrene (PS) are petroleum, which are difficult to degrade when discarded in nature after use, causing great harm to the environment. With the depletion of petroleum resources and the continuous enhancement of people's awareness of environmental protection, the development of fully degradable, environmentally friendly polymer materials used in the field of films and disposable injection molding products has become the mainstream of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/00C08L67/04C08L67/02C08K13/02B29B9/06B29C47/92B29C48/92
CPCB29C48/06B29C48/40B29C48/625B29C48/92B29C2948/9259B29C2948/92676B29C2948/92704B29C2948/92828
Inventor 杨桂生袁角亮
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka