Asphalt pavement water-based enhanced fog seal material and preparation method and construction method

A fog seal material and asphalt pavement technology, which is applied in the directions of roads, roads, side ditch/curbstone, etc., can solve the problem that the adhesion between the original fog seal layer and the original pavement stone cannot achieve the expected effect, and reduce the resistance of the asphalt pavement surface layer. It can reduce the slippage ability and the anti-seepage ability of the road surface, so as to achieve the effect of delaying ultraviolet aging, enhancing the ability of anti-ultraviolet aging, and good economic benefits.

Inactive Publication Date: 2016-03-23
CHANGAN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the relatively simple preventive maintenance method of fog seal layer commonly used at present, its biggest disadvantage is that the anti-seepage effect is not ideal, and the adhesion between the original fog seal layer and the original pavement stone material cannot achieve the expected effect. Detachment will occur, exposing the stone material of the original pavement, and the anti-seepage ability of the pavement will be reduced, thereby reducing the skid resistance of the surface layer of the asphalt pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt pavement water-based enhanced fog seal material and preparation method and construction method
  • Asphalt pavement water-based enhanced fog seal material and preparation method and construction method
  • Asphalt pavement water-based enhanced fog seal material and preparation method and construction method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Take the preparation of a water-based enhanced fog seal material for asphalt pavement as an example to illustrate.

[0050] (1) Weigh each component:

[0051]Composition A comprises the following components in parts by weight: 10 parts of JWRH-MKH slow-cracking and fast-setting cationic emulsifier, 50 parts of water, 15 parts of ethanol, 0.5 parts of sodium lauryl sulfate, and 0.1 part of sodium carboxymethylcellulose.

[0052] Composition B contains the following components in parts by weight: 15 parts of penetrating agent EA, 15 parts of modified latex, and 50 parts of asphalt.

[0053] Composition C contains the following components in parts by weight: 10 parts of penetrating agent EA, 25 parts of modified latex, 32 parts of benzophenone, and 50 parts of asphalt.

[0054] (2) The preparation method of water-based enhanced fog seal material:

[0055] The preparation method of composition A: first add the emulsifier into water at 50-80°C, and adjust the pH value to t...

Embodiment 2

[0065] Take the preparation of a water-based enhanced fog seal material for asphalt pavement as an example to illustrate.

[0066] (1) Weigh each component:

[0067] Composition A contains the following components in parts by weight: 20 parts of JWRH-MKH slow-cracking and fast-setting cationic emulsifier, 60 parts of water, 15 parts of ethanol, 0.8 parts of polyacrylamide, CaCl 2 0.2 parts.

[0068] Composition B contains the following components in parts by weight: 15 parts of penetrating agent EA, 20 parts of styrene butadiene particles, and 50 parts of asphalt.

[0069] Composition C contains the following components in parts by weight: 10 parts of penetrant EA, 30 parts of styrene butadiene particles, 32 parts of benzophenone, and 50 parts of asphalt.

[0070] (2) The preparation method of water-based enhanced fog seal material:

[0071] The preparation method of composition A: first add the emulsifier into water at 50-80°C, and adjust the pH value to the range required...

Embodiment 3

[0081] Take the preparation of a water-based enhanced fog seal material for asphalt pavement as an example to illustrate.

[0082] (1) Weigh each component:

[0083] Composition A contains the following components in parts by weight: 30 parts of JY-R2G cationic emulsifier, 70 parts of water, 20 parts of propanol, 1 part of carboxymethyl cellulose, and 0.2 part of sodium carboxymethyl cellulose.

[0084] Composition B comprises the following components in parts by weight: 20 parts of fatty alcohol polyoxyethylene ether, 40 parts of modified latex, and 35 parts of asphalt.

[0085] Composition C comprises the following components in parts by weight: 15 parts of fatty alcohol polyoxyethylene ether, 50 parts of modified latex, 4 parts of phenyl salicylate, and 50 parts of asphalt.

[0086] (2) The preparation method of water-based enhanced fog seal material:

[0087] The preparation method of composition A: first add the emulsifier into water at 50-80°C, and adjust the pH value ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of highway maintenance, and discloses a water-based reinforced type fog sealing layer material for an asphalt pavement, and a preparation method and a construction method of the water-based reinforced type fog sealing layer material for the asphalt pavement. The fog sealing layer material comprises a lower water-penetration-preventing sub-layer and an upper anti-skidding wear-resisting sub-layer, wherein materials for preparing the lower sub-layer contain an emulsifier, water, an organic solvent, a dispersant, an additive, a penetrating agent, a viscosifier and asphalt, and materials for preparing the upper sub-layer contain an emulsifier, water, an organic solvent, a dispersant, an additive, a penetrating agent, a viscosifier, an ultraviolet-resistant aging agent and asphalt. The construction method of the fog sealing layer material is a layered spreading method and comprises the following steps: mixing mixed liquor of the materials for preparing the lower sub-layer with a sand material to obtain a mixture, spreading the mixture on the asphalt pavement to form the lower water-penetration-preventing sub-layer, drying, spraying mixed liquor of materials for preparing the upper sub-layer on the lower water-penetration-preventing sub-layer, and spreading the sand material to form the upper anti-skidding wear-resisting sub-layer. The water-based reinforced type fog sealing layer material for the asphalt pavement, the preparation method and the construction method d of the water-based reinforced type fog sealing layer material for the asphalt pavement, disclosed by the invention, are used for pavement preventive maintenance, can improve the waterproof performance, anti-skidding performance, firmness and ultraviolet resistant aging performance, and are environmentally-friendly and economical.

Description

technical field [0001] The invention relates to the technical field of highway maintenance, in particular to a water-based enhanced fog seal material for asphalt pavement, a preparation method and a construction method. Background technique [0002] After several years of normal use of the asphalt pavement, the pavement will experience slight fatigue cracks and loss of fine aggregates, and its anti-seepage performance will deteriorate, and pavement water will enter the asphalt mixture through cracks or fine aggregate damage. , accelerated the damage of the road surface. [0003] Fog seal is currently the most effective preventive maintenance measure for asphalt pavement. This technology spreads the fog seal material on the asphalt pavement in the form of a mist to form a thin layer of seal to seal tiny cracks and surfaces. Voids, restore and protect the oxidized asphalt pavement, play a role in waterproofing and inhibiting looseness, and at the same time improve and enhance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E01C7/35E01C7/32E01C11/22C04B26/26
Inventor 耿九光杨婉怡靳美倩郑敏楠李炜光
Owner CHANGAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com