Competitive nylon fishing line and production method thereof

A production method and fishing line technology, applied in competitive nylon fishing line and its production field, can solve problems such as strength, elongation at break, affecting work performance and application range, and achieve wide application range, convenient operation, and simple process Effect

Active Publication Date: 2016-01-13
NANTONG NTEC MONOFILAMENT TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing monofilaments have defects in strength, elongation at break and other properties, which affect the working performance and application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A competitive nylon fishing line, composed of PA6, PA6 / PA66 copolymer and additives, wherein the weight percentage of PA6 is 90~95% (for example, 90%, 92%, 95%), and the weight percentage of PA6 / PA66 copolymer 0~5% (1%, 3%, 5%), the weight percentage of the additive is 5~10% (for example, 5%, 7%, 10%); the cross section of the monofilament is circular, and the diameter of the monofilament is 0.07~ 0.15mm (for example 0.07mm, 0.1mm, 0.15mm), single filament tensile strength is 10-12CN / dtex, elongation at break is 15~25% (for example 15%, 20%, 25%), knot strength 70% to 85% (eg 70%, 80%, 85%) of the tensile strength; the additive is a mixture of one or more of nano-nucleating agents, lubricants, and antioxidants; the antioxidant The agent is butyl hydroxytoluene, dioctadecyl sulfide or diphenyloctyl phosphite; the lubricant is butyl stearate or oleamide.

[0014] The production method of the competitive nylon fishing line includes the steps of mixing raw materials, melt ...

Embodiment 2

[0016] The weight percentage of PA6 is 90%, the weight percentage of PA6 / PA66 copolymer is 5%, and the weight percentage of additives is 5%; the diameter of monofilament is 0.1mm, the tensile strength of monofilament is greater than 11CN / dtex, and the elongation at break is 22%-24%, the knot strength is greater than 83% of the tensile strength; the additive is an antioxidant butyl hydroxytoluene; the lubricant is oleamide. The liquid in the liquid tank is a mixed solution of 5% sodium bisulfate, polyethylene wax, and dioctadecyl sulfide, and the mass ratio is: 5% sodium bisulfate solution: polyethylene wax: dioctadecyl sulfide=90: 5:5. All the other are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an athletic nylon fishing line and a producing method thereof. The athletic nylon fishing line consists of PA6, a PA6 / PA66 copolymer and an additive, wherein the PA6 accounts for 90-96 percentage by weight, the PA6 / PA66 copolymer accounts for 0-5 percentage by weight, and the additive accounts for 5-10 percentage by weight; the cross section of a monofilament is round, the diameter of the monofilament is 0.07-0.15 mm, the tensile strength of the monofilament is 10-12CN / dtex, the breakage elongation rate is 15-25%, and the knotting strength is 70-85% of the tensile strength. The technology is simple, the operation is convenient, the molded fiber has the characteristics of high strength and the like, and the use range is wide.

Description

technical field [0001] The invention relates to a competitive nylon fishing line and a production method thereof. Background technique [0002] The existing monofilaments have defects in properties such as strength and elongation at break, which affect the working performance and application range. Contents of the invention [0003] The object of the present invention is to provide a competitive nylon fishing line with good working performance and its production method. [0004] Technical solution of the present invention is: [0005] A competitive nylon fishing line, characterized in that it is composed of PA6, PA6 / PA66 copolymer and additives, wherein the weight percentage of PA6 is 90-95%, the weight percentage of PA6 / PA66 copolymer is 0-5%, and the additive The weight percentage of the monofilament is 5~10%; the cross section of the monofilament is circular, the diameter of the monofilament is 0.07~0.15mm, the tensile strength of the monofilament is 10-12CN / dtex, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/90D01F1/10D01D13/00D01D5/08D01D5/088D01D5/12
Inventor 马海燕陈辉宇
Owner NANTONG NTEC MONOFILAMENT TECH CO LTD