Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-rust coating, durable technology, applied in anti-corrosion coatings, rosin coatings, coatings, etc., can solve the problems of unfriendly environment, air pollution, damage to the ecological environment, etc., to achieve wide application, good anti-rust, good acid resistance alkaline effect
Inactive Publication Date: 2014-12-24
QINGDAO BAOLIKANG NEW MATERIALS
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, at present, most of the paints are solvent-based paints, which contain about 50% organic solvents. These paints will release a large amount of VOC gas after spraying, which not only seriously endangers the health of users, but also
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0010] A durable antirust paint, which is made of the following raw materials in parts by weight:
[0011] 10 parts of acrylic emulsion, 20 parts of iron oxide red, 6 parts of aluminum tripolyphosphate, 9 parts of mica powder, 8 parts of titanium dioxide, 3 parts of magnesium oxide, 7 parts of dicyandiamide, 10 parts of rosin, 2 parts of isobutanol, carbonic acid 6 parts of calcium, 1 part of curing agent.
Embodiment 2
[0013] A durable antirust paint, which is made of the following raw materials in parts by weight:
[0014] 20 parts of acrylic emulsion, 30 parts of iron oxide red, 9 parts of aluminum tripolyphosphate, 13 parts of mica powder, 13 parts of titanium dioxide, 8 parts of magnesium oxide, 12 parts of dicyandiamide, 15 parts of rosin, 4 parts of isobutanol, carbonic acid 9 parts of calcium, 3 parts of curing agent.
Embodiment 3
[0016] A durable antirust paint, which is made of the following raw materials in parts by weight:
[0017] 15 parts of acrylic emulsion, 25 parts of iron oxide red, 7 parts of aluminum tripolyphosphate, 11 parts of mica powder, 10 parts of titanium dioxide, 6 parts of magnesium oxide, 9 parts of dicyandiamide, 13 parts of rosin, 3 parts of isobutanol, carbonic acid 7 parts of calcium, 2 parts of curing agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a durable antirust coating. The durable antirust coating is prepared from the following raw materials in parts by weight: 10-20 parts of acrylic emulsion, 20-30 parts of red iron oxide, 6-9 parts of aluminum tripolyphosphate, 9-13 parts of mica powder, 8-13 parts of titanium dioxide powder, 3-8 parts of magnesium oxide, 7-12 parts of dicyandiamide, 10-15 parts of rosin, 2-4 parts of isobutanol, 6-9 parts of calcium carbonate and 1-3 parts of curing agent. The durable antirust coating disclosed by the invention has the beneficial effects of good antirust property and corrosion resistance and good acid and alkali resistance and is widely applied.
Description
technical field [0001] The invention relates to a durable antirust paint. Background technique [0002] The problem of metal corrosion pervades all walks of life in the national economy. It will cause great damage to the performance and commercial value of metal products, and even cause major failures and make equipment scrapped. Therefore, the problem of metal rust prevention has increasingly attracted people. s concern. Applying anti-rust paint is the most economical and effective anti-rust method at present. However, at present, most of the paints are solvent-based paints, which contain about 50% organic solvents. These paints will release a large amount of VOC gas after spraying, which not only seriously endangers the health of users, but also pollutes the atmosphere. , damage the ecological environment; at the same time, many corrosion inhibitors in antirust coatings currently use sodium nitrite compound corrosion inhibitors, which are not friendly to the environment....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more