A metallographic corrosion solution for hr-2 hydrogen-resistant steel and its preparation method and corrosion method

A metallographic corrosion and hydrogen-resistant steel technology, applied in the field of metallographic corrosion liquid, can solve the problems of unclear grain boundaries and inability to corrode grain boundaries, etc., and achieve good display effect, slow and stable corrosion reaction, and reasonable design

Inactive Publication Date: 2017-02-22
XI AN JIAOTONG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wipe the surface of the sample with newly prepared concentrated aqua regia, and the surface of the sample turns black quickly. When the corrosion surface structure is observed under a metallographic microscope, the crystal grains appear black, but the grain boundaries are still unclear; If there is no such surface, it is impossible to corrode a complete and clear grain boundary.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A metallographic corrosion solution for hr-2 hydrogen-resistant steel and its preparation method and corrosion method
  • A metallographic corrosion solution for hr-2 hydrogen-resistant steel and its preparation method and corrosion method
  • A metallographic corrosion solution for hr-2 hydrogen-resistant steel and its preparation method and corrosion method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of metallographic corrosion method of HR-2 hydrogen-resistant steel, concrete operation is:

[0041] Measure 25 ml of distilled water with a graduated cylinder, pour it into a beaker, add 15 ml of hydrochloric acid, and finally add 5 ml of nitric acid, stir gently with a glass rod, and prepare a metallographic corrosion solution.

[0042] Grind the HR-2 hydrogen-resistant steel sample (rough grinding and then fine grinding when grinding, and then use 400#, 600#, 800#, 1000# water-resistant sandpaper to polish), mechanical polishing (10W, 5W grinding), cleaning ( Wash with distilled water and absolute ethanol), blow dry, and make the sample to be corroded; hold an appropriate amount of absorbent cotton with tweezers, dip in the metallographic corrosion solution, take out the absorbent cotton, and gently wipe the surface of the sample for about 8 minutes until the surface of the sample Silver gray; pour a certain amount of newly prepared metallographic corrosion so...

Embodiment 2

[0045]A metallographic corrosion method of HR-2 hydrogen-resistant steel after stretching, the specific operations are:

[0046] Measure 25 ml of distilled water with a graduated cylinder, pour it into a beaker, add 15 ml of hydrochloric acid, and finally add 5 ml of nitric acid, stir gently with a glass rod, and prepare a metallographic corrosion solution.

[0047] Grind the HR-2 hydrogen-resistant steel sample with a deformation of 10% (when grinding, first coarsely grind and then finely grind with 400#, 600#, 800#, 1000# water-resistant sandpaper), mechanical polishing (10W, 5W Grinding), cleaning (cleaning with distilled water and absolute ethanol), drying, and making the sample to be corroded; holding an appropriate amount of absorbent cotton with tweezers, dipping in the metallographic corrosion solution configured according to claim 2, taking out the absorbent cotton, and repeatedly gently Wipe the surface of the sample for about 7 minutes until the surface of the sampl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metallographic etchant used for HR-2 antihydrogen steel, and a preparation method and a corrosion method of the metallographic etchant, and belongs to the technical field of the metallographic etchant. The metallographic etchant comprises nitric acid, hydrochloric acid and distilled water at the volume ratio of 1:3:5. The corrosion method comprises the following steps: 1) polishing, burnishing, cleaning and drying an HR-2 antihydrogen steel sample; 2) using a degreasing cotton to dip the newly prepared metallographic etchant, taking the wetted degreasing cotton to repeatedly scrub the surface of the sample to be corroded till the surface is silver gray; 3) immediately soaking the sample processed in the step 2) into the newly prepared metallographic etchant until a bubble which covers the surface of the sample is yellow; 4) taking out the sample, washing and drying to obtain an HR-2 antihydrogen steel metallographic observation sample, and observing the corrosion effect under a metallographic microscope. The metallographic etchant is a regular chemical agent, is simple to prepare and free of pollution, and subboundary, twin-boundary, crystal-boundary and austenite structures and strain-induced martensite are quite obviously observed.

Description

technical field [0001] The invention belongs to the technical field of metallographic corrosion liquid, and in particular relates to a metallographic corrosion liquid and corrosion method for HR-2 hydrogen-resistant steel. Background technique [0002] In the fields of petrochemical, oil and gas, nuclear, aviation, aerospace and other engineering systems, hydrogen embrittlement has always been a major factor causing premature fracture of components and equipment. With the development of aviation, marine, petroleum, nuclear industry, and hydrogen storage, the performance requirements of high-strength hydrogen embrittlement-resistant alloys used in hydrogen-facing environments are getting higher and higher. Hydrogen-resistant alloys refer to metal materials that can resist hydrogen damage or hydrogen embrittlement. They can be used as structural materials under high-pressure hydrogen (10-70MPa) conditions, and can also be used as lining materials for hydrogenation reaction tan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F1/28G01N1/32
Inventor 陈雁张永梅尚福林
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com