A magnetic orientation and pattern technology, applied in the field of magnetic orientation patterns and its preparation, can solve the problems of single overall optical effect of magnetic pigments and large amount of pigment usage, and achieve excellent optical effects, reduced pigment usage, and good tile performance Effect

Active Publication Date: 2016-11-23
HUIZHOU FORYOU OPTICAL TECH
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. It is used for the coating containing magnetic pigment (magnetic pigment containing layer) is relatively thick, and the magnetic pigment contained in the coating can have a better magnetic orientation space when the thickness is not less than d50 / 3. Thicker Coating means a large amount of pigment is used;
[0005] 2. The overall optical effect of the magnetic pigment is single

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A magnetic orientation pattern and its preparation method
  • A magnetic orientation pattern and its preparation method
  • A magnetic orientation pattern and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] see figure 1 , figure 1 It is a flowchart of a method for preparing a magnetic alignment pattern provided by an embodiment of the present invention. The method for preparing a magnetic alignment pattern in this embodiment includes:

[0036] S101: providing a base layer;

[0037] Wherein, the substrate layer may be a fibrous substrate, such as paper or cardboard. Fiber-free porous substrates are also possible, such as plastic substrates with a porous surface, or even non-porous substrates with a textured or uneven surface structure. The base layer can be transparent, opaque or translucent. Colorless or pigmented substrates are also available as desired.

[0038] S102: Coating a first coating on the base layer, the first coating contains a plurality of first magnetic pigments;

[0039] The first coating can be applied according to any printing means known in the art, such as inkjet printing, offset printing, flexographic printing, gravure printing, stencil printing, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a magnetic alignment pattern and a preparation method thereof. Wherein, the preparation method of the magnetic alignment pattern comprises: providing a base layer; coating a first coating on the base layer, containing a plurality of first magnetic pigments in the first coating; drying or curing the first coating; Or coat the second coating on the cured first coating, and the first coating is swelled by the second coating; the first magnetic pigment in the first coating swollen by the second coating is magnetically Orienting: drying or curing the second coating and the first coating swollen by the second coating to form a magnetic alignment pattern. Through the above method, the present invention can fully reduce the thickness of the magnetic pigment-containing layer, thereby reducing the amount of pigment used. Further, the present invention can obtain excellent diversified optical effects, can not only obtain the performance of ink film with special requirements, but also can produce set magnetic induction images.

Description

technical field [0001] The invention relates to a magnetic alignment pattern and a preparation method thereof. Background technique [0002] The method of producing a magnetic induction image is generally to coat the ink or coating composition containing magnetic pigments on the substrate, immediately apply an external magnetic field for magnetic orientation when the coating is in the wet film stage, and then harden the coating to form the final magnetic induction image components or decorative coatings. [0003] In the existing methods for obtaining magnetic induction images, the magnetic pigments contained in the coating must have sufficient deflection space and small enough resistance during magnetic orientation, so the magnetic orientation must be performed in a wet film state. Therefore, there are generally following defects in the prior art: [0004] 1. It is used for the coating containing magnetic pigment (magnetic pigment containing layer) is relatively thick, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B41M3/14B41M7/00
Inventor 樊长武邹文格王荇阳义峰
Owner HUIZHOU FORYOU OPTICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap