Broad spectrum solar cell material and preparation method thereof

A technology of solar cells and wide spectrum is applied in the field of solar cell materials to achieve the effects of improving photoelectric conversion efficiency, broad application prospects and good electron stacking performance

Inactive Publication Date: 2015-03-11
WUXI SUNOCEAN
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for fixed semiconductor materials, solar cells can only effectively use specific wavelengths of sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A wide-spectrum solar cell material, the components and the mass parts of each component are as follows: 20 parts of graphite, 5 parts of silicon carbide, 8 parts of silicon nitride, 1.5 parts of erbium oxide, 8 parts of quantum dots, and cyclopentenedithiophene 30 parts, 15 parts of benzothiadiazole, 5 parts of 1,8-octanedithiol, 0.55 parts of tribasic lead sulfate, free radical scavenger bis(2,2,6,6-tetramethyl -4-piperidinate) 8.5 parts, heat stabilizer dibutyltin dilaurate 5 parts, ultraviolet absorber phenyl salicylate 10 parts. The particle size of silicon carbide is 0.35~0.7nm.

[0023] The preparation method comprises the steps of:

[0024] 1) Mix cyclopentenedithiophene, benzothiadiazole and 1,8-octanedithiol evenly, heat to 340°C, and keep stirring at 1200rpm for 5h to obtain a copolymer;

[0025] 2) Mix graphite, silicon carbide, silicon nitride, erbium oxide, quantum dots and tribasic lead sulfate, and stir at 70°C for 30 minutes;

[0026]...

Embodiment 2

[0028] A wide-spectrum solar cell material, the components and the mass parts of each component are as follows: 10 parts of graphite, 2 parts of silicon carbide, 3 parts of silicon nitride, 0.8 parts of erbium oxide, 2 parts of quantum dots, and cyclopentenedithiophene 20 parts, 10 parts of benzothiadiazole, 2 parts of 1,8-octanedithiol, 0.15 parts of tribasic lead sulfate, free radical scavenger bis(2,2,6,6-tetramethyl -4-piperidinate) 1.5 parts, heat stabilizer dibutyltin dilaurate 1 part, ultraviolet absorber phenyl salicylate 3 parts. The particle size of silicon carbide is 0.35~0.7nm.

[0029] The preparation method comprises the steps of:

[0030] 1) Mix cyclopentenedithiophene, benzothiadiazole and 1,8-octanedithiol evenly, heat to 340°C, and keep stirring at 1200rpm for 5h to obtain a copolymer;

[0031] 2) Mix graphite, silicon carbide, silicon nitride, erbium oxide, quantum dots and tribasic lead sulfate, and stir at 70°C for 30 minutes;

[0032] 3) Ad...

Embodiment 3

[0034] A wide-spectrum solar cell material, the components and the mass parts of each component are as follows: 17 parts of graphite, 4 parts of silicon carbide, 5.5 parts of silicon nitride, 1.1 parts of erbium oxide, 4.9 parts of quantum dots, cyclopentenedithiophene 25.3 parts, 13.9 parts of benzothiadiazole, 3.3 parts of 1,8-octanedithiol, 0.3 parts of tribasic lead sulfate, free radical scavenger bis(2,2,6,6-tetramethyl -4-piperidinate) 6.5 parts, heat stabilizer dibutyltin dilaurate 4 parts, ultraviolet absorber phenyl salicylate 6.5 parts. The particle size of silicon carbide is 0.35~0.7nm.

[0035] The preparation method comprises the steps of:

[0036] 1) Mix cyclopentenedithiophene, benzothiadiazole and 1,8-octanedithiol evenly, heat to 340°C, and keep stirring at 1200rpm for 5h to obtain a copolymer;

[0037] 2) Mix graphite, silicon carbide, silicon nitride, erbium oxide, quantum dots and tribasic lead sulfate, and stir at 70°C for 30 minutes;

[003...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a broad spectrum solar cell material and a preparation method thereof. The broad spectrum solar cell material is composed of the components in weight parts: 10-20 parts of graphite, 2-5 parts of silicon carbide, 3-8 parts of silicon nitride, 0.8-1.5 parts of erbium oxide, 2-8 parts of quantum dots, 20-30 parts of cyclopentene thiophene, 10-15 parts of diazosulfide, 2-5 parts of 1,8-octane dithiol, 0.15-0.55 part of lead hydroxide oxide sulfate, 1.5-8.5 parts of radical scavenger, 1-5 parts of thermal stabilizer, 3-10 ultraviolet light absorber and 1-3 parts of carbon black. The broad spectrum solar cell material has good electron stacking performance, higher carrier mobility and absorption peaks within the scope of 150-4000 nm, is capable of effectively improving the photoelectric conversion efficiency of solar cells and has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of solar cell materials, and in particular relates to a wide-spectrum solar cell material and a preparation method thereof. Background technique [0002] The shortage of energy has seriously affected people's life and restricted the development of society. Abundant solar energy is an important clean energy, an inexhaustible, inexhaustible, pollution-free, cheap energy that human beings can use freely. After the first oil crisis, countries competed to carry out research on the application of clean and renewable energy such as solar energy, water energy, and wind energy, especially the application of solar energy is the most extensive. [0003] As a kind of green energy, solar energy has no pollution to the environment, and its source is simple, so it can be said that it is inexhaustible within the life span of human beings. Solar energy is not only a one-time energy source, but also a clean energy sourc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L51/46H01L51/48
CPCH10K85/113H10K30/00H10K71/00H10K2102/00Y02E10/549
Inventor 黄新东刘天人
Owner WUXI SUNOCEAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com