A kind of fluorosilicone resin, preparation method and application thereof

A fluorosilicone resin and reactor technology, applied in the field of building materials production, can solve the problems of high price, uneven protection effect, etc., and achieve the effects of easy availability of raw materials, simple and feasible production operation, and wide application range.

Active Publication Date: 2017-07-04
杜丽红
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the protection effect of foreign products is uneven, and the price is relatively expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fluorosilicone resin, preparation method and application thereof
  • A kind of fluorosilicone resin, preparation method and application thereof
  • A kind of fluorosilicone resin, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Synthesis of embodiment 1 perfluorobutyl triethoxy fluorosilicone resin

[0019]

[0020] (1) 100g vinyltriethoxysiloxane is added by weight in the reactor, add 2g of dibenzoyl peroxide and 3g of methyl ethyl ketone peroxide, stir well, and the solution is stirred at room temperature for 1 hour, Prepolymer A is obtained.

[0021] (2) 100g 2-(perfluorobutyl) ethyl methacrylate is added to the reactor by weight, 3g of azobisisobutyronitrile and 1g of tert-dodecyl mercaptan are added, stirred evenly, and The solution was stirred at room temperature for 1 hour to obtain prepolymer B.

[0022] (3) Add the above-mentioned prepolymers A100g and B10g into the reactor, add 2g of cobalt naphthenate, 3g of mercaptoethanol and 5g of 3-aminopropyltriethoxysilane coupling agent, stir well, and dissolve the solution Stir at room temperature for 3 hours to obtain perfluorobutyltriethoxyfluorosilicone resin.

[0023] The resin test results are as follows:

[0024] Molecular weigh...

Embodiment 2

[0027] Embodiment 2: the synthesis of perfluorobutyltrimethoxy fluorosilicone resin

[0028]

[0029] (1) 100g of vinyltrimethoxysiloxane is added by weight into the reactor, 5g of dibenzoyl peroxide and 1g of methyl ethyl ketone peroxide are added, stirred evenly, and the solution is stirred at room temperature for 0.5 hour to obtain Prepolymer A.

[0030] (2) 100g 2-(perfluorobutyl) ethyl methacrylate is added to the reactor by weight, azobisisobutyronitrile and 3g tert-dodecyl mercaptan are added, stirred evenly, and The solution was stirred at room temperature for 1 hour to obtain prepolymer B.

[0031] (3) Add the above-mentioned prepolymers A100g and B50g into the reactor, add 5g of cobalt naphthenate, 1g of mercaptoethanol and 10g of 3-(methacryloyloxy)propyltrimethoxysilane coupling agent, Stir evenly, and stir the solution at room temperature for 5 hours to obtain perfluorobutyltrimethoxyfluorosilicone resin.

[0032] The resin test results are as follows:

[0...

Embodiment 3

[0036] Embodiment 3: the synthesis of perfluorobutyl tripropropoxy fluorosilicone resin

[0037]

[0038] (1) 100g vinyltripropoxysiloxane is added by weight in the reactor, add 1g of dibenzoyl peroxide and 5g methyl ethyl ketone peroxide, stir well, and the solution is stirred at room temperature for 2 hours, Prepolymer A is obtained.

[0039] (2) 100g 2-(perfluorobutyl) ethyl methacrylate is added by weight into the reactor, 5g of azobisisobutyronitrile and 1g of tert-dodecyl mercaptan are added, stirred evenly, and The solution was stirred at room temperature for 1 hour to obtain prepolymer B.

[0040] (3) Add the above-mentioned prepolymers A100g and B30g into the reactor, add 3g of cobalt naphthenate, 5g of mercaptoethanol and 1g of 3-glycidyl etheroxypropyl trimethoxysilane coupling agent, stir evenly, The solution was stirred at room temperature for 2 hours to obtain perfluorobutyl tripropropoxyfluorosilicone resin.

[0041] The resin test results are as follows: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses fluoro-siloxane resin, a preparation method thereof and application thereof as an artificial stone antifouling agent. The fluoro-siloxane resin, the preparation method and the application have the benefits that vinyl silicone, 2-(perfluorinated butyl) ethyl methyl acrylic ester and the like are adopted to prepare a series of fluoro-siloxane resin; the synthesis method is scientific and reasonable, so that a universal method for synthesizing a series of fluoro-siloxane resin is provided, and the preparation method is easy to get raw materials, wide in application range, high in yield and simple and feasible in industrial production operation.

Description

technical field [0001] The invention relates to the technical field of building material production, in particular to a fluorosilicone resin, a preparation method and an application thereof. Background technique [0002] The development of stone protective agents in foreign countries has a history of more than 30 years. Some countries such as Japan, Europe and the United States are in the leading position in the research of stone protective agents, and have gradually transitioned from solvent-based products to water-based products. research is relatively late. At present, the country has just established relevant industry standards, and most of the protective agents used are imported from Japan, Europe, America and other countries. In some European and American countries, since the beginning of this century, research on professional stone maintenance has been started to maintain the original brilliance of the stone and prolong its service life. At present, countries with m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F299/00C08F130/08C08F120/24C04B41/49
Inventor 王桦郭延举李淑英张立燕乔玉春
Owner 杜丽红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products