A steel plate for load-bearing shelves and its processing technology

A processing technology and steel plate technology, applied in the field of steel plate and its processing technology, can solve the problems of broken storage equipment, increased storage costs, low-temperature toughness of steel plate, etc.

Inactive Publication Date: 2016-08-31
SUZHOU JIN YUAN OIL MACHINERY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially when it is used to store a high-weight cargo, the storage equipment often breaks in a short time due to insufficient transverse yield strength of the steel plate, which increases storage costs; and in some cold regions, the low-temperature toughness of the steel plate bearing the load on the shelf It is not high, and it often causes the storage equipment to break in a short time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This embodiment is a steel plate used for load-bearing shelves. The composition and mass percentage of the steel plate are: C: 0.37%, Mn: 0.41%, Si: 0.057%, P: 0.0068%, S: 0.002%, Nb: 0.09 %, V: 0.04%, Ti: 0.7%, Al: 0.05%, N: 0.006%, H: 0.00020%, Cu: 0.17%, Cr: 1.7%, Mo: 0.33%, Lanthanum: 0.02%, Ce: 0.01 %, praseodymium: 0.05%, the balance is Fe and unavoidable impurities; the first phase in the steel plate is ferrite, the second phase is pearlite, and the volume percentage of the second phase from the surface to 1 / 4 thickness is 3.5 %, the volume percentage of the second phase from 1 / 4 thickness to the center is 6.0%, and there is no band structure; the average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate is 4.5 μm, and the average diameter of pearlite clusters is 5.02μm, the average grain diameter of ferrite from 1 / 4 thickness to the center is 4.0μm, and the average diameter of pearlite group is 6.0μm.

[0045] The processing technol...

Embodiment 2

[0053] This embodiment is a steel plate used for load-bearing shelves. The composition and mass percentage of the steel plate are: C: 0.38%, Mn: 0.42%, Si: 0.067%, P: 0.007%, S: 0.003%, Nb: 0.1 %, V: 0.05%, Ti: 0.8%, Al: 0.06%, N: 0.001%, H: 0.000120%, Cu: 0.18%, Cr: 1.8%, Mo: 0.34%, Lanthanum: 0.03%, Ce: 0.02 %, praseodymium: 0.06%, the balance is Fe and unavoidable impurities; the first phase in the steel plate is ferrite, the second phase is pearlite, and the volume percentage of the second phase from the surface to 1 / 4 thickness is 3.7 %, the volume percentage of the second phase from 1 / 4 thickness to the center is 6.12%, and there is no band structure; the average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate is 4.6 μm, and the average diameter of pearlite clusters is 5.1 μm, the average grain diameter of ferrite from 1 / 4 thickness to the center is 4.1 μm, and the average diameter of pearlite group is 6.1 μm.

[0054] The processing techn...

Embodiment 3

[0062] This embodiment is a steel plate used for load-bearing shelves. The composition and mass percentage of the steel plate are: C: 0.39%, Mn: 0.43%, Si: 0.07%, P: 0.008%, S: 0.004%, Nb: 0.11 %, V: 0.06%, Ti: 0.9%, Al: 0.07%, N: 0.002%, H: 0.0001%, Cu: 0.19%, Cr: 1.9%, Mo: 0.35%, Lanthanum: 0.04%, Ce: 0.02 %, praseodymium: 0.07%, the balance is Fe and unavoidable impurities; the first phase in the steel plate is ferrite, the second phase is pearlite, and the volume percentage of the second phase from the surface to 1 / 4 thickness is 3.8 %, the volume percentage of the second phase from 1 / 4 thickness to the center is 6.2%, and there is no band structure; the average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate is 4.7 μm, and the average diameter of pearlite clusters is 5.2μm, the average grain diameter of ferrite from 1 / 4 thickness to the center is 4.2μm, and the average diameter of pearlite group is 6.2μm.

[0063] The processing technology ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a steel plate for a storage rack to bear load. The steel plate is prepared from such components as 0.37-0.39% of C, 0.41-0.43% of Mn, 0.05-0.07% of Si, 0.006-0.008% of P, 0.002-0.004% of S, 0.09-0.11% of Nb, 0.04-0.06% of V, 0.7-0.9% of Ti, 0.05-0.07% of Al, less than or equal to 0.006% of N, less than or equal to 0.00020% of H, 0.17-0.19% of Cu, 1.7-1.9% of Cr, 0.33-0.35% of Mo, 0.02-0.04% of lanthanum, 0.01-0.02% of cerium, 0.05-0.07% of praseodymium, and the balance of Fe and inevitable impurities. The transverse yield strength of the steel plate is greater than or equal to 220MPa; and the steel plate is high in ductility and excellent in low-temperature toughness.

Description

technical field [0001] The invention relates to a steel plate and a processing technology thereof, in particular to a steel plate used for load-bearing shelves and a processing technology thereof. Background technique [0002] Storage equipment refers to technical devices and tools that can meet the needs of storage and storage of goods. Storage equipment is the main symbol of the level of storage and logistics technology. Modern storage equipment reflects the development of modern storage and logistics technology. Shelves in storage equipment are relatively commonly used equipment. Due to the storage needs of special materials, the use conditions and environment of shelves are becoming more and more harsh, and the thickness of steel plates is required to be thicker and thicker. Correspondingly, the technology of steel plates used in storage equipment The requirements are also constantly increasing. Especially when it is used to store a high-weight cargo, the storage equipm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/28B23P15/00
Inventor 李琪
Owner SUZHOU JIN YUAN OIL MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com