A preparation method of physical anti-fouling nanocomposite ceramic spheres

A technology of nano-composite materials and ceramic balls is applied in the field of scale prevention by physical methods, which can solve the problems of high operation cost, serious water consumption and high maintenance cost, and achieve the effects of simple production process, wide source of raw materials and low cost.

Active Publication Date: 2016-06-15
天津健威泽节能环保科技股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-scaling and corrosion-inhibiting effect of the dosing method is better, and the bactericidal and algae-killing agents can be added at the same time. It is an ideal water treatment method for the cooling water system, but there are high operating costs, serious water consumption, and environmental problems. Disadvantages such as pollution and high maintenance costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of physical anti-fouling nanocomposite ceramic spheres
  • A preparation method of physical anti-fouling nanocomposite ceramic spheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of nanocomposite ceramic spheres of physical antifouling, wherein the composition and parts by weight are as follows:

[0028] 45 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 30 parts of kaolin; 5 parts of light rare earth (containing La element, Ce element, Nd element); 20 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn).

[0029] A method for preparing a physically antifouling nanocomposite ceramic sphere, comprising the following steps:

[0030] 1) prepare the following materials by weight:

[0031] 45 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 30 parts of kaolin; 5 parts of light rare earth (containing La element, Ce element, Nd element); 20 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn);

[0032] 2) powders that are processed into said materials respectively:

[0033] The particle size of tourmaline powder is 900nm, th...

Embodiment 2

[0038] A kind of nanocomposite ceramic spheres of physical antifouling, wherein the composition and parts by weight are as follows:

[0039] 55 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 10 parts of kaolin; 8 parts of light rare earth (containing La element, Ce element, Nd element); 27 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn).

[0040] A method for preparing a physically antifouling nanocomposite ceramic sphere, comprising the following steps:

[0041] 1) The first step, prepare the following materials by weight:

[0042] 55 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 10 parts of kaolin; 8 parts of light rare earth (containing La element, Ce element, Nd element); 27 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn);

[0043] 2) powders processed from the materials respectively: the particle size of tourmaline powder is 400nm, the pa...

Embodiment 3

[0048] A kind of nanocomposite ceramic spheres of physical antifouling, wherein the composition and parts by weight are as follows:

[0049] 45 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 35 parts of kaolin; 5 parts of light rare earth (containing La element, Ce element, Nd element); 15 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn).

[0050] A method for preparing a physically antifouling nanocomposite ceramic sphere, comprising the following steps:

[0051] 1) The first step, prepare the following materials by weight:

[0052]45 parts of tourmaline (the iron content of the tourmaline is less than 1.5%); 35 parts of kaolin; 5 parts of light rare earth (containing La element, Ce element, Nd element); 15 parts of copper-zinc alloy (containing 15- 40% Cu, 2.5-30% Zn, 2.5-8% Ni, 2.5-8% Sn);

[0053] 2) powders processed from the materials respectively: the particle size of tourmaline powder is 100nm, the par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a making method for physical anti-scaling nanocoposite ceramic ball particles. The making method is simple and low in cost, and the nanocomposite ceramic ball particles made through the method should be able to effectively prevent water scales from being generated, and effectively remove the water scales. According to the technical scheme, the making method for the physical anti-scaling nanocomposite ceramic ball particles includes the following steps that step1, by weight, the following materials of 20-85 parts of tourmaline, 10-40 parts of kaolin, 1-8 parts of light rare earth and 3-27 parts of copper zinc alloys are prepared; step2, the materials are machined to be powder of which the particle size ranges from 100 nm to 900 nm; step3, the powder is evenly mixed to make ball particles of which the particle size ranges from 2 mm to 5 mm; step4, the ball particles are sintered for 0.1-5 hours at the temperature of 700 DEG C-1100 DEG C, and then kept warm for 4-24 hours at the temperature of 45 DEG C-100 DEG C.

Description

technical field [0001] The invention belongs to the technology of anti-scaling by physical method, in particular to a preparation method of nano-composite ceramic spheres. Background technique [0002] Water is used as a heat exchange working medium, and an insurmountable obstacle is scaling. The texture of scale is relatively dense, and the thermal conductivity is low, which greatly reduces the heat transfer efficiency (according to experimental research, a thin scale of 0.6 mm can improve the heat transfer efficiency. reduced by more than 20%). [0003] In recent years, the anti-scaling technology and descaling technology have made great progress, but the scale is still hard to prevent and inexhaustible. Now commonly used anti-scaling and descaling methods in engineering include: softened water method, ultrasonic water treatment method, and chemical dosing method. [0004] (1) Softened water method: This water treatment method removes most of the calcium and magnesium io...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F3/10C22C30/06
Inventor 唐金泉周凯升金万金
Owner 天津健威泽节能环保科技股份有限公司