Silicate fireproof thermal insulation material and preparation method thereof

A fire-proof thermal insulation and silicate technology, applied in the field of fire-resistant materials, can solve the problems of poor thermal insulation effect, low compressive strength and high compressive strength, and achieve the effect of small bulk density, high compressive strength and improved compressive strength.

Active Publication Date: 2015-09-02
SHENZHEN SELEN SCI & TECH CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of large volume, poor heat preservation effect and low compressive strength of inorganic heat preservation materials in the prio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicate fireproof thermal insulation material and preparation method thereof
  • Silicate fireproof thermal insulation material and preparation method thereof
  • Silicate fireproof thermal insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0032] According to the components and contents in Table 2, the following preparation methods were used to prepare the silicate fireproof and thermal insulation materials of the present examples 1-3:

[0033] (1) Sodium silicate and azodicarbonamide are mixed, fully stirred, sealed and stored, and placed at room temperature for 24 hours;

[0034] (2) Add hollow glass microspheres, colloidal silicon dioxide, sodium fluorosilicate, polyether glycol, and stir evenly;

[0035] (3) add diphenylmethane diisocyanate, stir;

[0036] (4) Pour the above-mentioned slurry into the mold, bake at a constant temperature of 150°C for 1.5h, then raise the temperature to 190°C, and bake at this temperature for 3h, then raise the temperature to 350°C, and bake at this temperature for 3h , After foaming and demoulding, the silicate fireproof and thermal insulation material can be obtained.

[0037] Table 2

[0038]

Embodiment 4～6

[0040] According to the components and contents in Table 3, the following preparation methods were used to prepare the silicate fireproof and thermal insulation materials of the present embodiment 4-6:

[0041] (1) Mix potassium silicate, azobisisobutyronitrile, and bis-azoaminobenzene, stir well, seal and store, and place at room temperature for 72 hours;

[0042] (2) Add hollow glass microspheres, colloidal silicon dioxide, sodium fluorosilicate, polyether glycol, and stir evenly;

[0043] (3) Add diphenylmethane diisocyanate, polyphenyl polymethylene polyisocyanate, stir;

[0044] (4) Pour the slurry obtained above into a mold, bake at a constant temperature of 160°C for 1 hour, then raise the temperature to 210°C, and bake at this temperature for 2 hours, then raise the temperature to 400°C, and bake at this temperature for 2 hours, After foam molding, the mold is demoulded, and the silicate fire-proof and heat-insulating material is obtained.

[0045] table 3

[0046] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a silicate fireproof thermal insulation material composition. The silicate fireproof thermal insulation material composition is prepared from 100 parts by weight of water glass, 30-40 parts by weight of hollow glass microbeads, 0.5-1 part by weight of chemical foaming agent, 0.5-2 parts by weight of binder, 0.5-2 parts by weight of curing agent, 0.5-1 part by weight of polyether polyol and 0.5-1 part by weight of polyisocyanate; the fireproof thermal insulation material has the advantages of small volume weight, low heat conductivity coefficient and high compressive strength. The invention also provides a preparation method of the silicate fireproof thermal insulation material; the preparation method is simple in process, low in energy consumption and short in time.

Description

technical field [0001] The invention relates to a fireproof material, in particular to a silicate fireproof and thermal insulation material with small bulk density, low thermal conductivity and high compressive strength and a preparation method thereof. Background technique [0002] At present, there are two main types of materials used for building exterior wall insulation in my country: (1) Organic insulation materials: polystyrene foam materials, foam rubber materials, polyurethane foam materials, etc.; (2) Inorganic insulation materials: rock wool, slag wool , glass wool, cement foam materials, etc. Among them, although organic insulation materials have good thermal insulation properties and small bulk density, they have poor heat resistance and are easy to burn, and they release a lot of heat and produce a lot of toxic fumes during combustion, which will not only accelerate the spread of the epidemic, but also easily cause casualties. With the emphasis on fire protectio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B28/26
Inventor 侯毅管映亭胡树赵晨
Owner SHENZHEN SELEN SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap