Polysiloxane heat-reflective topcoat and preparation method thereof

A heat-reflecting topcoat, polysiloxane technology, applied in reflective/signal coatings, anti-corrosion coatings, coatings, etc., can solve problems such as poor gloss and color retention, and achieve less discoloration, lower use temperature, and recoatability. Good results

CN104946129AInactive Publication Date: 2015-09-30上海海悦涂料有限公司
5 Cites 1 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2015-09-30
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides a polysiloxane heat-reflective topcoat and a preparation method thereof. The polysiloxane heat-reflective topcoat comprises a component A and a component B, and the weight ratio of the component A to the component B is 8:(1-1.5); the component A comprises the following ingredients by weight: 30-40 parts of polysiloxane resin, 3-8 parts of a thermal insulation material, 0.6-0.9 part of a stabilizer, 25-48 parts of a mixed solvent, 0.2-0.5 part of a dispersant, 17-33 parts of an anti-aging pigment and an anti-aging filler, and 0.2-0.5 part of an anti-settling agent; the component B comprises the following ingredients by weight: 60-70 parts of a curing agent and 18-35 parts of a curing agent solvent. The polysiloxane heat-reflective topcoat is high in ageing-resistant performance, weather resistance and chemical resistance, has a heat reflection function, can be suitable for various construction methods, and is good in recoatability and excellent in cost performance; besides, external corrosion protection of the surface of coated steel is achieved, a lot of coating expenditures can be reduced, and the service life is prolonged.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a polysiloxane heat-reflecting topcoat and a preparation method thereof, belonging to the technical field of coatings. Background technique

[0002] In steel structure anti-corrosion engineering, coating has always been the most important, most economical and effective anti-corrosion method. At present, the corrosion of ships and general steel structures is mainly manifested in the damage of internal structures and parts exposed to atmospheric environments such as sunlight and salt spray.

[0003] The coatings used in domestic maintenance of steel structures and cabins are mainly alkyd and epoxy ester antirust primers, while alkyd coatings are mostly used for ship shells. The antirust primers and topcoats of these varieties have a protection period of only 1-2 years due to their poor water resistance, weather resistance, and chemical resistance, and even less than half a year in harsh environments.

[0004] In large-scale ant...

Examples

Embodiment

[0037] This embodiment provides a polysiloxane heat-reflecting topcoat, the topcoat includes A component and B component, and the weight ratio of A component and B component is 8:1; Wherein,

[0038] In parts by weight, component A includes: 30 parts by weight of polysiloxane resin, 5 parts by weight of heat insulating materials (aluminum powder and other heat insulating materials, in any ratio), 0.8 parts by weight of stabilizer (siloxane), Mixed solvent (15 parts by weight of xylene, 8 parts by weight of butyl acetate, 10 parts by weight of butanone), 0.2 parts by weight of dispersant (methoxypropyl acetate), anti-aging pigment, filler (12 parts by weight of imported rutile titanium dioxide part, 5 parts by weight of mica and 6 parts by weight of barium sulfate), anti-sedimentation agent (organic bentonite) 0.2-0.5 parts by weight;

[0039] In parts by weight, component B includes: 65 parts by weight of a curing agent (aliphatic isocyanate HDI trimer), and a solvent for the ...