Surface antiqued processing technology of antiqued product

A technology for processing crafts and products, which is applied in the field of antique products surface aging treatment technology, which can solve the problems of not being able to meet the aesthetic and practical needs of consumers, inconsistent antique decoration styles, and unrealistic effects, etc., to achieve better product color and antique Realistic effect and strong adhesion effect

Inactive Publication Date: 2015-12-16
宁波欧依欣卫浴有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the household products treated with OilRubbedBronze surface on the market have poor color, no sense of layering, unrealistic effect, and inconsistent with the antique decoration style; and the surface of the paint film is prone to scratches, peeling, corrosion, etc., which cannot satisfy consumers' expectations. High aesthetic and practical needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface antiqued processing technology of antiqued product
  • Surface antiqued processing technology of antiqued product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The surface of the substrate is mirror-polished, and the polished surface is inspected after the end to remove the polishing mud generated by polishing. Then electroplate a phosphor copper layer with a thickness of 10 μm on the surface of the substrate and conduct inspection to ensure that there are no pitting, blistering, mottled, waves, uneven plating, etc. on the surface of the phosphor copper layer. Then wash it with 5% dilute sulfuric acid solution to remove the oil on the surface, and hang it in the air for 3-5s. After emptying the excess water, wash it with water immediately. Then soak the base material in the antique solution prepared by cuprite blackening agent and water at a volume ratio of 0.3:1. The antique solution is heated to 80°C in advance and soaked until the surface of the base material turns black. Then take it out and rinse with water to remove the remaining antique liquid on the surface. Then dry it at a temperature of 80°C, and wipe and dry the s...

Embodiment 2

[0033] The surface of the substrate is mirror-polished, and the polished surface is inspected after the end to remove the polishing mud generated by polishing. Then electroplate a phosphor copper layer with a thickness of 10 μm on the surface of the substrate and conduct inspection to ensure that there are no pitting, blistering, mottled, waves, uneven plating, etc. on the surface of the phosphor copper layer. Then wash it with 5% dilute sulfuric acid solution to remove the oil on the surface, and hang it in the air for 3-5s. After emptying the excess water, wash it with water immediately. Then soak the base material in the antique solution prepared by cuprite blackening agent and water at a volume ratio of 0.3:1. The antique solution is heated to 80°C in advance and soaked until the surface of the base material turns black. Then take it out and rinse with water to remove the remaining antique liquid on the surface. Then dry it at a temperature of 85°C, and wipe the drying su...

Embodiment 3

[0035] The surface of the substrate is mirror-polished, and the polished surface is inspected after the end to remove the polishing mud generated by polishing. Then electroplate a phosphor copper layer with a thickness of 10 μm on the surface of the substrate and conduct inspection to ensure that there are no pitting, blistering, mottled, waves, uneven plating, etc. on the surface of the phosphor copper layer. Then wash it with 5% dilute sulfuric acid solution to remove the oil on the surface, and hang it in the air for 3-5s. After emptying the excess water, wash it with water immediately. Then soak the base material in the antique solution prepared by cuprite blackening agent and water at a volume ratio of 0.3:1. The antique solution is heated to 80°C in advance and soaked until the surface of the base material turns black. Then take it out and rinse with water to remove the remaining antique liquid on the surface. Then dry it at a temperature of 85°C, and wipe the drying su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a surface antiqued processing technology of an antiqued product. The surface antiqued processing technology comprises the steps that a base material is preprocessed; a basic layer is formed on the preprocessed base material; the base material with the formed basic layer is soaked in antiqued liquid, wherein the antiqued liquid is prepared from a blackening agent and water according to the volume ratio being (0.3-0.4):1; and the soaked base material is postprocessed to obtain the antiqued product. The surface antiqued processing technology of the antiqued product is simple, and the product is good in color and luster and realistic in antiqued effect and keeps consistent with an antiqued decoration style. The surface of the product has the beneficial effects of being high in hardness, strong in adhesive force, high in corrosion resistance and the like.

Description

technical field [0001] The invention relates to a surface treatment process, in particular to a surface aging treatment process for antique products. Background technique [0002] With the continuous deepening of China's reform and opening up and the acceleration of the internationalization process of Chinese enterprises, Chinese enterprises have set their sights on the international market and actively participated in international competition, allowing countries around the world to re-understand Chinese enterprises and the Chinese culture they contain. Therefore, with the continuous improvement of people's living standards, more and more people like to study Chinese traditional culture, and people's favorite decoration style has also begun to change to antique, more and more people like antique decoration style, so antique The household product market has broad prospects. [0003] At present, among the antique household products, OilRubbedBronze is a special surface treat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44D5/00B44F9/10
Inventor 杨欣
Owner 宁波欧依欣卫浴有限公司