A kind of lialo2 coating lini1-xcoxo2 lithium ion battery cathode material and preparation method thereof

A technology for lithium ion batteries and cathode materials, which is applied in battery electrodes, secondary batteries, circuits, etc., can solve the problems of uneven particle size distribution and surface coating of products, difficult to control stoichiometric ratio, and poor electrochemical performance. Achieve the effect of enhancing high-current charge-discharge performance and thermal stability, excellent electrochemical performance, and improving specific capacity

Active Publication Date: 2018-10-16
UNIV OF ELECTRONICS SCI & TECH OF CHINA
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method overcomes the shortcomings of the simple solid-phase synthesis method, such as long preparation time, difficulty in controlling the stoichiometric ratio, uneven product particle size distribution and surface coating, and poor electrochemical performance. The prepared product has high purity, high chemical uniformity, Good coating effect, high crystal quality, fine and uniform distribution of product particles, excellent electrochemical performance and low manufacturing cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lialo2 coating lini1-xcoxo2 lithium ion battery cathode material and preparation method thereof
  • A kind of lialo2 coating lini1-xcoxo2 lithium ion battery cathode material and preparation method thereof
  • A kind of lialo2 coating lini1-xcoxo2 lithium ion battery cathode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 1.08-1.15mol lithium hydroxide and 1.0mol Ni prepared by co-precipitation 0.8 co 0.2 (OH) 2 Mix the precursors evenly, put them into a ball mill, add an appropriate amount of absolute ethanol, grind to the required particle size, evaporate, dry, remove and recover the ethanol, and the obtained mixture containing Li, Ni, and Co is heated in oxygen-enriched air and at an appropriate temperature. (350~500℃) pre-fired for 2-10h, take out and grind, then sinter in oxygen-enriched air or pure oxygen atmosphere and at an appropriate temperature (650~900℃) for 10-16h, take out and grind and sieve , take the product between 1 and 25 μm to get LiNi 0.8 co 0.2 o 2 parent cathode material. XRD and electrochemical performance tests were carried out on the material.

[0042] 1.0mol LiNi 0.8 co 0.2 o 2 About 98.0g of the matrix positive electrode material is dispersed in an appropriate amount of deionized water, stirred to obtain a uniform suspension A; a proportional amount ...

Embodiment 2

[0045] Add 1.08-1.15mol of lithium hydroxide, 0.80mol of nickel acetate, 0.20mol of cobalt acetate and 1.2mol of citric acid into the container and mix evenly. Add an appropriate amount of deionized water into the container and stir vigorously until a transparent dark sol is obtained. With stirring, the sol was evaporated on a water bath at 50-80°C until a dark colored gel was obtained. Then the gel was dried overnight at 120° C. in a blast oven to obtain a dark xerogel containing Li, Ni, and Co. The obtained dark xerogel containing Li, Ni and Co is pre-calcined for 2-10 hours in oxygen-enriched air at a suitable temperature (350-550° C.), taken out and ground to obtain a precursor. The precursor is then sintered in oxygen-enriched air or pure oxygen atmosphere and at an appropriate temperature (650-900°C) for 10-16 hours, taken out, ground and sieved, and the product with a thickness of 1-25 μm is obtained to obtain LiNi 0.8 co 0.2 o 2 parent cathode material. XRD and ele...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of lithium ion batteries, and provides LiNi1-xCoxO2@LiAlO2, a lithium-ion battery cathode material LiNi1-xCoxO2@LiAlO2 modified on the surface of LiNi1-xCoxO2 coated with high thermal stability and a preparation method thereof, to overcome LiNi1-xCoxO2(0

Description

technical field [0001] The invention belongs to the field of lithium-ion batteries, and relates to a lithium-ion battery positive electrode material and a preparation method thereof, specifically LiNi, a lithium-ion battery positive electrode material 1-x co x o 2 @LiAlO 2 and a preparation method thereof, wherein 0<x≤0.5. Background technique [0002] With the deteriorating global environment and climate, energy conservation and emission reduction are imminent, and the international community is paying more and more attention to the development and application of new energy and renewable clean energy. As an excellent performance and environmentally friendly secondary battery, lithium-ion batteries have the advantages of high energy density, fast charging, small self-discharge, long-term storage, excellent cycle performance, and no memory effect. They have been widely used in various portable electronic devices. and will become the preferred power source for electric ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/485H01M4/525H01M10/0525
CPCH01M4/366H01M4/485H01M4/525H01M10/0525Y02E60/10
Inventor 刘兴泉王治国熊伟强赵红远陈炳张峥
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap