A kind of magnetic butyl damping composite material for vehicle and its preparation method

The technology of damping composite material and magnetic material is applied in the field of magnetic butyl damping composite material for vehicles and its preparation. The effect of ease and manufacture

Active Publication Date: 2017-09-26
WUHU HAICHENG RUBBER & PLASTIC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to reduce the noise caused by metal skin vibration, Chinese patent CN 201310258628.7 published on September 11, 2013 discloses a butyl rubber-based high-performance material, which contains butyl rubber, damping fillers, etc., which can effectively reduce vibration At the same time, the metal skin is thickened. This kind of material itself has self-adhesiveness and can be effectively attached to the metal skin. However, due to the long service life of the car, the viscosity will decrease, and there will be butyl damping compound. Risk of material falling from the metal skin
The Chinese patent CN 03134927.7 disclosed on September 15, 2004 discloses a magnetic damping plate and its preparation method, which provides a prefabricated magnetic damping plate, which can easily achieve accurate and reliable thickness on the skin of a motor vehicle. Controlled and combined with a firm damping rubber layer, but because the raw material of this damping plate contains petroleum asphalt, it is harmful to the environment, so it also has certain defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of magnetic butyl damping composite material for vehicle, is made up of the material shown in table 1:

[0043] Table 1

[0044] raw material

weight percentage

Butyl rubber 1675N

12%

Solid polyisobutylene rubber B100

5%

Liquid polyisobutylene PB2400

10%

Terpene phenolic resin TP2040

8%

Barium sulfate 800 mesh

18%

barium ferrite

40%

Naphthenic oil Nytex8200

5%

Carbon black MA-100

2%

[0045] The preparation method of the above-mentioned magnetic butyl damping composite material for vehicles is as follows:

[0046] (a) thin pass: butyl rubber and solid polyisobutylene rubber are placed on the open rubber mixer and thin pass 5 times, with a roll distance of 2mm, to obtain raw rubber;

[0047] (b) Internal mixing: put the plasticized raw rubber into the internal mixer, add liquid polyisobutene, terpene phenol resin, barium sulfate, barium ferrite, carbon black, pressuri...

Embodiment 2

[0052] A kind of magnetic butyl damping composite material for vehicle, is made up of the material shown in table 2:

[0053] Table 2

[0054] raw material

weight percentage

Butyl rubber 1675N

15%

Solid polyisobutylene rubber B150

2%

Liquid polyisobutylene PB1400

8%

Terpene phenolic resin TP96

10%

Barium sulfate 800 mesh

13%

barium ferrite

45%

Naphthenic oil Nytex8100

5%

Carbon black N330

2%

[0055] The preparation method of the above-mentioned magnetic butyl damping composite material for vehicles is as follows:

[0056] (a) thin pass: butyl rubber and solid polyisobutylene rubber are placed on the open rubber mixer and thin pass 6 times, with a roll distance of 2mm, to obtain raw rubber;

[0057] (b) Internal mixing: put the plasticized raw rubber into the internal mixer, add liquid polyisobutene, terpene phenol resin, barium sulfate, barium ferrite, carbon black, pressurized in...

Embodiment 3

[0062] A kind of magnetic butyl damping composite material for vehicle, is made up of the material shown in table 3:

[0063] table 3

[0064] raw material

weight percentage

Butyl rubber JSR268

12%

Solid polyisobutylene rubber B100

10%

Liquid polyisobutylene PB1300

8%

Terpene phenolic resin TP2040

10%

Mica powder 400 mesh

5%

barium ferrite

50%

Naphthenic oil Nytex8100

4%

Carbon black N330

1%

[0065] The preparation method of the above-mentioned magnetic butyl damping composite material for vehicles is as follows:

[0066] (a) thin pass: butyl rubber and solid polyisobutylene rubber are placed on the open rubber mixer and thin pass 7 times, with a roll distance of 3mm, to obtain raw rubber;

[0067] (b) Internal mixing: Put the plasticized raw rubber into the internal mixer, add liquid polyisobutene, terpene phenol resin, mica powder, barium ferrite, carbon black, pressurized int...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
thicknessaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a magnetic butyl damping composite material for automobiles and a preparation method of the magnetic butyl damping composite material. The composite material comprises following raw materials: 10%-15% of butyl rubber, 5%-20% of polyisobutylene, 5%-10% of petroleum resin, 5%-20% of filler, 30%-50% of a magnetic material, 2%-8% of processing oil and 1%-5% of carbon black. The raw materials are subjected to tight milling, mixing, extrusion and magnetization, and the magnetic butyl damping composite material coated with aluminum foil and used for the automobiles is prepared. The prepared magnetic butyl damping composite material for the automobiles can act on metal skin effectively for a long time, noise caused by vibration can be reduced very well in service cycles of the automobiles, and the composite material is more environment-friendly than a traditional magnetic petroleum asphalt damping mat.

Description

technical field [0001] The invention relates to a butyl damping composite material, in particular to a magnetic butyl damping composite material for vehicles and a preparation method thereof. Background technique [0002] During the driving process of the car, due to the work of the engine, the uneven road surface will cause vibration, and the vibration will be transmitted to the metal skin of the body through the frame. The metal skin will convert this vibration energy into noise, and the noise will make passengers feel uncomfortable. In terms of structure, the steel plate used for the metal skin is very thin, about 1mm. In order to reduce the noise caused by metal skin vibration, Chinese patent CN 201310258628.7 published on September 11, 2013 discloses a butyl rubber-based high-performance material, which contains butyl rubber, damping fillers, etc., which can effectively reduce vibration At the same time, the metal skin is thickened. This kind of material itself has sel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/22C08L23/20C08L45/00C08L57/02C08L93/04C08L91/00C08L91/06C08K3/04C08K3/30C08K3/34C08K3/26
CPCC08L23/20C08L23/22C08L2205/025C08L2205/03C08L45/00C08L91/00C08K3/04C08K2003/3045C08L91/06C08K3/34C08L57/02C08K2003/265C08L93/04
Inventor 谢宇邹天一
Owner WUHU HAICHENG RUBBER & PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products