Novel antibacterial polyester peach skin imitation fabric

A technology of imitating peach skin velvet and fabrics, which is applied in the fields of biochemical fiber processing, textile and papermaking, fiber processing, etc., can solve the problems of insufficient antibacterial properties and high price of fabrics, and achieve good antibacterial properties, improved softness, and soft gloss. Effect

Active Publication Date: 2016-01-13
CHANGXING RONGFENG TEXTILE CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of enzymes is relatively high, and the antibacterial properties of the fabrics made are not good enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel antibacterial polyester peach skin imitation fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A preparation method of a novel antibacterial imitation jeanette fabric, the steps are as follows:

[0022] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0023] Wherein the concentration of the caustic soda that adopts during singeing is 90g / L,

[0024] (2) Grinding: use metal abrasive grains for dry grinding;

[0025] (3) Microbial modification treatment:

[0026] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.2:1.5:0.2;

[0027] The brushed fabric is evenly sprayed with bacteria agent, and fermented at 38°C for 52 hours;

[0028] After fermentation, wash with warm water and dry;

[0029] (5) Polishing treatment: polishing the modified fabric;

[0030] (6) Dyeing according to conventional method...

Embodiment 2

[0032] A preparation method of a novel antibacterial imitation jeanette fabric, the steps are as follows:

[0033] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0034] Wherein the concentration of the caustic soda that adopts during singeing is 105g / L,

[0035] (2) Grinding: use metal abrasive grains for dry grinding;

[0036] (3) Microbial modification treatment:

[0037] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.2:1.5:0.1;

[0038] The brushed fabric is evenly sprayed with bacteria agent and fermented at 38°C for 65 hours;

[0039] After fermentation, wash with warm water and dry;

[0040] (5) Polishing treatment: polishing the modified fabric;

[0041] (6) Dyeing according to conventional method...

Embodiment 3

[0043] A preparation method of a novel antibacterial imitation jeanette fabric, the steps are as follows:

[0044] (1) The blending ratio of soybean fiber and cotton fiber is 3:7 for blending according to the weight percentage; conventional singeing, whitening and drying are carried out to the blended fabric;

[0045] Wherein the concentration of the caustic soda that adopts during singeing is 100g / L,

[0046] (2) Grinding: use metal abrasive grains for dry grinding;

[0047] (3) Microbial modification treatment:

[0048] Bacillus licheniformis, Sphingomonas, Lactococcus lactis, and Bifidobacterium are formulated into a composite bacterial agent according to the quantitative ratio of 1:0.2:1.5:0.2;

[0049] The brushed fabric is evenly sprayed with bacteria agent and fermented at 38°C for 60 hours;

[0050] After fermentation, wash with warm water and dry;

[0051] (5) Polishing treatment: polishing the modified fabric;

[0052] (6) Dyeing according to conventional method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a novel antibacterial polyester peach skin imitation fabric. The method is as below: conducting conventional singeing, whitening and drying on blended fabrics; conducting dry sanding; preparing Bacillus licheniformis, Sphingomonas, Lactococcus lactis and Bifidobacterium in the ratio of 1:0.2:1.5:0.1-0.2 into a compound inoculant; evenly spraying the after treatment inoculant on the sanded fabric, and conducting low temperature fermentation at 38 DEG C for 52-65 h; after fermentation, rinsing with warm water, and drying; polishing the modified fabric; and dyeing according to the conventional method, shaping and drying to obtain a finished product. The processing method of the invention is natural environment-friendly and residue-free, does not cause environmental pollution and belongs to the green technology. The prepared polyester peach skin imitation fabric has the advantages of good handle, softness, delicacy, soft gloss, good antibacterial property, and is a novel fabric with a very high market potential; and the prepared polyester peach skin imitation fabric has a greatly improved mellowness compared to ordinary pure cotton polyester peach skin imitation fabric subjected to softening finishing.

Description

technical field [0001] The invention relates to a novel antibacterial imitation jeanette fabric, which belongs to the technical field of textiles. Background technique [0002] Peach skin is a novel thin pile fabric of microfiber fabric, which is born out of artificial suede, and has a softer texture because it has not been wet-processed with polyurethane. And because the down is shorter, there is almost no down on the surface, but the skin can feel it, so that the feel and appearance are more delicate and unique. The luster of peach skin is soft and elegant. Compared with artificial suede, it gives consumers a sense of novelty and suits people's curious consumption psychology, so it quickly became popular in the international market. Tencel is treated to obtain a peach skin feel. The formation of the unique style of peach skin fabrics can be said to be based on ultra-fine denier high-density thin fabrics, and sanding finishing is the key to the product. The main factors ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M16/00D06M101/04D06M101/06
Inventor 许蓉许建斌
Owner CHANGXING RONGFENG TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com