Montmorillonite-containing functional toothpaste and preparation method thereof

A montmorillonite, functional technology, applied in the field of montmorillonite functional toothpaste and its preparation, can solve the problems of rough particles, enamel wear on the tooth surface, poor adsorption, etc., to prevent bacterial invasion, reduce tooth wear, prevent The effect of wound infection

Pending Publication Date: 2016-02-03
SHANDONG SBOND PHARMA
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The shortcomings of the above patents are: calcium carbonate is used as the abrasive, its hardness is relatively high, the particles are rough, no stickiness, poor adsorption, and long-term use is easy to cause wear on the enamel on the tooth surface
The weak point of this patent is that adopt antibacterial metal ion such as Ag in this technology + 、Cu 2+ etc. Since more antibacterial ions are heavy metal ions, they will have greater side effects on the human body
The disadvantage of the above-mentioned patent is that nano-montmorillonite is used in this technology. The known content is that if montmorillonite is prepared into nano-montmorillonite, it is currently prepared by intercalation. The intercalation agent can be selected from quaternary ammonium salts. The particle size of nano-montmorillonite is small, and it only plays an adsorption role in this patent
So far, montmorillonite has not been reported as an abrasive in toothpaste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Montmorillonite-containing functional toothpaste and preparation method thereof
  • Montmorillonite-containing functional toothpaste and preparation method thereof
  • Montmorillonite-containing functional toothpaste and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0244] Embodiment 1: a kind of preparation method of montmorillonite toothpaste

[0245] 1. A montmorillonite functional toothpaste is made by parts by mass of the following raw materials:

[0246]

[0247] 2. The preparation method is as follows:

[0248] (1) Pulverize the montmorillonite, pass through a 100-mesh sieve, and then use laser particle size measurement to obtain an average particle size of 8 to 17 μm;

[0249] (2) the montmorillonite that step (1) obtains is removed iron wherein by magnetic separation equipment;

[0250] (3) Add deionized water to step (2) to make mass ratio montmorillonite: deionized water=1:4, carry out ultrasonic treatment, ultrasonic frequency is 40KHz, continue to stir for 1h, and make montmorillonite suspension solution ,spare;

[0251] (4) Take each raw material according to the formula quantity, and glycerin and sorbitol are configured into a solution with a mass concentration of 70% with deionized water for subsequent use; then sodi...

Embodiment 2

[0254] Embodiment 2: A kind of preparation method of montmorillonite functional toothpaste

[0255] 1, a kind of montmorillonite toothpaste, is made by mass parts by following raw material:

[0256]

[0257] 2. The preparation method is as follows:

[0258] (1) Pulverize the montmorillonite, pass through a 110-mesh sieve, and then use laser particle size measurement to obtain an average particle size of 8 to 27 μm;

[0259] (2) step (1), remove iron wherein by magnetic separation equipment;

[0260] (3) Add deionized water to step (2) to prepare a mass ratio of montmorillonite: deionized water=1:10, carry out ultrasonic treatment, the ultrasonic frequency is 45KHz, continue to stir for 1.5h, make a suspension solution, and set aside ;

[0261] (4) Take each raw material according to the formula quantity, and glycerin and sorbitol are configured into a solution with a concentration of 70% for subsequent use with deionized water; then sodium carboxymethylcellulose, sodium ...

Embodiment 3

[0264] Embodiment 3: a kind of preparation method of montmorillonite functional toothpaste

[0265] 1, a kind of montmorillonite toothpaste, is made by mass parts by following raw material:

[0266]

[0267]

[0268] 2. The preparation method is as follows:

[0269] (1) Pulverize the montmorillonite, pass through a 90-mesh sieve, and then use laser particle size measurement to obtain an average particle size of 8 to 27 μm;

[0270] (2) step (1), remove iron wherein by magnetic separation equipment;

[0271] (3) Add deionized water to step (2) to prepare a mass ratio of montmorillonite: deionized water=1:5, carry out ultrasonic treatment, the ultrasonic frequency is 40KHz, continue to stir for 1h, make a suspension solution, and set aside;

[0272] (4) Take each raw material according to the formula quantity, and glycerin and sorbitol are configured into a solution with a concentration of 70% for subsequent use with deionized water; then sodium carboxymethylcellulose, s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Dynamic viscosityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses montmorillonite-containing functional toothpaste and a preparation method thereof. The toothpaste comprises an abrasive and auxiliary materials. The abrasive is montmorillonite, whose weight percentage in the toothpaste is 5-30%. The auxiliary materials are any auxiliary materials that can be accepted and needed by the toothpaste, and mainly contain a humectant, an adhesive, a foaming agent, essence, sodium saccharin and other additives. The montmorillonite-containing functional toothpaste has tooth-cleaning, haemostasis, antibiosis and other effects, the toothpaste is used partially, so that the absorption and utilization problems do not exist, and the usage is safer.

Description

technical field [0001] The invention relates to a montmorillonite functional toothpaste with high cleaning power, excellent tooth brushing taste, and the effect of inhibiting dental plaque and (or) alleviating inflammatory manifestations such as redness, swelling and bleeding of gums and a preparation method thereof, belonging to the field of daily chemical products . Background technique [0002] Toothpaste is a cleaning product commonly used in daily life and has a long history. With the continuous development of science and technology, the continuous improvement and perfection of process equipment, various types of toothpaste have come out one after another, and the quality and grade of products have been continuously improved. Now the variety of toothpaste has developed from a single clean toothpaste to a complete variety and multiple functions. , hundreds of brands of multi-functional toothpaste, to meet the needs of different levels of consumption. The quality of too...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/73A61K8/46A61K8/34A61K8/26A61Q11/00A61P1/02A61P7/04A61P31/04
CPCA61K8/26A61K8/345A61K8/463A61K8/731A61Q11/00
Inventor 乔敏袁武杰刘钢李红新孟震晓
Owner SHANDONG SBOND PHARMA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap