Ultrasonic Fatigue Test Method for Metals with Plate Specimens Containing Equal Section Sections

A fatigue test, constant section technique, applied to the analysis of solids with sonic/ultrasonic/infrasonic waves in the same direction

Active Publication Date: 2018-10-09
武汉钢铁有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention mainly solves the following three problems:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic Fatigue Test Method for Metals with Plate Specimens Containing Equal Section Sections
  • Ultrasonic Fatigue Test Method for Metals with Plate Specimens Containing Equal Section Sections
  • Ultrasonic Fatigue Test Method for Metals with Plate Specimens Containing Equal Section Sections

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0136] Taking a steel material for automobile sheets as an example, it is assumed that the dimensional accuracy is well controlled during the processing of the sample.

[0137] 1. Measure the elastic modulus E=206GPa and the density ρ=7850kg / m of steel materials for automobile panels 3 .

[0138] 2. Design the sample size. The preset axial tension and compression specimens are plate-shaped ultrasonic fatigue specimens with equal cross-sections, such as image 3 shown. First draw up its size parameters, L 1 =12.5mm, L 2 =20mm,b 1 = 3mm, b 2 = 10mm, b 1 is the thickness of the equal section section of the plate, b 2 is the thickness at both ends of the plate, L 1 is half of the length of the constant section section of the plate, L 2 is the variable section length of the plate. When calculating, convert all known parameters into mm, g, ms dimensional units, and calculate the length L at both ends of the sample from the calculation formula of the length at both ends of...

Embodiment 2

[0144] Taking the same steel material for automobile sheets as in Example 1 as an example, it is assumed that the dimensional accuracy is not well controlled during the processing of the sample, and the actual size of the sample deviates greatly from the design size due to surface grinding after the sample is processed .

[0145] 1. Measure the elastic modulus E=206GPa and the density ρ=7850kg / m of steel materials for automobile panels 3 .

[0146] 2. Design the sample size. The preset axial tension and compression specimens are plate-shaped ultrasonic fatigue specimens with equal cross-sections, such as image 3 shown. First draw up its size parameters, L 1 =12.5mm, L 2 =20mm,b 1 = 3mm, b 2 = 10mm, b 1 is the thickness of the equal section section of the plate, b 2 is the thickness at both ends of the plate, L 1 is half of the length of the constant section section of the plate, L 2 is the variable section length of the plate. When calculating, convert all known p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
elastic modulusaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metal ultrasonic fatigue testing method of a uniform cross section segment-containing plate-shaped sample. The method comprises the following parts: a first part, firstly, according to density and elastic modulus of a test material, and a dimension designing formula of the uniform cross section segment-containing plate-shaped ultrasonic fatigue sample under a axial tension-compression loading is calculated by analysis; a second part, a stress transformation formula between the uniform cross section segment-containing plate-shaped sample and an arc-shaped sample is derived, a stress of the uniform cross section segment-containing plate-shaped ultrasonic fatigue sample is transformed into a stress corresponding to the arc-shaped sample on a system control software, and a ultrasonic fatigue test control of the uniform cross section segment-containing plate-shaped sample is completed by using existing equipment and software; a third part, a stress correction formula is derived, when a deviation exists between an actual size and a design size of the uniform cross section segment-containing plate-shaped sample, so that more accurate test control is guaranteed. The method is suitable different metal materials, and the cover range is wide; the method can be used for completing an ultra-high cycle fatigue test of the uniform cross section segment-containing plate-shaped sample, upgrade is not needed, and the cost is saved.

Description

technical field [0001] The invention relates to the field of ultrasonic fatigue performance testing of metal materials, in particular to a metal ultrasonic fatigue test method with plate-shaped samples with equal cross-section sections. Background technique [0002] Fatigue phenomenon is a phenomenon in which structural materials form cracks or further expand cracks until they are completely broken after a certain number of cycles under cyclic loading. Statistics show that more than 80% of structural strength failures are caused by fatigue, so the fatigue performance testing and research of materials is of great significance. Traditional fatigue performance research generally takes 10 7 as the limit cycle. In fact, some high-strength steels used in key components, or structural steels subjected to high-frequency loads, often have an actual service life of 10 years. 8 ~10 10 Weeks, more and more results have also confirmed that many engineering steels in 10 7 Fatigue fra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N29/12
Inventor 彭文杰薛欢陈一鸣刘冬严龙曾永龙张彦文
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More