Soft shell material and preparation method thereof

A technology of soft nails and raw materials, applied in manicure or pedicure tools, applications, clothing, etc., can solve the problems of real nails such as reduced comfort, insufficient firmness, and low fees, so that it is not easy to scratch or notch, The preparation method is simple and the material is soft

CN105315650AInactive Publication Date: 2016-02-10TIANJIN HUA YING PRINTING
4 Cites 3 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2016-02-10
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention relates to a soft shell material and a preparation method thereof. The soft shell material is composed of the following components in parts by weight: 30 to 50 parts of TPU, 10 to 20 parts of TPEE, 10 to 15 parts of ABS resin, 5 to 8 parts of SBS resin, and 2 to 5 parts of DOA resin, and is prepared by the following steps: mixing the components mentioned above, insulating the mixture from air, and connecting the mixture with glass under pressure. The provided soft shell material is soft and wear resistant. The shell made of the soft shell material is comfortable and close-fitting, and scratches or notches cannot be easily generated on the surface. Furthermore, the preparation method is simple and can be applied to massive industrial production.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of nail patch production, in particular to a method for preparing soft nail materials. Background technique

[0002] Patch nails are the most popular among various nail art techniques at present. Its characteristic is that it can visually change the shape of the fingers, modify the shape of the hands, and give people a sense of slenderness, so as to make up for the regret of the unsightly shape of the hands.

[0003] There are many types of pasted nails, mainly including shallow pasted nails, half pasted nails and full pasted nails. Among them, shallow nails are also called C-type nails, or front-edge patches. This kind of nails must be used in combination with crystal nail powder or phototherapy gel. (toenail) must-have material, cannot be pasted on the real nail independently. Shallow stickers have various colors and different lengths. The common ones are white, transparent, natural color, various colors, and even...

Examples

Embodiment 1

[0018] A soft armor material, made of TPU (thermoplastic polyurethane elastomer rubber), TPEE (thermoplastic polyester elastomer), ABS resin, SBS resin (styrene-butadiene-styrene triblock copolymer) and DOA resin powder Composition, among them, TPU45kg, TPEE15kg, ABS12kg, SBS7kg, DOA4kg.

[0019] The preparation method of above-mentioned soft armor material, concrete steps are as follows:

[0020] (1) Weigh TPU45kg, TPEE15kg, ABS12kg, SBS7kg, DOA4kg as raw materials;

[0021] (2) After the components are mixed evenly, under the condition of isolating the air, put them into the mold for glass crimping, and the mold is an annular stainless steel mold with a diameter (inner diameter) of 30 mm and a thickness of 200 μm.

Embodiment 2

[0023] A soft armor material, made of TPU (thermoplastic polyurethane elastomer rubber), TPEE (thermoplastic polyester elastomer), ABS resin, SBS resin (styrene-butadiene-styrene triblock copolymer) and DOA resin powder Composition, among them, TPU50kg, TPEE20kg, ABS10kg, SBS5kg, DOA5kg.

[0024] The preparation method of above-mentioned soft armor material, concrete steps are as follows:

[0025] (1) Weigh TPU50kg, TPEE20kg, ABS10kg, SBS5kg, DOA5kg as raw materials;

[0026] (2) After mixing the components evenly, put them into a mold and press them with glass under the condition of isolating the air.

Embodiment 3

[0028] A soft armor material, made of TPU (thermoplastic polyurethane elastomer rubber), TPEE (thermoplastic polyester elastomer), ABS resin, SBS resin (styrene-butadiene-styrene triblock copolymer) and DOA resin powder Composition, among them, TPU30kg, TPEE10kg, ABS15kg, SBS8kg, DOA2kg.

[0029] The preparation method of above-mentioned soft armor material, concrete steps are as follows:

[0030] (1) Weigh TPU30kg, TPEE10kg, ABS15kg, SBS8kg, DOA2kg as raw materials;

[0031] (2) After mixing the components evenly, put them into a mold and press them with glass under the condition of isolating the air.