A kind of mesoporous zirconium phosphate loaded nano silver antibacterial fiber and preparation method thereof

A nano-silver antibacterial and mesoporous zirconium phosphate technology is applied in the chemical characteristics of fibers, rayon manufacturing, single-component polyester rayon, etc. Large and other problems, to achieve the effect of filling the gap of preparation technology, no color change in performance, and low cost

Active Publication Date: 2017-06-30
DONGHUA UNIV
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this method, the addition amount is relatively large, and the distribution of antibacterial components is uneven, so it is difficult to realize continuous production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate, including a polymer matrix, Ag@mesoporous zirconium phosphate is dispersed in the polymer matrix, and the size of the Ag@mesoporous zirconium phosphate is 200-700nm .

[0029] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial fiber, the specific steps are:

[0030] (1) Mesoporous zirconium phosphate is treated with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: oleum with a mass fraction of 98% and mesoporous zirconium phosphate The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 20 minutes.

[0031] (2) Take silver nitrate, ethylene glycol, and mesoporous zirconium phosphate with sulfonic acid groups on the surface at a mass ratio of 0.5: 39.5: 60, add silver n...

Embodiment 2

[0035] A nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate, including a polymer matrix, Ag@mesoporous zirconium phosphate is dispersed in the polymer matrix, and the size of the Ag@mesoporous zirconium phosphate is 200-700nm .

[0036] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial fiber, the specific steps are:

[0037] (1) Treat mesoporous zirconium phosphate with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: 50% oleum and mesoporous The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 80 minutes.

[0038] (2) get silver sulfate, isosorbide and the mesoporous zirconium phosphate that the surface has sulfonic acid group that mass ratio is 0.5: 5: 94.5, add silver sulfate, isosorbide earlier at normal temperature and st...

Embodiment 3

[0042] A nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate, including a polymer matrix, Ag@mesoporous zirconium phosphate is dispersed in the polymer matrix, and the size of the Ag@mesoporous zirconium phosphate is 200-700nm .

[0043] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial fiber, the specific steps are:

[0044] (1) Mesoporous zirconium phosphate is treated with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: oleum with a mass fraction of 98% and mesoporous zirconium phosphate The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 20 minutes.

[0045] (2) Take silver nitrate, propylene glycol, and mesoporous zirconium phosphate with sulfonic acid groups on the surface at a mass ratio of 5:39.5:54.5, and add silve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate and a preparation method thereof. The nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate is characterized in that it includes a polymer matrix, and Ag@mesoporous zirconium phosphate is dispersed in the polymer matrix. The preparation method of the above-mentioned mesoporous zirconium phosphate-loaded nano-silver antibacterial fiber includes: preparing the silver@mesoporous zirconium phosphate sol precursor, and the above-mentioned silver@mesoporous zirconium phosphate sol precursor, terephthalic acid (PTA), two Polyhydric alcohols, stabilizers and catalysts are added in proportion to the polyester reactor for in-situ polymerization, and the polymerized products are granulated to obtain nano-silver antibacterial masterbatches, which are blended and granulated with nano-silver antibacterial masterbatches and polymers, dried, Mesoporous zirconium phosphate-loaded nano-silver antibacterial fibers were obtained by melt spinning. The method of the invention is simple in operation, high in efficiency, low in cost, durable in effect and broad in application prospect.

Description

technical field [0001] The invention belongs to the field of preparation of antibacterial fibers, in particular to a nano-silver antibacterial fiber loaded with mesoporous zirconium phosphate and a preparation method thereof. Background technique [0002] In today's society, the extreme environment, environmental pollution and other ecological environments have seriously deteriorated, and special living microenvironments such as confined spaces have led to an urgent need for functional protective textiles. At present, the fibers used to prepare textiles do not have antibacterial ability, and under certain conditions, they will provide an environment for bacteria to survive and reproduce, threatening human health. The main method to solve the antibacterial problem of fibers is to use antibacterial nanoparticles and polymer matrix for composite modification to prepare modified fibers with antibacterial effects. The fiber will gradually release antibacterial ingredients during...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G63/183C08K9/12C08K3/08
Inventor 朱美芳周家良胡泽旭夏维孙宾江晓泽
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com