High-yield fishing net

A fishing net and high-yield technology, applied in the field of fishing net production, can solve the problems of changing the smell of fishing nets, low fishing efficiency, etc., and achieve the effects of increasing fishing efficiency, good wear resistance, and prolonging service life.

Inactive Publication Date: 2016-02-24
六安市沪渔网具有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing fishing nets will put a lot of chemical substances in the production process, which will change the smell of the fishing net itself, and the fishing efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A fishing net for high-yield fishing is composed of the following ingredients in parts by weight: polyethylene 70, nylon 60, polystyrene 20, dimethyl silicone oil 3, fish bone meal 2, polyisodiene 5, spice 1 and compound additives 11.

[0014] The composite auxiliary is composed of the following components by weight: phenyl-p-phenylenediamine 1.4, phenolic resin 1.6, sodium citrate 1.8, bay leaf 0.2, mineral 0.6 and nano titanium dioxide 1.9; the preparation method of the composite auxiliary is: Sodium citrate and phenolic resin are added into the mixture of other components, heated while stirring, and stirred for 35 minutes, and the temperature is controlled at 90° C., so as to obtain the composite auxiliary agent.

[0015] A method for preparing a fishing net for high-yield fishing, comprising the following preparation steps:

[0016] (1) Add the above-mentioned polyethylene 70, nylon 60 and polystyrene 20 into the mixer and stir evenly, and the stirring time is 20 m...

Embodiment 2

[0026] A high-yield fishing net is composed of the following components by weight: polyethylene 78, nylon 65, polystyrene 25, dimethyl silicone oil 4, fish bone meal 2, polyisodiene 6, spice 1 and compound additives 12.

[0027] The composite auxiliary is composed of the following components by weight: phenyl-p-phenylenediamine 1.5, phenolic resin 1.8, sodium citrate 1.9, bay leaf 0.3, mineral 0.8 and nano titanium dioxide 2.1; the preparation method of the composite auxiliary is: Sodium citrate and phenolic resin are added to the mixture of other components, heated while stirring, and stirred for 42 minutes, and the temperature is controlled at 95°C to prepare the composite auxiliary agent.

[0028] A method for preparing a fishing net for high-yield fishing, comprising the following preparation steps:

[0029] (1) Add the above-mentioned polyethylene 78, nylon 65 and polystyrene 25 into the mixer and stir evenly, and the stirring time is 28 minutes;

[0030] (2) Put the ev...

Embodiment 3

[0040] A fishing net for high-yield fishing is composed of the following ingredients in parts by weight: polyethylene 85, nylon 70, polystyrene 30, dimethyl silicone oil 6, fish bone meal 3, polyisodiene 7, spice 2 and compound additives 14.

[0041] The composite auxiliary is composed of the following components by weight: phenyl-p-phenylenediamine 1.6, phenolic resin 2.1, sodium citrate 2.0, bay leaf 0.5, mineral 0.9 and nano titanium dioxide 2.2; the preparation method of the composite auxiliary is: Sodium citrate and phenolic resin are added to the mixture of other components, heated while stirring, and stirred for 50 minutes, and the temperature is controlled at 105° C., so as to obtain the composite auxiliary agent.

[0042] A method for preparing a fishing net for high-yield fishing, comprising the following preparation steps:

[0043] (1) Add above-mentioned polyethylene 85, nylon 70 and polystyrene 30 together in the mixer and stir evenly, and the stirring time is 35...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-yield fishing net and relates to the technical field of fishing net making. The high-yield fishing net comprises, by weight, 70-85 parts of polyethylene, 60-70 parts of nylon, 20-30 parts of polystyrene, 3-6 parts of dimethicone, 2-3 parts of fish bone meal, 5-7 parts of polyisoprene, 1-2 parts of spice and 11-14 parts of a composite auxiliary agent. The high-yield fishing net solves the problem of low fishing net fishing efficiency, has high strength and good wear resistance, is prepared from special materials by a special technology, changes a fishing net smell, has a smell in favor with fish, substantially improves fishing efficiency and has a long service life.

Description

technical field [0001] The invention relates to the technical field of fishing net production, in particular to a high-yield fishing net. Background technique [0002] Fishing nets are used for fishing, and modern fishing nets are mainly made of polyethylene and nylon materials. Existing fishing nets will put a large amount of chemical substances in the process of making, which will change the smell of the fishing net itself, and the fishing efficiency is low. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a fishing net capable of high-yield fishing. [0004] In order to solve the above problems, a sun-resistant fishing net according to the present invention is composed of the following ingredients in parts by weight: polyethylene 70-85, nylon 60-70, polystyrene 20-30, dimethyl silicone oil 3-6, fish bone powder 2-3, polyisodiene 5-7, spices 1-2 and compound additives 11-14. [0005] The compound auxiliary ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L77/00C08L25/06C08L83/04C08L47/00C08L61/06C08K13/02C08K3/22C08K5/18C08K5/098
CPCC08L23/06C08K2201/011C08L2205/035C08L77/00C08L25/06C08L83/04C08L47/00C08L61/06C08K13/02C08K2003/2241C08K5/18C08K5/098
Inventor 陆秀林王修德高志友
Owner 六安市沪渔网具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com