Hydrogel composition for facial mask comprising water-soluble polyurethane

A technology of water-soluble polyurethane and composition, which is applied in the direction of medical preparations containing active ingredients, dressing preparations, skin care preparations, etc., which can solve the problems of skin softening, environmental protection, and low ventilation, and achieve increased Production efficiency, production efficiency improvement, tear strength improvement effect

Active Publication Date: 2017-04-05
株式会社伊思韩佛
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, hydrogels contain a lot of water and have low air permeability, causing the problem of skin softening when applied for a long time
[0004] Ordinary polyurethane is flexible and has excellent air permeability, but it is insoluble in water. As a cosmetic, there are restrictions in containing water-soluble active ingredients that account for a large part of the active ingredients on the skin; gels composed only of water-soluble polyurethane materials themselves , can contain water-soluble active ingredients, but the skin adhesion is reduced. Compared with the gel composed of natural polymer gels, there are problems that are not compatible with the skin and are not environmentally friendly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogel composition for facial mask comprising water-soluble polyurethane
  • Hydrogel composition for facial mask comprising water-soluble polyurethane
  • Hydrogel composition for facial mask comprising water-soluble polyurethane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5 and comparative example 1～2

[0053] In order to determine the mixing ratio of the natural polymer gelling agent carrageenan and other natural polymer gelling agents, the following Examples and Comparative Examples were carried out.

[0054] In Examples 1 to 5 and Comparative Examples 1 to 2, the mixing ratio of carrageenan and cinnamon gum was adjusted in the range of 0.2 to 0.8% by weight, and stirred at 75° C. for 30 minutes to produce a hydrogel composition.

[0055] 【Table 1】

[0056]

[0057] The compressive strength was measured and confirmed for the state of the hydrogel composition of the composition.

[0058] The gel strength was measured at normal temperature using Instron 5569 (Instron co. USA). The thickness of the test piece used for measurement is 5.0 mm, and its diameter is 10 mm. Three test pieces are manufactured for each sample and measured. During the measurement, the cross head speed was 10 mm / min., and the compressive strength of the test piece was measured when 50% of the deform...

Embodiment 6～10 and comparative example 3～4

[0061] In order to determine the preferable electrolyte content, experiments of the following examples and comparative examples were carried out.

[0062] In Examples 6 to 10 and Comparative Examples 3 to 4, cinnamon gum and carrageenan were respectively maintained at 0.5% by weight, potassium chloride was changed to 0.09 to 1.1% by weight, and stirred at 75°C for 30 minutes to produce water Gel composition.

[0063] 【Table 2】

[0064]

[0065] The compressive strength was measured and confirmed for the state of the hydrogel composition of the composition.

[0066] The gel strength was measured at normal temperature using Instron 5569 (Instron co. USA). The thickness of the test piece used for measurement is 5.0 mm, and its diameter is 10 mm. Three test pieces are manufactured for each sample and measured. During the measurement, the cross head speed was 10 mm / min., and the compressive strength of the test piece was measured when 50% of the deformation was achieved.

[...

Embodiment 11～14 and comparative example 5～6

[0069] In order to confirm the preferable content ratio of water-soluble polyurethane, the experiment of the following Example and a comparative example was performed.

[0070] In Examples 11-14 and Comparative Examples 5-6, 0.5% by weight of cinnamon gum, 0.5% by weight of carrageenan, and 0.2% by weight of potassium chloride were maintained in the purified water, and the water-soluble polyurethane was adjusted within the range of 0.009-5.5% by weight. , and stirred at 75° C. for 30 minutes to prepare a hydrogel composition.

[0071] 【table 3】

[0072]

[0073] The gel elastic properties of the fabricated hydrogel compositions were confirmed.

[0074] Gel elasticity was measured at normal temperature using Instron 5569 (Instron co. USA). The thickness of the test piece used for measurement is 5.0 mm, and its diameter is 10 mm. Three test pieces are manufactured for each sample and measured. During the measurement, the speed of the cross head was 10mm / min., and the value...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to a hydrogel composition and, more specifically, to a hydrogel composition having improved elasticity and air permeability by including water-soluble polyurethane. Based on the total weight of the hydrogel composition, the hydrogel composition comprises 0.01 to 5.0 wt% of water-soluble polyurethane; 0.4 to 5.0 wt% of a natural polymer gelating agent; 1.0 to 60.0 wt% of a functional cosmetic component for imparting a skin beautifying function; 0.1 to 1.0 wt% of an electrolyte; 10.0 to 30.0 wt% of polyalcohol as a plasticizer; a preserving agent; and a solvent including other water. The hydrogel composition of the present invention is a cosmetic mask distributed after being pre-produced in a face shape or patch shape. The hydrogel composition has improved elasticity so as to be excellently adhered on the skin without an additional adhesive component, and the shape thereof can be maintained for a long time. Air permeability is improved, so that a useful component for skin can be easily transferred to the skin without concern over skin irritation.

Description

technical field [0001] The present invention relates to a hydrogel composition, and more specifically, to a hydrogel composition for a facial mask containing water-soluble polyurethane that improves the elastic properties of the gel and has air permeability. Background technique [0002] As a substance with high water content that contains a large amount of water, such as medicine, pharmaceuticals, prostheses and contact lenses, its application fields are showing a trend of diversification. Recently, it is used not only as a wound dressing and a drug delivery medium, but also in the field of cosmetics to deliver various effects such as moisturizing, nutrition supply, wrinkle improvement, and whitening to the skin. [0003] Generally speaking, hydrogels containing natural polymer gels are produced through various processes such as liquid-assisted forming, processing, and packaging. They are only realized with natural polymer gels, and their elastic properties and resistance t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/87A61K8/73A61K8/02A61Q19/00A61Q19/02A61Q19/08
CPCA61K8/0212A61K8/042A61K8/73A61K8/87A61Q19/00A61Q19/02A61Q19/08A61K8/20A61K2800/59
Inventor 金泰勋李根秀表亨培
Owner 株式会社伊思韩佛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com