Scratch-resistant imitated-metal-effect polypropylene composite material and preparation method thereof

A technology of composite material and polypropylene, which is applied in the field of scratch-resistant metal imitation polypropylene composite material and its preparation, can solve the problems of being easy to scratch and affecting the appearance, and achieves the effect of low production cost and good scratch resistance

Inactive Publication Date: 2016-04-20
SHANGHAI PRET COMPOSITES
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the above methods all play a certain role in the scratch resistance of the specific polypropylene composite material system, the imitation metal effect polypropylene composite material is mainly used as a decorative part and appearance part material, which is an easy-to-scratch part. If scratches occur, It directly affects its appearance, so the metal-like effect polypropylene material has very high requirements for scratch resistance, but the scratch-resistant metal-like effect polypropylene composite material is rarely studied and reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scratch-resistant imitated-metal-effect polypropylene composite material and preparation method thereof
  • Scratch-resistant imitated-metal-effect polypropylene composite material and preparation method thereof
  • Scratch-resistant imitated-metal-effect polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A scratch-resistant metal-like effect polypropylene composite material, the method comprises the following steps:

[0035] (1) Prepare materials according to the following components and contents

[0036] 70% polypropylene, 15% inorganic filler, 10% toughening agent, 1.5% effect pigment, 0.2% anti-scratch agent, 0.2% light stabilizer, 0.1% primary antioxidant, 0.2% secondary antioxidant.

[0037] Among them, polypropylene is AP3N and 7555KNE2 produced by Exxon Mobil, each with 35%.

[0038] The inorganic filler is 5000 mesh talc powder with an average particle size of 2.5 μm.

[0039] The toughening agent POE is Engage8180 produced by American Dow Company.

[0040] The metal pigment is an aluminum powder pigment with a particle size of 50 μm and a silver dollar shape, and the carrier is PE wax.

[0041] The anti-scratch agent is erucamide solid powder.

[0042] The light stabilizers are 944 and 770, and the addition amount is 0.2% each

[0043] The main antioxidant...

Embodiment 2

[0047] A scratch-resistant metal-like effect polypropylene composite material, the method comprises the following steps:

[0048] (1) Prepare materials according to the following components and contents

[0049] 70% polypropylene, 15% inorganic filler, 10% toughening agent, 1.5% effect pigment, 0.5% anti-scratch agent, 0.2% light stabilizer, 0.1% primary antioxidant, 0.2% secondary antioxidant.

[0050] Among them, polypropylene is AP3N and 7555KNE2 produced by Exxon Mobil, each with 35%.

[0051] The inorganic filler is 5000 mesh talc powder with an average particle size of 2.5 μm.

[0052]The toughening agent POE is Engage8180 produced by American Dow Company.

[0053] The metal pigment is an aluminum powder pigment with a particle size of 50 μm and a silver dollar shape, and the carrier is PE wax.

[0054] The anti-scratch agent is erucamide solid powder.

[0055] The light stabilizers are 944 and 770, and the addition amount is 0.2% each

[0056] The main antioxidant ...

Embodiment 3

[0060] A scratch-resistant metal-like effect polypropylene composite material, the method comprises the following steps:

[0061] (1) Prepare materials according to the following components and contents

[0062] 70% polypropylene, 15% inorganic filler, 10% toughening agent, 1.5% effect pigment, 1.0% anti-scratch agent, 0.2% light stabilizer, 0.1% primary antioxidant, 0.2% secondary antioxidant.

[0063] Among them, polypropylene is AP3N and 7555KNE2 produced by Exxon Mobil, each with 35%.

[0064] The inorganic filler is 5000 mesh talc powder with an average particle size of 2.5 μm.

[0065] The toughening agent POE is Engage8180 produced by American Dow Company.

[0066] The metal pigment is an aluminum powder pigment with a particle size of 50 μm and a silver dollar shape, and the carrier is PE wax.

[0067] The anti-scratch agent is erucamide solid powder.

[0068] The light stabilizers are 944 and 770, and the addition amount is 0.2% each

[0069] The main antioxidant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a scratch-resistant imitated-metal-effect polypropylene composite material and a preparation method thereof. The scratch-resistant imitated-metal-effect polypropylene composite material is prepared from the following raw materials in percentage by weight: 41-92% of polypropylene, 0-25% of inorganic filler, 0-15% of toughener, 0.1-4% of effect pigment, 0.1-4% of scratch resisting agent, 0.1-1% of light stabilizer and 0.1-1% of antioxidant. By adding a right amount of scratch resisting agent into the imitated-metal-effect polypropylene composite material, the prepared imitated-metal-effect polypropylene has better scratch resistance. Various physical mechanical properties of the prepared imitated-metal-effect polypropylene composite material are basically not influenced on the premise of ensuring the wear resistance of the material. The method for improving the wear resistance of the imitated-metal-effect polypropylene composite material has the advantages of simple preparation technique and low production cost.

Description

technical field [0001] The invention relates to a scratch-resistant metal-imitating polypropylene composite material and a preparation method thereof, which can be used for interior and exterior trim parts of automobiles and belongs to the technical field of polymer modification and processing. Background technique [0002] As people pay more and more attention to environmental protection, a class of imitation metal effect resin that can achieve spraying effect through direct injection molding without spraying is showing its strong competitiveness. The usual way to prepare this kind of imitation metal effect materials is to fill the resin materials with metal pigments and pearlescent pigments to achieve their special color effects. The imitation metal effect resin material can not only bring customers a variety of products, make it maintain a leading edge in the same industry, but also reduce the spraying process from raw materials to finished products that pollute the envir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/10C08L23/08C08L83/04C08K13/06C08K9/10C08K3/08C08K3/34C08K5/20C08J3/22B29C47/92B29C48/92
CPCC08L23/10B29C48/92B29C2948/92704C08J3/226C08J2323/10C08J2483/04C08K2201/003C08L2201/06C08L2205/025C08L2205/03C08L2205/035C08L23/0815C08K13/06C08K9/10C08K2003/0812C08K3/34C08K5/20C08L83/04
Inventor 吴俊张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com