Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Steel wire rod for high-strength boron-contained and annealing-free fastening piece and preparation method thereof

A high-strength fastener technology, applied in the field of materials, can solve the problems of plastic toughness and processing deformation ability that cannot meet market demand, and achieve the effects of reducing processing procedures and steel consumption, reducing production costs, and improving deformation ability of upset forging

Active Publication Date: 2016-05-04
WUKUN STEEL
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The plastic toughness and processing deformation ability of the existing boron-containing high-strength fastener steel can not meet the market demand, therefore, it is very necessary to develop a product that can solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel wire rod for high-strength boron-contained and annealing-free fastening piece and preparation method thereof
  • Steel wire rod for high-strength boron-contained and annealing-free fastening piece and preparation method thereof
  • Steel wire rod for high-strength boron-contained and annealing-free fastening piece and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the boron-containing high-strength annealing-free fastener steel wire rod according to the present invention is characterized in that it comprises the following steps:

[0026] A. Hot metal pretreatment desulfurization: the chemical composition C4.5~5.0wt%, Si0.30~0.50wt%, Mn0.25~0.50wt%, P0.090~0.110wt%, S≤0.020wt%, the rest is Fe and unavoidable impurities in the blast furnace molten iron are transported to the KR method molten iron pretreatment device for desulfurization treatment, the insertion depth of the stirring head is controlled at 2200~2400mm, according to 15.0~17.0kg / t 钢 Add the conventional CaO-based desulfurizer for desulfurization treatment, and control the stirring time to 8 minutes; after the stirring, carry out the slag removal operation to ensure that the molten iron surface in the ladle is exposed ≥ 4 / 5, and remove the desulfurization slag; the molten iron composition after pretreatment The control is: C4.5~4.8wt%, Si0.30~0....

Embodiment 1

[0053] A, hot metal pretreatment desulfurization: blast furnace hot metal (chemical composition C4.5wt%, Si0.30wt%, Mn0.25wt%, P0.090wt%, S0.012wt%, the rest is Fe and unavoidable impurities) transport To the KR method molten iron pretreatment device for desulfurization treatment, the insertion depth of the stirring head is controlled at 2200-2400mm, according to 15.0kg / t 钢 Add the conventional CaO-based desulfurizer for desulfurization treatment, and control the stirring time to 8 minutes; after the stirring, carry out the slag removal operation to ensure that the molten iron surface in the ladle is exposed ≥ 4 / 5, and remove the desulfurization slag; the molten iron composition after pretreatment The control is: C4.5wt%, Si0.30wt%, Mn0.25wt%, P0.090wt%, S0.002wt%, the rest is Fe and unavoidable impurities.

[0054] B, molten steel smelting: the pretreatment deep desulfurization hot metal of step A (chemical composition C4.5wt%, Si0.30wt%, Mn0.25wt%, P0.090wt%, S0.002wt%, the ...

Embodiment 2

[0067] A, hot metal pretreatment desulfurization: blast furnace hot metal (chemical composition C4.8wt%, Si0.40wt%, Mn0.38wt%, P0.102wt%, S0.017wt%, the rest is Fe and unavoidable impurities) transport To the KR method molten iron pretreatment device for desulfurization treatment, the insertion depth of the stirring head is controlled at 2200-2400mm, according to 16.0kg / t 钢 Add the conventional CaO-based desulfurizer for desulfurization treatment, and control the stirring time to 8 minutes; after the stirring, carry out the slag removal operation to ensure that the molten iron surface in the ladle is exposed ≥ 4 / 5, and remove the desulfurization slag; the molten iron composition after pretreatment The control is: C4.6wt%, Si0.40wt%, Mn0.38wt%, P0.102wt%, S0.003wt%, the rest is Fe and unavoidable impurities.

[0068] B, molten steel smelting: the pretreatment deep desulfurization hot metal of step A (chemical composition C4.6wt%, Si0.40wt%, Mn0.38wt%, P0.102wt%, S0.003wt%, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
reduction of areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel wire rod for a high-strength boron-contained and annealing-free fastening piece and a preparation method thereof. The steel wire rod for the high-strength boron-contained and annealing-free fastening piece comprises the following chemical components in percentage by weight: 0.20-0.24 wt% of C, Si not more than 0.04 wt%, 0.50-0.70 wt% of Mn, 0.25-0.35 wt% of Cr, 0.035-0.055 wt% of Ti, 0.035-0.055 wt% of Als, 0.0045-0.0060 wt% of B, S not more than 0.004 wt%, P not more than 0.012 wt%, O not more than 0.0015 wt%, H not more than 0.00015 wt%, and the balance of Fe and inevitable impurities. The preparation method comprises the steps of molten iron pretreatment desulfurization, molten steel smelting, deoxidation alloying, molten steel LF furnace refining, molten steel VD furnace vacuum refining, molten steel pouring, steel blank heating and controlled rolling and controlled cooling. The steel wire rod for high-strength boron-contained and annealing-free fastening piece is high in cleanness, few in inclusions, excellent in hardenability, proper in strength and hardness and excellent in ductility and toughness and cold heading and upsetting deformation capacity, can directly form a 10.9-grade high-level standard part through cold heading without needing spheroidizing annealing, reduces the processing procedures and the steel consumption, and reduces the production cost.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a boron-containing high-strength annealing-free fastener steel wire rod and a preparation method thereof. Background technique [0002] Steel for fasteners is steel for standard parts with high interchangeability produced by cold heading extrusion molding process. Steel for fasteners is formed by metal plastic processing at room temperature. The internal structure of the material is tight, the mechanical properties of the product are good, the loss of processed materials is small, the production efficiency is high, the energy consumption is low, the product has high dimensional accuracy, and the surface finish is good. It is widely used in Production of cold heading bolts, nuts, screws, rivets and pins and other fasteners and spare parts. [0003] In recent years, with the adjustment of the product structure of the fastener industry, the development of fasteners fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/18C22C38/14C22C38/06C22C33/04
CPCC22C33/04C22C38/002C22C38/04C22C38/06C22C38/14C22C38/18
Inventor 陈伟赵宇张卫强陆大章王卫东李金柱岳伟杨春雷文玉兵张瑜苏灿东朱锡森张志波马松
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com