Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of three-dimensional red chestnut matte artistic glaze for ceramic container

A ceramic container and three-dimensional technology, which is applied in the field of preparation of three-dimensional red chestnut frosted artistic glaze for ceramic containers, can solve problems such as non-compliance with low-carbon environmental protection production, glaze surface defects, and monotonous color rendering

Active Publication Date: 2016-05-11
JIANGSU YIXIANG CERAMIC TECH CO LTD
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

An exquisite glazed ceramic container has very high requirements on the appearance quality. The glaze of traditional ceramic products has a single color, poor gloss, monotonous color, and is prone to glaze defects, such as pinholes, glaze shrinkage, glaze bubbles and other defects. The product It is difficult to upgrade and upgrade, and cannot meet the cultural needs of multi-level and multi-field consumer groups for ceramic containers
Products with flaws in the glaze are unqualified products, which not only waste resources, but also reduce enterprise benefits, and do not meet the requirements of low-carbon and environmentally friendly production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation method of three-dimensional red chestnut frosted artistic glaze for ceramic containers, the glaze is composed of the following raw materials according to parts by weight: 11 parts of Suzhou soil, 54 parts of feldspar, 7 parts of calcite, 4 parts of dolomite, 12 parts of boron frit, spodumene 3 parts of stone, 2 parts of silicon carbide, 8 parts of iron oxide, 4 parts of manganese carbonate;

[0020] According to the above ingredients: ball: water ratio of 1:1.31:1.27, ball milling time is 45 hours, after ball milling, pass through 120 mesh sieve to get three-dimensional red chestnut frosted art glaze;

[0021] The body of the ceramic container is biscuit-fired at a temperature of 1030°C. The glaze is applied by the method of dipping the glaze, and the glaze is fired after drying; the glaze is fired by the oxidizing flame of the roller kiln;

[0022] The firing curve is: within 1-1.5 hours, the kiln temperature rises to 830°C at a constant speed; within 1...

Embodiment 2

[0024] The preparation method of the three-dimensional red chestnut frosted artistic glaze for ceramic containers, the glaze is composed of the following raw materials in parts by weight: 9 parts of Suzhou soil, 52 parts of feldspar, 8 parts of calcite, 6 parts of dolomite, 9 parts of boron frit, spodumene 4 parts of stone, 3 parts of silicon carbide, 9 parts of iron oxide, 2 parts of manganese carbonate;

[0025] According to the above ingredients: ball: water ratio of 1: 1.28: 1.29, ball milling time is 46 hours, after ball milling, pass through a 120 mesh sieve to get the three-dimensional red chestnut frosted art glaze;

[0026] The body of the ceramic container is biscuit-fired at a temperature of 1030°C. The glaze is applied by the method of dipping the glaze, and the glaze is fired after drying; the glaze is fired by the oxidizing flame of the roller kiln;

[0027] The firing curve is: within 1-1.5 hours, the kiln temperature rises to 830°C at a constant speed; within 1...

Embodiment 3

[0029] The preparation method of three-dimensional red chestnut frosted artistic glaze for ceramic containers, the glaze is composed of the following raw materials according to parts by weight: 8 parts of Suzhou soil, 56 parts of feldspar, 5 parts of calcite, 5 parts of dolomite, 10 parts of boron frit, spodumene 5 parts of stone, 2 parts of silicon carbide, 7 parts of iron oxide, 5 parts of manganese carbonate;

[0030] According to the above ingredients: ball: water is 1:1.33:1.26, the ball milling time is 42 hours, after ball milling, pass through a 120-mesh sieve to obtain the three-dimensional red chestnut frosted art glaze;

[0031] The body of the ceramic container is biscuit-fired at a temperature of 1030°C. The glaze is applied by the method of dipping the glaze, and the glaze is fired after drying; the glaze is fired by the oxidizing flame of the roller kiln;

[0032] The firing curve is: within 1-1.5 hours, the kiln temperature rises to 830°C at a constant speed; wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention belongs to a preparation method of ceramics, and particularly relates to a preparation method of a three-dimensional red chestnut matte artistic glaze for a ceramic container. The glaze comprises the following materials by weight: 8-11 parts of Suzhou clay, 52-56 parts of feldspar, 5-8 parts of calcite, 4-6 parts of dolomite, 9-12 parts of boron frit, 3-5 parts of spodumene, 2-3 parts of silicon carbide, 7-9 parts of iron oxide and 2-5 parts of manganese carbonate. The method is as below: conducting biscuiting on a ceramic container blank at 1030 DEG C; applying glaze by using a glaze dipping method, drying and conducting glaze firing by using a roller kiln oxidizing flame firing method. The preparation method of the three-dimensional red chestnut matte artistic glaze for the ceramic container uses glaze combination to realize color mechanism, and controls the glaze to have a high viscosity at high temperature melting; the glaze surface after firing produces a three-dimensional matte particles artistic effect, so as to achieve the simple, elegant, dignified and thick artistic texture.

Description

technical field [0001] The invention belongs to a method for preparing ceramics, in particular to a method for preparing a three-dimensional red chestnut frosted art glaze for ceramic containers. Background technique [0002] At present, with the heating up of the wine market, high-end famous wine companies adopt a large number of exquisite ceramic containers that match the pottery culture and wine culture. An exquisite glazed ceramic container has very high requirements on the appearance quality. The glaze of traditional ceramic products has a single color, poor gloss, monotonous color, and is prone to glaze defects, such as pinholes, glaze shrinkage, glaze bubbles and other defects. The product It is difficult to upgrade and upgrade, and cannot meet the cultural needs of multi-level and multi-field consumer groups for ceramic containers. Products with flaws in the glaze are substandard products, which not only waste resources, but also reduce enterprise benefits, and do n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C03C8/02C04B41/86
CPCC03C8/00C03C8/02C04B41/5022C04B41/86
Inventor 葛宜翔何畏孙素强
Owner JIANGSU YIXIANG CERAMIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com