Reinforced soakage agent for basalt fibers

A technology of basalt fiber and sizing agent, which is applied in the field of reinforced fiber sizing agent and its preparation, can solve the problems of poor resin bonding force, poor film-forming performance, flying silk and hairiness, etc., and achieves strong bonding force and film-forming performance. Good, the effect of less flying wire breaking phenomenon

Inactive Publication Date: 2016-05-25
晏玲莉
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A film-forming agent used alone has poor film-forming performance, and subsequent processing is prone to fly silk and hairiness, and its binding force with resin is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced soakage agent for basalt fibers
  • Reinforced soakage agent for basalt fibers
  • Reinforced soakage agent for basalt fibers

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method comprises the following steps:

[0027] a. Add water-soluble epoxy resin, polyester resin and vinyl resin emulsion respectively into water and stir evenly to disperse fully.

[0028] b. Add a pH regulator in deionized water to adjust the pH value to 4-6, add aminosilane coupling agent under stirring, and continue stirring for 25-35 minutes until the aqueous solution is clear and transparent; the amount of water accounts for 10% of the total weight of the wetting agent 1 / 20;

[0029] c. Dissolving the antistatic agent into an aqueous solution at a mass concentration of 20%;

[0030] d. Add enough soft water to the above raw materials according to the ratio, stir evenly and put it into use.

Embodiment 1

[0032] A basalt fiber-reinforced sizing agent consists of the following components in terms of weight percentage:

[0033]

[0034] The preparation method comprises the following steps:

[0035] a. Add water-soluble epoxy resin, polyester resin and vinyl resin emulsion respectively into water and stir evenly to disperse fully.

[0036] b. Add a pH regulator in deionized water to adjust the pH value to 4-6, add aminosilane coupling agent under stirring, and continue stirring for 25-35 minutes until the aqueous solution is clear and transparent; the amount of water accounts for 10% of the total weight of the wetting agent 1 / 20;

[0037] c. Dissolving the antistatic agent into an aqueous solution at a mass concentration of 20%;

[0038] d. Add enough soft water to the above raw materials according to the ratio, stir evenly and put it into use.

Embodiment 2

[0040] A basalt fiber-reinforced sizing agent consists of the following components in terms of weight percentage:

[0041]

[0042] The preparation method comprises the following steps:

[0043] a. Add water-soluble epoxy resin, polyester resin and vinyl resin emulsion respectively into water and stir evenly to disperse fully. The water temperature is 50-70 degrees; the amount of water used is 5-10 times the weight of each emulsion for later use;

[0044] b. Add a pH regulator in deionized water to adjust the pH value to 4-6, add aminosilane coupling agent under stirring, and continue stirring for 25-35 minutes until the aqueous solution is clear and transparent; the amount of water accounts for 10% of the total weight of the wetting agent 1 / 20;

[0045] c. Dissolving the antistatic agent into an aqueous solution at a mass concentration of 20%;

[0046] d. Add enough soft water to the above raw materials according to the ratio, stir evenly and put it into use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a soakage agent for basalt fibers and a preparation method of the soakage agent. The soakage agent is prepared from 2%-8% of water-soluble epoxy resin, 1%-5% of a polyester emulsion, 2%-4% of a vinyl resin emulsion, 0.5%-1.0% of a coupling agent, 0.2%-0.8% of an antistatic agent, 0.6%-1.2% of a plasticizer, 0.08%-0.25% of a pH regulator and the balance of deionized water. The soakage agent which is prepared in the rated weight ratio and used for surface modification of the basalt fibers can be directly applied to the surfaces of the basalt fibers in the production and drawing process of the basalt fibers, surface modification can be completed after drying, the soakage agent is more convenient to use, and an aqueous solution of the soakage agent has good adhesion and film-forming properties.

Description

Technical field: [0001] The invention relates to a reinforced fiber sizing agent and a preparation method thereof, belonging to the technical field of sizing agents. Background technique: [0002] Basalt fiber is a continuous fiber drawn at high speed by a platinum-rhodium alloy wire drawing bushing after melting basalt rock at 1450°C to 1500°C, and its strength is equivalent to that of high-strength S glass fiber. Basalt fiber has good mechanical strength, high temperature resistance, chemical corrosion resistance, heat insulation, sound insulation, good wave transmission and absorption performance and environmental protection performance. One of the high performance fibers. [0003] In the fiber drawing process, a surface treatment agent mainly composed of organic emulsion is coated on the surface of the fiber, that is, the fiber sizing agent. The use of sizing agent can effectively change the processing performance of inorganic fibers; in the molding process of inorgani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/42
CPCC03C25/36C03C25/28C03C25/323
Inventor 晏玲莉
Owner 晏玲莉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap