A kind of production method of high-density and long-life tungsten-molybdenum alloy crucible

A technology of tungsten-molybdenum alloy and production method, applied in metal processing equipment, metal material coating technology, gaseous chemical plating and other directions, can solve the problems of difficulty in producing high density and long life, and achieve dense organization and good isotropy. , the effect of small wear

Active Publication Date: 2018-02-06
ACHEMETAL TUNGSTEN & MOLYBDENUM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a production method of a high-density and long-life tungsten-molybdenum alloy crucible. The technical problem to be solved is to overcome the difficulty in producing high-density, long-term Lifetime Crucible Problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production method of high-density and long-life tungsten-molybdenum alloy crucible

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]A production method of a high-density and long-life tungsten-molybdenum alloy crucible comprises the following steps: step 1, pretreating tungsten powder and molybdenum powder and then screening respectively, the pretreatment process is: tungsten powder and molybdenum powder are placed under vacuum conditions The annealing treatment was carried out at 1300°C for 2 hours; the particle size of the tungsten powder after sieving was 20 microns, and the particle size of the molybdenum powder was 10 microns. Carry out ball milling 5h, make tungsten-molybdenum mixed powder, set aside;

[0032] Step 2. According to the target size of the required crucible, weigh the mass or volume of the tungsten-molybdenum mixed powder required to form a crucible, and make a cold isostatic pressing mold with the same volume as the molding cavity and the tungsten-molybdenum mixed powder, and cold The structure of the isostatic pressing die is as described above, specifically as figure 1 As show...

Embodiment 2

[0037] A molding method of tungsten and molybdenum powder metallurgy products, comprising the following steps: step 1, pretreating tungsten powder and molybdenum powder and then screening respectively, the pretreatment process is: annealing the tungsten powder and molybdenum powder under vacuum conditions 2h, the annealing temperature is 1300°C; the particle size of the sieved tungsten powder is 0.6 microns, and the particle size of the molybdenum powder is 0.05 microns, and the sieved tungsten powder and molybdenum powder are mixed according to the mass ratio of 9:1 and ball milled for 1 hour. Then mix at room temperature for 20 hours to obtain tungsten-molybdenum mixed powder, which is set aside;

[0038] Step 2. According to the target size of the required crucible, weigh the mass or volume of the tungsten-molybdenum mixed powder required to form a crucible, and make a cold isostatic pressing mold with the same volume as the molding cavity and the tungsten-molybdenum mixed p...

Embodiment 3

[0043] A method for forming a tungsten-molybdenum powder metallurgy product, comprising the following steps: step 1, sieving the tungsten powder and the molybdenum powder after pretreatment, the particle size of the tungsten powder after screening is 0.25 microns, and the particle size of the molybdenum powder is 0.1 microns , mix the sieved tungsten powder and molybdenum powder according to the mass ratio of 4:6, then ball mill for 3 hours, and then mix at room temperature for 20 hours to obtain tungsten-molybdenum mixed powder for later use; wherein, the pretreatment process is: the tungsten The powder and molybdenum powder were annealed for 2 hours under vacuum conditions, and the annealing temperature was 1300°C;

[0044] Step 2. According to the target size of the required crucible, weigh the mass or volume of the tungsten-molybdenum mixed powder required to form a crucible, and make a cold isostatic pressing mold with the same volume as the molding cavity and the tungsten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A production method of a high-density and long-life tungsten-molybdenum alloy crucible, comprising the steps of preparing tungsten-molybdenum mixed powder, preparing a powder blank, machining the powder blank to size, sintering, and surface treatment. Steps of hot isostatic pressing. The present invention combines cold isostatic pressing, sintering treatment, and hot isostatic pressing to process tungsten and molybdenum powder, so that the dislocation density inside the product is high, and the dislocations intersect each other to form cut steps to improve the strength of the product. At the same time, hot isostatic pressing makes the fibrous structure of the green body formed by cold isostatic pressing break again and recrystallize, avoiding the occurrence of tissue delamination, uneven grain distribution and uneven grain size, and the obtained structure Uniform and fine, dense structure, improve service life.

Description

technical field [0001] The invention relates to the technical field of metal materials, in particular to a production method of a high-density and long-life tungsten-molybdenum alloy crucible. Background technique [0002] Materials are one of the four major industries in China, including organic polymer materials, composite materials, metal materials and inorganic non-metal materials. As a kind of metal material manufacturing, powder metallurgy technology develops together with other manufacturing methods with its irreplaceable unique advantages. Porous materials and other methods cannot produce or have advantages such as materials that are difficult to produce. Powder metallurgy is the technology of producing metal powder and forming and sintering metal powder or metal powder and non-metal powder mixture to produce powder metallurgy materials or powder metallurgy products. [0003] Powder forming is the basic process of powder material preparation process, and mold is th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F3/04B22F3/15B22F3/03B22F5/10C23C16/08
CPCC23C16/08B22F3/03B22F3/04B22F3/15B22F5/10B22F2998/10B22F1/142
Inventor 耿宏安崔耀国
Owner ACHEMETAL TUNGSTEN & MOLYBDENUM