High-performance colorized water-permeable asphalt concrete and preparation method thereof

A permeable asphalt, high-performance technology, applied in the field of colored permeable asphalt concrete and its preparation, can solve the problems of affecting the growth of urban surface plants, destroying the ecological balance of urban surface, and unable to supplement urban groundwater, etc., to achieve beautiful visual enjoyment and improvement. City image, the effect of good mood

Active Publication Date: 2016-08-31
南京同力建设集团股份有限公司 +2
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the pavement technology of this kind of pavement is simple and low in cost, it will bring many negative effects to the ecological environment of the city.
First of all, this kind of impermeable and airtight pavement significantly reduces the rainwater infiltrated into the ground, and the urban groundwater cannot be replenished, which damages the city's water balance, affects the growth of urban surface plants, and destroys the ecological balance of the urban surface; secondly, Due to the inability to drain water in time on rainy days, this kind of dense pavement will cause water accumulation on the road, which will bring a lot of inconvenience to pedestrians and vehicles, and will also increase the noise pollution of the city and form the city's "heat island effect".

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance colorized water-permeable asphalt concrete and preparation method thereof
  • High-performance colorized water-permeable asphalt concrete and preparation method thereof
  • High-performance colorized water-permeable asphalt concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A preparation method of high-performance colored permeable asphalt concrete: the raw material formula is: according to the mass ratio, 25 parts of heavy oil, 2 parts of SBS, 3 parts of SBR, 20 parts of C5 petroleum resin, 1.0 part of silane coupling agent, 20 parts of pigment (iron oxide), 1000 parts of medium-sized ore type I graded ore.

[0052] The medium-sized ore I meets the following requirements:

[0053] The mass percentage of the ore passing through the square hole sieve with the following sieve holes (mm)

[0054]

[0055] (1) Add 25 parts of heavy oil and 20 parts of C5 petroleum resin according to the above mass ratio, heat to 170°C, fully swell, then add 2 parts of SBS and 3 parts of SBR, and completely After dissolving to form a uniform mixture and stirring and mixing evenly, the colorless binder for high-performance colored asphalt can be prepared (see Table 2 for performance);

[0056] (2) Mix 20 parts of the colorless binder for high-performance co...

Embodiment 2

[0058] A preparation method of high-performance colored permeable asphalt concrete: the raw material formula is: according to the mass ratio, 25 parts of heavy oil minus tetrahydrogenation and rewetting, 5 parts of TPS, 2 parts of SBR, 22 parts of C5 petroleum resin, and 1.0 parts of silane coupling agent Parts, 18 parts of pigment (iron oxide), 1000 parts of medium-sized mineral material II type graded mineral material.

[0059] Medium-sized ore II meets the following requirements:

[0060] The mass percentage of the ore passing through the square hole sieve with the following mm sieve holes

[0061]

[0062] (1) According to the above mass ratio, add 25 parts of heavy oil minus tetrahydrogenated remoisturization and 22 parts of C5 petroleum resin, heat to 175°C, fully swell, then add 5 parts of TPS and 2 parts of SBR, and undergo high-speed shearing After completely dissolving to form a uniform mixture and stirring and mixing evenly, the colorless binder for high-perform...

Embodiment 3

[0065] A preparation method of high-performance colored permeable asphalt concrete: the raw material formula is: according to the mass ratio, 20 parts of KP6040, 10 parts of heavy oil, 3 parts of SBS, 3 parts of SBR, 3 parts of EVA, 21 parts of C9 petroleum resin, silane 1.0 parts of coupling agent, 20 parts of pigment (iron oxide), 1000 parts of fine-grained mineral material Type I graded mineral material.

[0066] Fine-grained mineral material I meets the following requirements:

[0067] The mass percentage of the ore passing through the square hole sieve with the following mm sieve holes

[0068]

[0069] (1) According to the above mass ratio, add 20 parts of KP6040, 10 parts of heavy oil and 21 parts of C9 petroleum resin, under the condition of heating to 170 ℃, fully swell, then add 3 parts of SBS, 3 parts of SBR, 3 parts of 1 part of EVA, after being completely dissolved by high-speed shearing to form a uniform mixture and stirred evenly, the colorless binder for hi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-performance colorized water-permeable asphalt concrete and a preparation method thereof. The high-performance colorized water-permeable asphalt concrete is prepared from mineral aggregate, a colorless bonding material and a pigment satisfying grading requirements through mixing according to a mass ratio of 100: 4.5-7.5: 1.5-2.5, wherein the colorless bonding material is prepared from base oil, petroleum resin, a polymer and a coupling agent according to a mass ratio of 40-60: 30-45: 2-25: 0.05-3.0 through blending. The high-performance colorized water-permeable asphalt concrete has a red, yellow, green, blue or silver gray color, has pavement performances completely according with or exceeding the JTG F40-2004 road asphalt pavement construction technology standard requirements and is suitable for low carbon green road surfaces of various roads, squares, parks and stadiums.

Description

technical field [0001] The invention belongs to the technical field of municipal engineering construction, and in particular relates to a colored permeable asphalt concrete and a preparation method thereof. Background technique [0002] With the development of economy and the acceleration of urban construction, the surface of modern cities is being gradually covered by reinforced concrete houses and impermeable concrete pavement. At present, the pavements of urban streets, sidewalks, bicycle lanes, parks, courtyards and public squares in China are mainly made of impermeable stone plates and concrete. Although the pavement technology of this kind of pavement is simple and the cost is low, it will bring many negative effects to the ecological environment of the city. First of all, this kind of impermeable and airtight pavement significantly reduces the rainwater infiltrated into the ground, and the urban groundwater cannot be replenished, which damages the city's water balanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/00284C04B2111/0075C04B24/26C04B24/2676C04B24/42C04B14/308C04B14/02C04B20/0076C04B24/24C04B24/2623
Inventor 徐庆平杨勇富靳坤江培新高宝俭马娟王文忠
Owner 南京同力建设集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap