Preparation method of copper-based neutron absorbing material
A technology for absorbing materials and neutrons, applied in the field of preparation of copper-based neutron absorbing materials, can solve the problems of low boron solid solubility, reduced matrix processing performance and mechanical properties, and high inability to withstand high wear resistance. The effect of uniform distribution and tight bonding, excellent electrical and thermal conductivity
A technology for absorbing materials and neutrons, applied in the field of preparation of copper-based neutron absorbing materials, can solve the problems of low boron solid solubility, reduced matrix processing performance and mechanical properties, and high inability to withstand high wear resistance. The effect of uniform distribution and tight bonding, excellent electrical and thermal conductivity
CN105950897AInactive Publication Date: 2016-09-21TAIYUAN UNIV OF TECH
Image
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0057]The following will be further described in detail in conjunction with the following drawings;
[0058] figure 1 The schematic diagram of the discharge plasma sintering furnace is shown, and all parts must be connected correctly, proportioned according to quantity, and operated in sequence. Copper-based neutron-absorbing materials are made by spark plasma sintering. Under the joint action of electric field, thermal field and force field, sintering at a temperature lower than the melting point of the material can break the oxide layer on the particle surface, purify the material and avoid grains. grow up, so that the sintered body maintains excellent mechanical properties and good particle dispersion. The spark plasma sintering furnace is a vertical structure, such as figure 1 The structures shown are 1. Servo motor, 2. Upper indenter, 3. Graphite indenter, 4. Graphite mold, 5. Thermocouple, 6. Control panel, 7. Control button, 8. Control electric control cabinet, 9. Low...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| flexural strength | aaaaa | aaaaa |
| bending strength | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a preparation method of a copper-based neutron absorbing material. Specifically, the spark plasma sintering technique is used for applying pulse currents to mixed powder materials, so that joule heat and point discharge plasma are generated between particles, and the particles are made to melt locally to be connected in a metallurgical bonding mode; and the chemical materials used in the preparation process mainly include copper powder, boron carbide powder, absolute ethyl alcohol, hydrochloric acid, hydrofluoric acid, deionized water, graphite paper, sand paper and diamond paste. The preparation method comprises the steps of pretreatment of the copper powder, pretreatment of the boron carbide powder, weighing of the raw materials, ball milling of mixed materials, filling of powder, prepressing of a mold, spark plasma sintering for preparation, cleaning of the surface of a sample, detection and analysis of the sample and the like. The compactness of the prepared copper-based neutron absorbing material can reach 99% or over, the boron carbide in the copper-based neutron absorbing material is distributed in a dispersed mode, the bending strength can reach 350+ / -5 MPa, and the neutron absorbing performance can reach 98%.
Description
technical field [0001] The content of the invention is a preparation method of a copper-based neutron absorbing material, which belongs to the technical field of material processing, preparation and application. Background technique [0002] Neutron absorbing materials are widely used in the nuclear industry. At present, the commonly used neutron absorbing materials are mainly metals, nonmetals, and their compounds with high thermal neutron and epithermal neutron absorption cross-sections, such as commonly used elements boron, cadmium, silver etc. Silver is often not used as a neutron absorbing material because of its high price, but is often used as a control rod. Although cadmium has excellent neutron absorption performance, it has been gradually eliminated in recent decades due to its small reserves, high price and toxicity. Boron is an element with abundant reserves in nature. Natural boron has two stable isotopes B 10 and B 11 , boron element has neutron absorption ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
21 Sep 2016
Publication
CN105950897A
- IPC
- C22C1/05; C22C9/00; C22C32/00; B22F3/105; G21C7/24; G21C21/18
- CPC
- B22F3/105; C22C1/05; C22C9/00; C22C32/0057; G21C7/24; G21C21/18; Y02E30/30
- Inventors
- ηζε ; ιζ΄ͺθ