A kind of preparation method of SIC-based composite phase ceramic solidified body

A technology of multiphase ceramics and solidified bodies, which can be used in radioactive purification, nuclear engineering, etc., can solve the problems of excessive graphite and by-products, expensive disposal costs, and poor solidification of solidified bodies, and achieve excellent chemical stability, high mechanical strength, Excellent radiation resistance

Active Publication Date: 2021-12-31
SOUTHWEAT UNIV OF SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the solidification treatment of high-radioactive graphite, high-temperature self-propagating synthesis of TiC-Al at home and abroad 2 o 3 Many researches have been done on solidifying high-radioactive graphite based on ceramics, but this method has waste gas (CO, CO 2 etc.), the compactness of the solidified body is poor, there are more unreacted graphite and by-products, and the performance of the solidified body needs to be improved, especially the volume ratio of the solidified body is very large (theoretically, the solidified body is 10.6 times the weight of graphite, and it can actually reach more than 20 times), the disposal cost is extremely expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation method of a SiC-based composite phase ceramic solidified body, the steps are: using silicon powder, graphite, ZnO, CaO, Al 2 o 3 , SiO 2 As raw material, the formula is ZnO: CaO: Al 2 o 3 : SiO 2 =0.2:0.7:1:6 (molar ratio), Si:C=1.05 (molar ratio), 85wt% (mass percent) (Si+C)+15wt% ZCAS. First weigh ZnO, CaO, Al 2 o 3 , SiO 2 , adopt planetary mill ball mill for 5 hours, the material of ball mill: ball: dehydrated alcohol is 1: 3: 0.8 (mass ratio), oven dry (temperature 80 ℃, time 6 hours), calcining in ceramic fiber furnace, temperature is 1600 ℃, heat preservation for 1 hour, water quenching, pulverization and fine grinding to obtain ZCAS glass powder, then weigh silicon powder and graphite powder, then weigh the prepared ZCAS glass powder and add a mixture of Si and C, and use a planetary ball mill for 5 hours. Material: ball: absolute ethanol is 1: 3: 2 (mass ratio), vacuum drying (first temperature 50 ℃, time 6 hours; then temperature 120 ℃, t...

Embodiment 2

[0033] A preparation method of a SiC-based composite phase ceramic solidified body, the steps are: using silicon powder, graphite, ZnO, CaO, Al 2 o 3 , SiO 2 As raw material, the formula is ZnO: CaO: Al 2 o 3 : SiO 2 =0.4:0.5:1:6 (molar ratio), Si:C=1.05 (molar ratio), 85wt% (mass percent) (Si+C)+15wt% ZCAS. First weigh ZnO, CaO, Al 2 o 3 , SiO 2 , adopt planetary mill ball mill for 5 hours, the material of ball mill: ball: dehydrated alcohol is 1: 3: 0.8 (mass ratio), oven dry (temperature 80 ℃, time 6 hours), calcining in ceramic fiber furnace, temperature is 1600 ℃, heat preservation for 1 hour, water quenching, pulverization and fine grinding to obtain ZCAS glass powder, then weigh silicon powder and graphite powder, then weigh the prepared ZCAS glass powder and add a mixture of Si and C, and use a planetary ball mill for 5 hours. Material: ball: absolute ethanol is 1: 3: 2 (mass ratio), vacuum drying (first temperature 50 ℃, time 6 hours; temperature 120 ℃, time 6...

Embodiment 3

[0035] A preparation method of a SiC-based composite phase ceramic solidified body, the steps are: using silicon powder, graphite, ZnO, CaO, Al 2 o 3 , SiO 2 As raw material, the formula is ZnO: CaO: Al 2 o 3 : SiO 2 =0.5:0.4:1:6 (molar ratio), Si:C=1.05 (molar ratio), 85wt% (mass percent) (Si+C)+15wt% ZCAS. First weigh ZnO, CaO, Al 2 o 3 , SiO 2, adopt planetary mill ball mill for 5 hours, the material of ball mill: ball: dehydrated alcohol is 1: 3: 0.8 (mass ratio), oven dry (temperature 80 ℃, time 6 hours), calcining in ceramic fiber furnace, temperature is 1600 ℃, heat preservation for 1 hour, water quenching, pulverization and fine grinding to obtain ZCAS glass powder, then weigh silicon powder and graphite powder, then weigh the prepared ZCAS glass powder and add a mixture of Si and C, and use a planetary ball mill for 5 hours. Material: ball: absolute ethanol is 1: 3: 2 (mass ratio), vacuum drying (first temperature 50 ℃, time 6 hours; then temperature 120 ℃, ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a SiC-based multiphase ceramic solidified body, which is characterized in that the steps are: using ZnO, CaO, Al 2 o 3 , SiO 2 As a raw material, ZCAS glass is obtained by ball milling, drying, calcining, ball milling, and drying; SiC-ZCAS composite powder is obtained by ball milling, drying, and calcining using silicon powder, graphite, and ZCAS glass as raw materials; Adding polyvinyl alcohol sol, mixing, granulating, and pressing to shape; heat-treating the shaped green body and sintering it in a vacuum hot-pressing sintering furnace to obtain a SiC-based multiphase ceramic solidified body. The invention adopts safe and cheap raw materials, simple and practical vacuum hot pressing sintering technology, and prepares a SiC-based multiphase ceramic solidified body with excellent radiation resistance stability, chemical stability, mechanical stability and thermal stability at a relatively low temperature. The SiC-based multiphase ceramic solidified body prepared by the invention is suitable for safe treatment of high-radioactive graphite waste produced by decommissioning of nuclear reactors.

Description

technical field [0001] The invention belongs to the solidification treatment of radioactive waste, and relates to a preparation method of a SiC-based composite ceramic solidified body. It is suitable for ceramic solidification treatment of highly radioactive graphite waste. The SiC-based multiphase ceramic solidified body prepared by the present invention is especially suitable for safe treatment of high-radioactive graphite waste produced due to decommissioning of nuclear reactors, making radioactive 14 C nuclides are stably solidified in the SiC ceramic lattice to meet the requirements of deep geological disposal. Background technique [0002] With the increase in energy demand, the improvement of environmental protection awareness and the accelerated transformation of energy structure, nuclear energy is still the preferred energy source in terms of resources, economy, and safety, but the radioactive waste produced restricts the sustainable development of nuclear science ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/573C04B35/577C04B35/575C04B35/622C03C6/04C03C12/00G21F9/30
CPCC04B35/573C04B35/622C04B35/575C04B35/62204C03C1/00C03C12/00G21F9/302C04B2235/36C04B2235/428C04B2235/425C04B2235/656C04B2235/6567C04B2235/6581C04B2235/96C04B2235/9607
Inventor 滕元成王文曹雪吴浪
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com