Tent supporting rod

A technology for support rods and tents, applied in the field of tents, can solve the problems affecting the use of support rods, the easy wear and deformation of aluminum alloy materials, and achieve the effects of improving resilience, reducing damage and deformation, and improving wear resistance.

Inactive Publication Date: 2016-09-28
YANCHENG CHANGHUA OUTDOOR PROD CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many deficiencies in the strength and resilience of the current aluminum alloy support rods, and the aluminum alloy material is easy to wear and deform, which affects the use of the support rods to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: a kind of tent support pole, it comprises aluminum alloy base pole and the coating on the outside of aluminum alloy base pole, and the material of aluminum alloy base pole is composed of the following components by weight: 3 parts of Cu, 5 parts of Ti, 0.5 parts of Fe, 7 parts of Zn, 6 parts of Mg, 2 parts of Ni, 0.3 parts of Zr, 1 part of Si, 70 parts of Al; the coating material consists of 80% epoxy by mass percentage Resin, 15% pigment, 2% plasticizer and 3% flame retardant.

Embodiment 2

[0013] Embodiment 2: a kind of tent support pole, it comprises aluminum alloy base pole and the coating outside aluminum alloy base pole, and the material of aluminum alloy base pole is made up of the following components by weight: 2 parts of Cu, 4 parts of Ti, 1 part of Fe, 6 parts of Zn, 4.5 parts of Mg, 1.52 parts of Ni, 0.2 parts of Zr, 1 part of Si, 72 parts of Al; the coating material consists of 80% epoxy by mass percentage Resin, 15% pigment, 2% plasticizer and 3% flame retardant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tent supporting rod which comprises an aluminum alloy base rod and a coating outside the aluminum alloy base rod. The tent supporting rod is characterized in that the aluminum alloy base rod consists of the following components in parts by weight: 2-3 parts of Cu, 4-6 parts of Ti, 0.2-1 part of Fe, 6-8 parts of Zn, 4-7 parts of Mg, 1-2 parts of Ni, 0.2-0.5 part of Zr, 1-2 parts of Si, and 65-72 parts of Al; and the coating comprises the following materials: epoxy resin, pigment, a plasticizer and a flame retardant. The supporting rod has high strength, high elastic modulus, relatively good wear resistance and a relatively long service life.

Description

technical field [0001] The invention relates to the field of tents, in particular to a tent support pole. Background technique [0002] With the expansion of people's outdoor activities, and more and more people like outdoor sports, travel and leisure, the market demand for tents is also increasing. The tent needs to be well fixed outdoors to support and fix the expansion of the tent, and even have better wind resistance. The tent support rod is the skeleton of the tent, and the performance of the support rod is the key to determine the function and service life of the tent. At present, the mainstream support rods on the market are mainly made of metal materials and fiberglass materials. Glass fiber material is widely used due to its advantages of light weight, high modulus of elasticity, and low cost. However, the limited strength and stability of glass fiber also restricts the application of tents with high requirements. The metal materials are mainly steel and aluminum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C21/08C22C21/10
CPCC22C21/00C22C21/08C22C21/10
Inventor 严正华钱玉严加军
Owner YANCHENG CHANGHUA OUTDOOR PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products