A kind of flexible and stretchable electromagnetic shielding film and preparation method thereof

An electromagnetic shielding film and electromagnetic shielding technology, applied in the fields of magnetic field/electric field shielding, chemical instruments and methods, electrical components, etc., can solve the problems of poor bonding ability between metals and materials, loss of shielding performance, easy scratching of coatings, etc., to achieve Excellent electromagnetic shielding performance, improved electromagnetic shielding performance, and stable electromagnetic shielding performance

Inactive Publication Date: 2019-06-25
DONGHUA UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, many electromagnetic shielding materials on the market are made by metal plating, coating, pasting or blending conductive fibers on the surface of the material. Many problems are prone to occur in the process of preparation and use, such as poor bonding ability between metal and material, and easy to fall off. , the coating is easily scratched and loses shielding performance, the preparation process is seriously polluted, etc., and the material is relatively rough, poor in flexibility, airtight, poor in touch, not wearable, and it is difficult to meet the "thinness" required by modern electromagnetic shielding materials. Therefore, it is urgent to develop a wearable electromagnetic shielding material with high electromagnetic shielding performance, good flexibility, light weight, good durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of flexible and stretchable electromagnetic shielding film and preparation method thereof
  • A kind of flexible and stretchable electromagnetic shielding film and preparation method thereof
  • A kind of flexible and stretchable electromagnetic shielding film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Example 1: Ultra-thin elastic and stretchable electromagnetic shielding film

[0035] A method for preparing a flexible and stretchable electromagnetic shielding film, the specific steps are:

[0036] The first step: immerse the carbon nanotube film in the graphene suspension for 3 hours, immerse once, take it out, and let it dry naturally at room temperature to obtain a flexible nano-electromagnetic shielding composite film 2, and pass conductive Copper wire electrode adhered by silver glue;

[0037] The selected size of the carbon nanotube film is 20×28cm 2 The carbon nanotube film (Suzhou Institute of Nanotechnology and Nano-Bionics, Chinese Academy of Sciences) is obtained from multi-walled carbon nanotubes. The diameter of carbon nanotubes is about 20nm, the film thickness is 20um, the porosity is 75%, and the tensile strength is about 200MPa, conductivity about 1×10 5 S / m; The concentration of described graphene suspension is the graphene suspension of 2mg / ml (...

Embodiment 2

[0045] Embodiment 2: Elastic electromagnetic shielding film with ultra-high shielding effectiveness

[0046] A method for preparing a flexible and stretchable electromagnetic shielding film, the specific steps are:

[0047] The first step: immerse three carbon nanotube films in the graphene suspension respectively for 3 hours, immerse once, take them out, and dry them naturally at room temperature to obtain a three-layer flexible nano-electromagnetic shielding composite film 2, in which One end of the two pieces is adhered to the copper wire electrode by coating conductive silver glue;

[0048]The selected size of the carbon nanotube film is 20×30cm 2 The carbon nanotube film (Suzhou Institute of Nanotechnology and Nano-Bionics, Chinese Academy of Sciences) is obtained from multi-walled carbon nanotubes. The diameter of carbon nanotubes is about 20nm, the film thickness is 20um, the porosity is 75%, and the tensile strength is about 200MPa, conductivity about 1×10 5 S / m; Th...

Embodiment 3

[0057] Example 3: Elastic and Stretchable Electromagnetic Shielding Adhesive Film

[0058] A method for preparing a flexible and stretchable electromagnetic shielding film, the specific steps are:

[0059] The first step: immerse the carbon nanotube film in the graphene suspension for 3 hours, immerse once, take it out, and let it dry naturally at room temperature to obtain a flexible nano-electromagnetic shielding composite film 2, and pass conductive Copper wire electrode adhered by silver glue;

[0060] The selected size of the carbon nanotube film is 20×30cm 2 The carbon nanotube film (Suzhou Institute of Nanotechnology and Nano-Bionics, Chinese Academy of Sciences) is obtained from multi-walled carbon nanotubes. The diameter of carbon nanotubes is about 20nm, the film thickness is 20um, the porosity is 75%, and the tensile strength is about 200MPa, conductivity about 1×10 5 S / m; The concentration of described graphene suspension is the graphene suspension of 2mg / ml (Ne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a flexible stretchable electromagnetic shielding film and a preparation method thereof. The preparation method of the flexible stretchable electromagnetic shielding film comprises the following steps: selecting an elastic membrane as an elastic adhesion matrix, stretching the elastic membrane to a certain elongation, then fixing the elastic membrane, and coating a liquid elastic adhesive layer on the surface of the elastic membrane; crushing a flexible nano electromagnetic shielding complex film on the liquid elastic adhesive layer, coating resin with protective effect at the upper side of the flexible nano electromagnetic shielding complex film to form a resin layer, and curing the liquid elastic adhesive and the resin under certain conditions; and releasing a tensile force applied onto the elastic adhesion matrix, so as to drive the flexible nano electromagnetic shielding complex film to retract, namely the flexible stretchable electromagnetic shielding film is obtained. The prepared flexible stretchable electromagnetic shielding film has good elasticity, high elongation (20-50%) and excellent electromagnetic shielding property (electromagnetic wave absorptivity is more than or equal to 99% at the frequency of 1-5GHz) and can bear certain bending and compression deformation.

Description

technical field [0001] The invention relates to the field of electromagnetic shielding materials, more specifically, to the field of flexible and stretchable electromagnetic shielding films. Background technique [0002] With the rapid development of science and technology, electromagnetic waves have been widely used in aviation, aerospace, communications, household appliances, military and other fields, and the problem of electromagnetic pollution has become increasingly prominent. The electromagnetic energy radiated by electromagnetic waves is increasing at a rate of 7%-14% per year, and electromagnetic pollution to the environment is becoming increasingly serious. All over the world, various information networks transmit hundreds of millions of important military, political, and economic intelligence and information, and information leakage incidents caused by electromagnetic wave radiation also occur from time to time, directly threatening national politics, economy, mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B9/00B32B9/04B32B27/28B32B27/30B32B27/36B32B25/00B32B7/12B32B3/08B32B33/00B32B37/12B32B37/10B32B38/12H05K9/00
CPCB32B3/08B32B7/12B32B9/007B32B9/043B32B9/045B32B25/00B32B27/283B32B27/308B32B27/36B32B33/00B32B37/10B32B37/12B32B38/12B32B2037/1269B32B2255/26B32B2260/02B32B2260/04B32B2307/212B32B2307/51B32B2307/554H05K9/0081
Inventor 许福军高扬
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com