Mothproof and mildewproof glass magnesium board

A glass magnesium board and mildew-proof technology, applied in the field of decorative materials, can solve the problems of mildew, peculiar smell, deterioration of clothes and other items, etc. of decorative materials, and achieve the effect of preventing mildew

Inactive Publication Date: 2016-10-12
徐高强
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in some special environments, such as humid environment conditions, it is easy to make the decoration materials moldy, thus welcoming many small bugs, causing the deterioration of clothes and other items, and the appearance of peculiar smell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An insect-proof and mildew-proof glass magnesium board is prepared from the following raw materials in parts by weight: 30 parts of magnesium oxide, 25 parts of magnesium chloride, 10 parts of sodium bentonite, 2 parts of styrene-butadiene latex, 2 parts of water-based polyurethane and 20 parts of pure water.

[0018] An insect-proof and mildew-proof glass magnesium board is made by the following specific steps:

[0019] 1) Mix 10 parts of sodium-based bentonite with 2 parts of styrene-butadiene latex and 2 parts of water-based polyurethane, then add 10 parts of water, mix the slurry, pour it into a ball mill for grinding, dry it to obtain powder, and pass through 200 meshes;

[0020] 2) Mix 30 parts of magnesium oxide with 25 parts of magnesium chloride, grind to obtain powder, and pass through 200 mesh;

[0021] 3) Mix the powder obtained in step 1) with the powder obtained in step 2), then add 10 parts of water, put it in a blender, and stir for 60 minutes to form a ...

Embodiment 2

[0024] An insect-proof and mildew-proof glass magnesium board is prepared from the following raw materials in parts by weight: 40 parts of magnesium oxide, 25 parts of magnesium chloride, 10 parts of sodium bentonite, 2 parts of styrene-butadiene latex, 2 parts of water-based polyurethane and 20 parts of pure water.

[0025] An insect-proof and mildew-proof glass magnesium board is made by the following specific steps:

[0026] 1) Mix 10 parts of sodium-based bentonite with 2 parts of styrene-butadiene latex and 2 parts of water-based polyurethane, then add 10 parts of water, mix the slurry, pour it into a ball mill for grinding, dry it to obtain powder, and pass through 200 meshes;

[0027] 2) Mix 40 parts of magnesium oxide with 25 parts of magnesium chloride, grind to obtain powder, and pass through 200 mesh;

[0028] 3) Mix the powder obtained in step 1) with the powder obtained in step 2), then add 10 parts of water, put it in a blender, and stir for 60 minutes to form a ...

Embodiment 3

[0031] An insect-proof and mildew-proof glass magnesium board is prepared from the following raw materials in parts by weight: 30 parts of magnesium oxide, 25 parts of magnesium chloride, 10 parts of sodium bentonite, 2 parts of styrene-butadiene latex, 2 parts of water-based polyurethane and 20 parts of pure water.

[0032] An insect-proof and mildew-proof glass magnesium board is made by the following specific steps:

[0033] 1) Mix 10 parts of sodium-based bentonite with 2 parts of styrene-butadiene latex and 2 parts of water-based polyurethane, then add 10 parts of water, mix the slurry, pour it into a ball mill for grinding, dry it to obtain powder, and pass through 200 meshes;

[0034] 2) Mix 35 parts of magnesium oxide with 25 parts of magnesium chloride, grind to obtain powder, and pass through 200 mesh;

[0035] 3) Mix the powder obtained in step 1) with the powder obtained in step 2), then add 10 parts of water, put it in a blender, and stir for 60 minutes to form a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of decorating materials, in particular to a mothproof and mildewproof glass magnesium board which is made from, by weight, 30-40 parts of magnesium oxide, 25-35 parts of magnesium chloride, 10-20 parts of sodium-based bentomite, 2-3 parts of styrene-butadiene latex, 2-2.5 parts of waterborne polyurethane and 20-40 parts of pure water. The glass magnesium board is mildewproof and mothproof.

Description

technical field [0001] The invention relates to the field of decorative materials, in particular to an insect-proof and mildew-proof glass magnesium board. Background technique [0002] China's building decoration materials industry has developed rapidly with the development of real estate and building decoration industries. At present, China has become a major producer, consumer and exporter of decorative materials in the world. Material-led products not only rank first in the world in terms of total volume for many years, but also the per capita consumption index is close to or higher than the world's advanced level. [0003] With the improvement of Chinese people's living standards and the strengthening of comprehensive national strength, the architectural decoration industry not only continues to increase its proportion in the construction industry and its role has become increasingly prominent, but also plays an increasingly important role in economic development and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32
CPCC04B28/32C04B2111/20C04B14/12C04B24/26C04B24/282C04B14/42
Inventor 徐高强
Owner 徐高强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com