High-strength aramid paper and preparation method thereof
A kind of aramid paper, high-strength technology, applied in chemical instruments and methods, paper, papermaking, etc., can solve the problems of short service life, easy to tear, low mechanical strength, etc., and achieve the effect of improving service life and good mechanical strength
Active Publication Date: 2018-07-13
X FIPER NEW MATERIAL CO LTD
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Existing aramid paper is usually composed of para-aramid chopped fibers, meta-aramid pulp and adhesives. Aramid paper has low mechanical strength and is easy to tear, resulting in a short service life. Therefore, It is necessary to provide a new aramid paper to solve the above problems
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0018] The present invention will be further described below in conjunction with specific embodiments.
[0019] The present invention provides a high-strength aramid paper, comprising a spunlace non-woven fabric layer 2 and an aramid fiber paper 1, the spunlace non-woven fabric layer 2 and the aramid fiber paper 1 are combined, and the spunlace non-woven fabric layer 2 is combined with the aramid fiber paper 1 The woven fabric layer 2 is composed of intertwined first aramid chopped fibers, the aramid fiber paper 1 is composed of intertwined second aramid chopped fibers and aramid fibrids, part of the first aramid fibers Chopped fibers are intertwined with part of the second aramid chopped fibers, part of the first aramid chopped fibers are intertwined with part of the aramid precipitated fibers, and the thickness of the aramid fiber paper 1 is greater than or equal to The thickness of the spunlace nonwoven layer 2.
[0020] Wherein, the first aramid chopped fibers are crimped...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| Basis weight | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses high-strength aramid paper and a preparing method thereof. The high-strength aramid paper comprises a spunlace nonwoven cloth layer and aramid fiber paper, wherein the spunlace nonwoven cloth layer and the aramid fiber paper are compounded, and the spunlace nonwoven cloth layer is formed by first aramid chopped fiber mutually wound; the aramid fiber paper is composed of second aramid chopped fiber and aramid fibrid mutually wound, part of the first aramid chopped fiber and part of the second aramid chopped fiber are wound mutually, part of the first aramid chopped fiber and part of the aramid fibrid are wounded mutually, and the thickness of the aramid fiber paper is larger than that of the spunlace nonwoven cloth layer. Compared with the prior art, the high-strength aramid paper has the spunlace nonwoven cloth layer formed by first aramid chopped fiber mutually wound, the spunlace nonwoven cloth layer has high mechanical strength, and the service life of the high-strength aramid paper is prolonged.
Description
technical field [0001] The invention relates to a high-strength aramid fiber paper and a preparation method thereof. Background technique [0002] Aramid insulating paper, also known as aramid paper, has good thermal stability, flame retardancy, high temperature insulation and chemical stability, so it is widely used in aerospace, transportation, electronics and other fields. Existing aramid paper is usually composed of para-aramid chopped fibers, meta-aramid pulp and adhesives. Aramid paper has low mechanical strength and is easy to tear, resulting in a short service life. Therefore, It is necessary to provide a new aramid paper to solve the above problems. Contents of the invention [0003] The purpose of the present invention is to provide a high-strength aramid paper with high strength and long service life. [0004] In order to achieve the above object, the technical scheme adopted in the present invention is as follows: [0005] A high-strength aramid paper, compr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/30D21H15/02D21H13/26B32B5/08B32B27/02B32B27/12
CPCB32B5/024B32B5/08B32B5/26B32B2262/0269B32B2262/12B32B2262/14D21H13/26D21H15/02D21H27/30
Inventor 钟洲王丽丽车明国丁秀臣
Owner X FIPER NEW MATERIAL CO LTD