A kind of pendant and its manufacturing method

A production method and pendant technology, which can be applied in clothing, applications, jewelry, etc., can solve the problems of single pendant shape, aesthetic fatigue, and lack of novelty, and achieve the effect of increasing concreteness, unique shape, and rich layering

Active Publication Date: 2018-01-16
蒋海明
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many kinds of pendants, such as diamond pendants, gemstone pendants and gold pendants, etc., and their shapes are fixed when they are made. Therefore, the pendants purchased by users have a single shape, especially when worn for a long time, which is prone to aesthetic fatigue and is not innovative.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pendant and its manufacturing method
  • A kind of pendant and its manufacturing method
  • A kind of pendant and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A method for making a universe series pendant, comprising the steps of:

[0051] S1: Making the planet: use small glass beads with a diameter of 2-6mm to paint the surface effect of the planet, or use a non-porous spherical mineral gemstone with a diameter of 4-6mm as the planet;

[0052] S2: The production of star rings: use a specially designed spiral mold, prepare a little resin, add color, pearl powder, and glitter, apply semi-solidified resin on the mold, and get star rings after solidification; or directly inject color with small Stir with a stick to make a star ring;

[0053] S3: Making of the pendant:

[0054] a. Prepare a little resin, add color, pour into the mold as the bottom of the starry sky;

[0055]b. Prepare a large amount of resin, vacuumize and defoam, wait until it is semi-solidified, inject the color material into the resin with a needle, and stir it with a thin stick to make it blend with the resin background color in the first process at the bot...

Embodiment 2

[0059] A method for manufacturing starry sky series pendants, comprising the following steps:

[0060] S1: Production of the planet: Spray release agent on multiple spherical molds or hemispherical molds with a diameter of 4mm to 20mm, from the mold with a diameter of 4mm to the mold with a diameter of 20mm, each injection of resin is solidified for 6 to 12 hours before painting , and then put it into a mold of one size larger, and repeat the operation again until finally forming a concentric sphere with multi-layer drawing as a planet; the concentric sphere with multi-layer drawing can also be drawn by a computer, and the method of printing and transferring water stickers Print the pattern multiple times;

[0061] S2: The production of star rings: use a specially designed spiral mold, prepare a little resin, add color, pearl powder, and glitter, apply semi-solidified resin on the mold, and get star rings after solidification; or directly inject color with small Stir with a s...

Embodiment 3

[0070] A method for manufacturing a three-dimensional universe starry sky series pendant, comprising the following steps:

[0071] S1: Production of the planet: Use small glass beads with a diameter of 2 to 6 mm to paint the surface effect of the planet on it, or use a non-porous spherical mineral gem with a diameter of 4 to 6 mm as the planet; or use a diameter of 4 to 6 mm. Spray release agent for multiple spherical molds or hemispherical molds of 20mm. From the diameter of 4mm to the mold of 20mm, inject the resin into the mold for 6 to 12 hours each time to paint, then put it into a mold with a larger size, and then paint again. Repeat until you end up with concentric spheres with multiple layers drawn as planets;

[0072] S2: The production of star rings: use a specially designed spiral mold, prepare a little resin, add color, pearl powder, and glitter, apply semi-solidified resin on the mold, and get star rings after solidification; or directly inject color with small S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a pendant and a making method thereof. The pendant comprises a pendant head and a suspension clasp integrated with the pendant head, wherein the pendant head is spherical and comprises a sphere structure, an annular structure and a spherical bottom structure; the sphere structure and the annular structure are coated in the pendant head. The making method comprises the following steps: making a star ball, making a star ring and making the finished pendant. The invention also provides a shell used for containing the pendant. According to the pendant made by the invention, due to the integrated unique design of combining multilayer drawing with three-dimensional patterns, coating the drawing by the multilayer sphere in a three-dimensional manner and fusing a gemstone material, the pendant is innovative in design and unique in style, the wearing comfort and attractive appearance are greatly improved, and the texture representation and rich hierarchy of the pendant are increased. Meanwhile, a mold for making the pendant is designed by adopting a 3D printing technology, a multilayer homocentric sphere is accurately made, and a gorgeous three-dimensional effect and a unique effect of solid-state and liquid-state dynamic and static combination are formed.

Description

Technical field: [0001] The invention belongs to the technical field of jewelry manufacturing, and in particular relates to a pendant and a manufacturing method thereof. Background technique: [0002] Pendant is a kind of jewelry, which belongs to the ornaments worn on the neck, mostly made of precious metals, stainless steel or silver, and also made of diamonds, crystals, jade and so on. It mainly has the functions of praying for peace, calming the mind and looking beautiful. [0003] At present, there are many kinds of pendants, such as diamond pendants, gemstone pendants and gold pendants, etc., and their shapes are fixed when they are made. Therefore, the pendants purchased by users have a single shape, especially when worn for a long time, which is prone to aesthetic fatigue and is not innovative. . To this end, the applicant used a new type of resin material and combined with 3D printing technology to produce a pendant ornament with the theme of the universe and star...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A44C25/00A44C27/00
CPCA44C25/001A44C27/00
Inventor 蒋海明何洁
Owner 蒋海明